SABIC Innovative Plastics Lexan® ML6230 PC Copolymer

Category Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Lexan®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Lexan® ML6230 PC Copolymer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Low viscosity PC copolymer blend with enhanced UV stabilization and added release agent. Available in transparent and tinted colors.This data was supplied by SABIC-IP for the Americas region.
Physical Properties Metric English Comments
Specific Gravity 1.20 g/cc
1.20 g/cc
ASTM D 792
Density 1.20 g/cc
0.0434 lb/in³
ISO 1183
Moisture Absorption at Equilibrium 0.15 %
0.15 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.35 %

@Temperature 23.0 °C
0.35 %

@Temperature 73.4 °F
ISO 62
Linear Mold Shrinkage, Flow 0.0050 - 0.0070 cm/cm

@Thickness 3.20 mm
0.0050 - 0.0070 in/in

@Thickness 0.126 in
SABIC Method
Melt Flow 16 g/10 min

@Load 1.20 kg,
Temperature 300 °C
16 g/10 min

@Load 2.65 lb,
Temperature 572 °F
[cm^3/10 min] Melt Volume Rate; ISO 1133
17.5 g/10 min

@Load 1.20 kg,
Temperature 300 °C
17.5 g/10 min

@Load 2.65 lb,
Temperature 572 °F
ASTM D 1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 67.0 MPa
9720 psi
Type I, 50 mm/min; ASTM D 638
70.0 MPa
10200 psi
50 mm/min; ISO 527
Tensile Strength, Yield 65.0 MPa
9430 psi
Type I, 50 mm/min; ASTM D 638
67.0 MPa
9720 psi
50 mm/min; ISO 527
Elongation at Break >= 100 %
>= 100 %
Type I, 50 mm/min; ASTM D 638
>= 100 %
>= 100 %
50 mm/min; ISO 527
Elongation at Yield 6.0 %
6.0 %
Type I, 50 mm/min; ASTM D 638
6.0 %
6.0 %
50 mm/min; ISO 527
Tensile Modulus 2.30 GPa
334 ksi
1 mm/min; ISO 527
2.40 GPa
348 ksi
5 mm/min; ASTM D 638
Flexural Yield Strength 96.0 MPa
13900 psi
1.3 mm/min, 50 mm span; ASTM D 790
96.0 MPa
13900 psi
2 mm/min; ISO 178
Flexural Modulus 2.45 GPa
355 ksi
1.3 mm/min, 50 mm span; ASTM D 790
2.45 GPa
355 ksi
2 mm/min; ISO 178
Izod Impact, Notched 1.30 J/cm

@Temperature -30.0 °C
2.44 ft-lb/in

@Temperature -22.0 °F
ASTM D 256
7.80 J/cm

@Temperature 23.0 °C
14.6 ft-lb/in

@Temperature 73.4 °F
ASTM D 256
Izod Impact, Notched (ISO) 7.00 kJ/m²

@Temperature -30.0 °C
3.33 ft-lb/in²

@Temperature -22.0 °F
80*10*4; ISO 180/1A
10.0 kJ/m²

@Temperature 23.0 °C
4.76 ft-lb/in²

@Temperature 73.4 °F
80*10*4; ISO 180/1A
Charpy Impact, Notched 1.00 J/cm²

@Temperature 23.0 °C
4.76 ft-lb/in²

@Temperature 73.4 °F
V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA
Impact Test 80.0 J

@Temperature 23.0 °C
59.0 ft-lb

@Temperature 73.4 °F
Instrumented Impact Total Energy; ASTM D 3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 70.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
38.9 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
70.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
38.9 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
CTE, linear, Transverse to Flow 70.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
38.9 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
70.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
38.9 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
Deflection Temperature at 1.8 MPa (264 psi) 118 °C
244 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
133 °C

@Thickness 3.20 mm
271 °F

@Thickness 0.126 in
unannealed; ASTM D 648
Vicat Softening Point 136 °C
277 °F
Rate B/50; ISO 306
137 °C
279 °F
Rate B/120; ISO 306
148 °C
298 °F
Rate B/50; ASTM D 1525
Flammability, UL94 V-2

@Thickness 1.50 mm
V-2

@Thickness 0.0591 in
UL 94 by SABIC-IP
Glow Wire Test 825 °C

@Thickness 1.00 mm
1520 °F

@Thickness 0.0394 in
Glow Wire Ignitability Temperature; IEC 60695-2-13
825 °C

@Thickness 2.00 mm
1520 °F

@Thickness 0.0787 in
Glow Wire Ignitability Temperature; IEC 60695-2-13
825 °C

@Thickness 2.50 mm
1520 °F

@Thickness 0.0984 in
Glow Wire Ignitability Temperature; IEC 60695-2-13
825 °C

@Thickness 3.00 mm
1520 °F

@Thickness 0.118 in
Glow Wire Ignitability Temperature; IEC 60695-2-13
960 °C

@Thickness 1.50 mm
1760 °F

@Thickness 0.0591 in
Glow Wire Flammability Index; IEC 60695-2-12
Optical Properties Metric English Comments
Haze 0.60 %

@Thickness 2.54 mm
0.60 %

@Thickness 0.100 in
ASTM D 1003
Transmission, Visible 89 %

@Thickness 2.54 mm
89 %

@Thickness 0.100 in
ASTM D 1003
Descriptive Properties Value Comments
Ball Pressure Test, 125°C +/- 2°C passes
IEC 60695-10-2