SABIC Innovative Plastics NORYL FN170X PPE+PS
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Noryl |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics NORYL FN170X PPE+PS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Foamable resin. All properties at 10% density reduction; 0.250"" thick test specimens.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.00 g/cc | 1.00 g/cc | foam molded; ASTM D792 |
| 1.11 g/cc | 1.11 g/cc | ASTM D792 | |
| Water Absorption | 0.060 % @Time 86400 sec |
0.060 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0060 - 0.0080 cm/cm @Thickness 6.40 mm |
0.0060 - 0.0080 in/in @Thickness 0.252 in |
SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 28.0 MPa @Thickness 6.35 mm |
4060 psi @Thickness 0.250 in |
ASTM D638 |
| Tensile Strength, Yield | 29.0 MPa @Thickness 6.35 mm |
4210 psi @Thickness 0.250 in |
ASTM D638 |
| Elongation at Break | 13.1 % @Thickness 6.35 mm |
13.1 % @Thickness 0.250 in |
ASTM D638 |
| Elongation at Yield | 5.7 % @Thickness 6.35 mm |
5.7 % @Thickness 0.250 in |
ASTM D638 |
| Flexural Yield Strength | 66.0 MPa | 9570 psi | 6.4 mm; ASTM D790 |
| Flexural Modulus | 2.13 GPa | 309 ksi | 6.4 mm; ASTM D790 |
| Izod Impact, Unnotched | 2.77 J/cm @Thickness 6.40 mm |
5.19 ft-lb/in @Thickness 0.252 in |
ASTM D4812 |
| Dart Drop, Total Energy | 57.0 J | 42.0 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 89.0 °C @Thickness 6.40 mm |
192 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 78.0 °C @Thickness 6.40 mm |
172 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| UL RTI, Electrical | 85.0 °C | 185 °F | UL 746B |
| UL RTI, Mechanical with Impact | 85.0 °C | 185 °F | UL 746B |
| UL RTI, Mechanical without Impact | 85.0 °C | 185 °F | UL 746B |
| Flammability, UL94 | V-1 @Thickness 2.99 mm |
V-1 @Thickness 0.118 in |
UL 94 |
| 5VA @Thickness 4.69 mm |
5VA @Thickness 0.185 in |
UL 94 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Arc Resistance | 60 - 120 sec | 60 - 120 sec | Tungsten; ASTM D495 |
| Comparative Tracking Index | 400 - 600 V | 400 - 600 V | UL 746A |
| Hot Wire Ignition, HWI | >= 120 sec | >= 120 sec | UL 746A |
| High Amp Arc Ignition, HAI | 30 - 60 arcs | 30 - 60 arcs | UL 746A |
| High Voltage Arc-Tracking Rate, HVTR | >= 150 mm/min | >= 5.91 in/min | UL 746A |
| Descriptive Properties | Value | Comments |
|---|---|---|
| FOAM - Flame Class Minimum Density | 1g/cm^3 | |
| FOAM - IMPACT 6.4 mm Wt Reduction | 10% | |
| FOAM - MECHANICAL 6.4 mm Wt Reduction | 10% | |
| FOAM - PHYSICAL 6.4mm Wt Reduction | 10% | |
| FOAM - THERMAL 6.4mm Wt Reduction | 10% | |
| Radiant Panel Listing | YES | UL Tested |
| UV-light, water exposure/immersion | F2 | UL 746C |
Users viewing this material also viewed the following:
- PolyOne OnFlex™ S EF 80A-3S1977 Thermoplastic Elastomer (TPE)
- Malvern Minerals Nylon with Novakup® L-337 Silane-Treated Quartz Filler
- Kinlead PG14 Bag Grade BOPP Plain Film (thickness: 50 µm)
- McDanel Advanced Ceramics AP 35 99% Alumina
- Ipiranga Petrochem PH 0130 Polypropylene
- Gromax BFG20-DN00N1 Nylon 6 20% Glass Filled (Conditioned)
- Topas Advanced Polymers TOPAS® 9903D-10 Cyclic Olefin Copolymer (COC)
- A. Schulman ComAlloy Hiloy® 511 Polycarbonate, Glass Reinforced, UL
- A. Schulman POLYBATCH™ Orange 10334 Concentrate Based In LLDPE
Copyright © lookpolymers.com All Rights Reserved