SABIC Innovative Plastics NORYL APS130 PPE+PPS (Asia Pacific)
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polyphenylene Sulfide (PPS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Noryl |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics NORYL APS130 PPE+PPS (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.44 g/cc | 1.44 g/cc | ASTM D792 |
| Water Absorption | 0.020 % @Time 86400 sec |
0.020 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0025 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0025 - 0.0070 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 29.1 g/10 min @Load 5.00 kg, Temperature 300 °C |
29.1 g/10 min @Load 11.0 lb, Temperature 572 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 112 MPa | 16200 psi | SABIC - Japan Method |
| Elongation at Break | 8.0 % | 8.0 % | SABIC - Japan Method |
| Flexural Strength | 156 MPa | 22600 psi | ASTM D790 |
| Flexural Modulus | 8.43 GPa | 1220 ksi | ASTM D790 |
| Izod Impact, Notched | 0.880 J/cm | 1.65 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 25.0 - 55.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
13.9 - 30.6 µin/in-°F @Temperature -22.0 - 86.0 °F |
TMA |
| Deflection Temperature at 1.8 MPa (264 psi) | 267 °C @Thickness 3.20 mm |
513 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 1.00e+16 ohm | 1.00e+16 ohm | ASTM D257 |
| Dielectric Constant | 3.3 @Frequency 50.0 - 60.0 Hz |
3.3 @Frequency 50.0 - 60.0 Hz |
ASTM D150 |
| Dielectric Strength | 22.1 kV/mm @Thickness 1.60 mm |
561 kV/in @Thickness 0.0630 in |
in oil; ASTM D149 |
Users viewing this material also viewed the following:
- Okulen® 500 - REG PE Multicoloured coarse
- Nilit FRIANYL B63 SG-GV 2515 Nylon 6 for injection molding, 25% mineral filled and 15% glass fiber reinforced
- ExxonMobil Escorene® LD-103 LDPE Industrial Film Resin (discontinued **)
- Gouda Vuurvast CURON 13 S Dense Refractory Castable
- Ineos N07N-00 Polypropylene Impact Copolymer
- ExxonMobil Mobil Centaur Moly 2
- EMS-Griltech Grilon® M 369 Black Nylon 6 Fiber
- Plastcom SLOVAMID 6 NG GF 20 PA6, 20% glass fibre
- ExxonMobil Santoprene® 101-64 Thermoplastic Elastomer
Copyright © lookpolymers.com All Rights Reserved