SABIC Innovative Plastics NORYL FN215X PPE+PS
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Noryl |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics NORYL FN215X PPE+PS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Structural foam resin. 170F (77C) HDT. Improved reliability and productivity. All values at 20% weight reduction.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.880 g/cc | 0.880 g/cc | foam molded; ASTM D792 |
| 1.10 g/cc | 1.10 g/cc | ASTM D792 | |
| Water Absorption | 0.070 % @Time 86400 sec |
0.070 % @Time 24.0 hour |
ASTM D570 |
| Moisture Absorption at Equilibrium | 0.17 % | 0.17 % | ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0060 - 0.0080 cm/cm @Thickness 6.40 mm |
0.0060 - 0.0080 in/in @Thickness 0.252 in |
SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 28.0 MPa @Thickness 6.35 mm |
4060 psi @Thickness 0.250 in |
ASTM D638 |
| Elongation at Break | 12 % @Thickness 6.35 mm |
12 % @Thickness 0.250 in |
ASTM D638 |
| Flexural Yield Strength | 61.0 MPa | 8850 psi | 6.4 mm; ASTM D790 |
| Flexural Modulus | 1.90 GPa | 276 ksi | 6.4 mm; ASTM D790 |
| Izod Impact, Unnotched | 2.02 J/cm @Thickness 6.40 mm |
3.78 ft-lb/in @Thickness 0.252 in |
ASTM D4812 |
| Dart Drop, Total Energy | 10.0 J | 7.38 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| 3.00 J @Temperature -30.0 °C |
2.21 ft-lb @Temperature -22.0 °F |
Instrumented Impact Energy @ peak; ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 88.0 °C @Thickness 6.40 mm |
190 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 76.0 °C @Thickness 6.40 mm |
169 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| UL RTI, Electrical | 85.0 °C | 185 °F | UL 746B |
| UL RTI, Mechanical with Impact | 85.0 °C | 185 °F | UL 746B |
| UL RTI, Mechanical without Impact | 85.0 °C | 185 °F | UL 746B |
| Flammability, UL94 | V-1 @Thickness 2.99 mm |
V-1 @Thickness 0.118 in |
UL 94 |
| V-0 @Thickness 5.99 mm |
V-0 @Thickness 0.236 in |
UL 94 | |
| 5VA @Thickness 3.91 mm |
5VA @Thickness 0.154 in |
UL 94 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | >= 1.00e+17 ohm | >= 1.00e+17 ohm | ASTM D257 |
| Dielectric Constant | 2.2 @Frequency 1.00e+6 Hz |
2.2 @Frequency 1.00e+6 Hz |
ASTM D150 |
| Dielectric Strength | 12.0 kV/mm @Thickness 1.60 mm |
305 kV/in @Thickness 0.0630 in |
in oil; ASTM D149 |
| Dissipation Factor | 0.0044 @Frequency 1.00e+6 Hz |
0.0044 @Frequency 1.00e+6 Hz |
ASTM D150 |
| Arc Resistance | 60 - 120 sec | 60 - 120 sec | Tungsten; ASTM D495 |
| Comparative Tracking Index | 400 - 600 V | 400 - 600 V | UL 746A |
| High Voltage Arc-Tracking Rate, HVTR | >= 150 mm/min | >= 5.91 in/min | UL 746A |
| Descriptive Properties | Value | Comments |
|---|---|---|
| FOAM - Flame Class Minimum Density | 0.85g/cm^3 | |
| FOAM - IMPACT 6.4 mm Wt Reduction | 20% | |
| FOAM - MECHANICAL 6.4 mm Wt Reduction | 20% | |
| FOAM - PHYSICAL 6.4mm Wt Reduction | 20% | |
| FOAM - THERMAL 6.4mm Wt Reduction | 20% | |
| Radiant Panel Listing | YES | UL Tested |
| UV-light, water exposure/immersion | F1 | UL 746C |