SABIC Innovative Plastics NORYL GFN1 PPE+HIPS (Asia Pacific)

Category Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Noryl
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics NORYL GFN1 PPE+HIPS (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PPE+PS blend. 10% Glass reinforced. FDA compliance (restrictions apply). Low water absorption. Hydrolytic stability. Dimensional stability. Suitable for fluid engineering applications including water filter and water meter components.
Physical Properties Metric English Comments
Specific Gravity 1.17 g/cc
1.17 g/cc
ASTM D792
Density 1.17 g/cc
0.0423 lb/in³
ISO 1183
Moisture Absorption 0.0400 %
0.0400 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.12 %
0.12 %
ISO 62
Linear Mold Shrinkage, Flow 0.0055 - 0.0066 cm/cm

@Thickness 3.20 mm
 0.0055 - 0.0066 in/in

@Thickness 0.126 in
 SABIC Method
Melt Flow 4.0 g/10 min

@Load 5.00 kg,
Temperature 280 °C
 4.0 g/10 min

@Load 11.0 lb,
Temperature 536 °F
 ASTM D1238
Melt Index of Compound 4.0 g/10 min

@Load 5.00 kg,
Temperature 280 °C
 4.0 g/10 min

@Load 11.0 lb,
Temperature 536 °F
 MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 60.0 MPa
8700 psi
50 mm/min; ISO 527
75.0 MPa
10900 psi
Type I, 50 mm/min; ASTM D638
Tensile Strength, Yield 60.0 MPa
8700 psi
50 mm/min; ISO 527
75.0 MPa
10900 psi
Type I, 50 mm/min; ASTM D638
Elongation at Break 3.5 %
3.5 %
Type I, 50 mm/min; ASTM D638
4.5 %
4.5 %
50 mm/min; ISO 527
Elongation at Yield 3.5 %
3.5 %
Type I, 50 mm/min; ASTM D638
4.5 %
4.5 %
50 mm/min; ISO 527
Tensile Modulus 3.90 GPa
566 ksi
1 mm/min; ISO 527
4.40 GPa
638 ksi
5 mm/min; ASTM D638
Flexural Yield Strength 105 MPa
15200 psi
1.3 mm/min, 50 mm span; ASTM D790
115 MPa
16700 psi
2 mm/min; ISO 178
Flexural Modulus 3.40 GPa
493 ksi
1.3 mm/min, 50 mm span; ASTM D790
3.70 GPa
537 ksi
2 mm/min; ISO 178
Izod Impact, Notched 0.840 J/cm
1.57 ft-lb/in
ASTM D256
0.800 J/cm

@Temperature -30.0 °C
 1.50 ft-lb/in

@Temperature -22.0 °F
 ASTM D256
Izod Impact, Unnotched 4.10 J/cm
7.68 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 10.0 kJ/m²
4.76 ft-lb/in²
80*10*4; ISO 180/1A
9.00 kJ/m²

@Temperature -30.0 °C
 4.28 ft-lb/in²

@Temperature -22.0 °F
 80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 30.0 kJ/m²
14.3 ft-lb/in²
80*10*4; ISO 180/1U
30.0 kJ/m²

@Temperature -30.0 °C
 14.3 ft-lb/in²

@Temperature -22.0 °F
 80*10*4; ISO 180/1U
Charpy Impact, Notched 0.800 J/cm²
3.81 ft-lb/in²
Edgew 80*10*4 sp=62mm; ISO 179/1eA
Dart Drop, Total Energy 20.0 J

@Temperature 23.0 °C
 14.8 ft-lb

@Temperature 73.4 °F
 ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 38.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 21.1 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
45.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 25.0 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
CTE, linear, Transverse to Flow 82.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 45.6 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
85.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 47.2 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 135 °C

@Thickness 3.20 mm
 275 °F

@Thickness 0.126 in
 unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 129 °C
264 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
130 °C

@Thickness 3.20 mm
 266 °F

@Thickness 0.126 in
 unannealed; ASTM D648
Vicat Softening Point 138 °C
280 °F
Rate B/50; ASTM D1525
138 °C
280 °F
Rate B/50; ISO 306
140 °C
284 °F
Rate B/120; ISO 306