SABIC Innovative Plastics NORYL FXN119BK PPE+HIPS (Asia Pacific)

Category Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Noryl
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics NORYL FXN119BK PPE+HIPS (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Noryl* FXN119BK is a low gloss PPE/HIPS grade. It provides a balance of mechanical properties and heat performance with intrinsic low gloss appreance. FXN119BKBK is available in black only.
Physical Properties Metric English Comments
Specific Gravity 1.06 g/cc
1.06 g/cc
ASTM D792
Density 1.06 g/cc
0.0383 lb/in³
ISO 1183
Moisture Absorption 0.0600 %
0.0600 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.23 %
0.23 %
ISO 62
Linear Mold Shrinkage, Flow 0.0050 - 0.0070 cm/cm

@Thickness 3.20 mm
0.0050 - 0.0070 in/in

@Thickness 0.126 in
SABIC Method
Melt Flow 8.0 g/10 min

@Load 5.00 kg,
Temperature 280 °C
8.0 g/10 min

@Load 11.0 lb,
Temperature 536 °F
ASTM D1238
Melt Index of Compound 8.0 g/10 min

@Load 5.00 kg,
Temperature 280 °C
8.0 g/10 min

@Load 11.0 lb,
Temperature 536 °F
MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Hardness, Rockwell R 116
116
ISO 2039-2
Hardness, H358/30 95.0 MPa
13800 psi
ISO 2039-1
Tensile Strength at Break 48.0 MPa
6960 psi
50 mm/min; ISO 527
49.0 MPa
7110 psi
Type I, 50 mm/min; ASTM D638
Tensile Strength, Yield 51.0 MPa
7400 psi
50 mm/min; ISO 527
53.0 MPa
7690 psi
Type I, 50 mm/min; ASTM D638
Elongation at Break 40 %
40 %
Type I, 50 mm/min; ASTM D638
40 %
40 %
50 mm/min; ISO 527
Elongation at Yield 4.2 %
4.2 %
50 mm/min; ISO 527
5.1 %
5.1 %
Type I, 50 mm/min; ASTM D638
Tensile Modulus 2.20 GPa
319 ksi
1 mm/min; ISO 527
2.40 GPa
348 ksi
5 mm/min; ASTM D638
Flexural Yield Strength 77.0 MPa
11200 psi
2 mm/min; ISO 178
85.0 MPa
12300 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 2.20 GPa
319 ksi
1.3 mm/min, 50 mm span; ASTM D790
2.20 GPa
319 ksi
2 mm/min; ISO 178
Izod Impact, Notched 1.60 J/cm
3.00 ft-lb/in
ASTM D256
1.10 J/cm

@Temperature -30.0 °C
2.06 ft-lb/in

@Temperature -22.0 °F
ASTM D256
Izod Impact, Notched (ISO) 11.0 kJ/m²
5.23 ft-lb/in²
80*10*4; ISO 180/1A
7.00 kJ/m²

@Temperature -30.0 °C
3.33 ft-lb/in²

@Temperature -22.0 °F
80*10*4; ISO 180/1A
Charpy Impact, Notched 1.40 J/cm²
6.66 ft-lb/in²
Edgew 80*10*4 sp=62mm; ISO 179/1eA
0.700 J/cm²

@Temperature -30.0 °C
3.33 ft-lb/in²

@Temperature -22.0 °F
Edgew 80*10*4 sp=62mm; ISO 179/1eA
Dart Drop, Total Energy 42.0 J

@Temperature 23.0 °C
31.0 ft-lb

@Temperature 73.4 °F
ASTM D3763
Taber Abrasion, mg/1000 Cycles 75
75
CS-17, 1 kg; SABIC Method
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 92.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
51.1 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
92.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
51.1 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
CTE, linear, Transverse to Flow 95.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
52.8 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
95.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
52.8 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 133 °C
271 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
Deflection Temperature at 1.8 MPa (264 psi) 117 °C
243 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
117 °C

@Thickness 3.20 mm
243 °F

@Thickness 0.126 in
unannealed; ASTM D648
Vicat Softening Point 139 °C
282 °F
Rate B/50; ISO 306
140 °C
284 °F
Rate B/50; ASTM D1525
142 °C
288 °F
Rate B/120; ISO 306
Flammability, UL94 HB

@Thickness 1.50 mm
HB

@Thickness 0.0591 in
UL 94 by SABIC-IP
Glow Wire Test 750 °C

@Thickness 3.20 mm
1380 °F

@Thickness 0.126 in
IEC 60695-2-12
Optical Properties Metric English Comments
Gloss 20 %
20 %
untextured, 60 degrees; ASTM D523
Descriptive Properties Value Comments
Ball Pressure Test, 125°C +/- 2°C Passes
IEC 60695-10-2