- HOME
- POLYMER SEARCH
- Thermoplastic
- Polystyrene (PS)
- SABIC Innovative Plastics NORYL GTX GTX830 PPE+PS+PA
SABIC Innovative Plastics NORYL GTX GTX830 PPE+PS+PA
| Category | Polymer , Thermoplastic , Nylon , Polyphenylene Ether/PPO , Polystyrene (PS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | NORYL GTX |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics NORYL GTX GTX830 PPE+PS+PA.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
30% Glass Reinforced PPE+PA Alloy.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.33 g/cc | 1.33 g/cc | ASTM D792 |
| Density | 1.328 g/cc | 0.04798 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.500 % | 0.500 % | 50% RH, 24 hrs; ASTM D570 |
| Moisture Absorption at Equilibrium | 1.0 % | 1.0 % | 50% RH; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0030 cm/cm @Thickness 3.20 mm |
0.0020 - 0.0030 in/in @Thickness 0.126 in |
SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.0065 - 0.0085 cm/cm @Thickness 3.20 mm |
0.0065 - 0.0085 in/in @Thickness 0.126 in |
SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 120 | 120 | ASTM D785 |
| Tensile Strength at Break | 158 MPa | 22900 psi | Nominal Stress, brk, Type I, 5 mm/min; ASTM D638 |
| Tensile Strength, Yield | 151 MPa | 21900 psi | Nominal Stress, yld, Type I, 5 mm/min; ASTM D638 |
| Elongation at Break | 7.0 % | 7.0 % | Nominal Strain, 5 mm/min; ASTM D638 |
| Flexural Yield Strength | 248 MPa | 36000 psi | 2.6 mm/min, 100 mm span; ASTM D790 |
| Flexural Modulus | 8.58 GPa | 1240 ksi | 2.6 mm/min, 100 mm span; ASTM D790 |
| Izod Impact, Notched | 1.06 J/cm | 1.99 ft-lb/in | ASTM D256 |
| 0.800 J/cm @Temperature -30.0 °C |
1.50 ft-lb/in @Temperature -22.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 19.8 - 30.6 µm/m-°C @Temperature -20.0 - 150 °C |
11.0 - 17.0 µin/in-°F @Temperature -4.00 - 302 °F |
ASTM E 831 |
| Deflection Temperature at 0.46 MPa (66 psi) | 254 °C @Thickness 6.40 mm |
489 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 240 °C @Thickness 6.40 mm |
464 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| Vicat Softening Point | 248 °C | 478 °F | Rate B/50; ASTM D1525 |
| UL RTI, Electrical | 50.0 °C | 122 °F | UL 746B |
| UL RTI, Mechanical with Impact | 50.0 °C | 122 °F | UL 746B |
| UL RTI, Mechanical without Impact | 50.0 °C | 122 °F | UL 746B |
| Flammability, UL94 | HB @Thickness 1.47 mm |
HB @Thickness 0.0579 in |
UL 94 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Arc Resistance | 60 - 120 sec | 60 - 120 sec | Tungsten; ASTM D495 |
| Comparative Tracking Index | 250 - 400 V | 250 - 400 V | UL 746A |
| Hot Wire Ignition, HWI | >= 120 sec | >= 120 sec | UL 746A |
| High Amp Arc Ignition, HAI | 30 - 60 arcs | 30 - 60 arcs | UL 746A |
| High Voltage Arc-Tracking Rate, HVTR | 10.0 - 25.4 mm/min | 0.394 - 1.00 in/min | UL 746A |
Users viewing this material also viewed the following:
- Nye Lubricants 368AS (RL) Synthetic Oil
- Osprey Metals Fe3Si Binary Alloy Powder (Grade 90% - 16)
- PolyOne Geon™ Vinyl Flexible R130AE White 41 Polyvinyl Chloride, Flexible (PVC, Flexible)
- Master Bond EP21TDC-7 Highly Flexible Two Component Epoxy System
- 3M 5461 Anti-Slip/Anti-Stick Tape
- AlphaGary Evoprene™ GF 6256 Automotive Thermoplastic Elastomer
- Ametek P434L P/M Stainless Steel, Sintered from 6.6 g/cc Green Density
- Ametek Ultra 304L P/M Stainless Steel, Sintered from 6.38 g/cc Green Density
- Teknor Apex APEX® 97-G0029B-80 Polyvinyl Chloride, Flexible