- HOME
- POLYMER SEARCH
- Thermoplastic
- Polystyrene (PS)
- SABIC Innovative Plastics NORYL GTX GTX902 PPE+PS+PA (Asia Pacific)
SABIC Innovative Plastics NORYL GTX GTX902 PPE+PS+PA (Asia Pacific)
| Category | Polymer , Thermoplastic , Nylon , Polyphenylene Ether/PPO , Polystyrene (PS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | NORYL GTX |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics NORYL GTX GTX902 PPE+PS+PA (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Unreinforced. Excellent chemical resistance and paintability. 312F (155C) HDT.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.08 g/cc | 1.08 g/cc | ASTM D792 |
| Water Absorption | 0.40 % @Time 86400 sec |
0.40 % @Time 24.0 hour |
ASTM D570 |
| Moisture Absorption at Equilibrium | 3.6 % | 3.6 % | ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.011 - 0.015 cm/cm | 0.011 - 0.015 in/in | annealed 130C 1hr; ASTM D955 |
| 0.0090 - 0.012 cm/cm @Thickness 3.20 mm |
0.0090 - 0.012 in/in @Thickness 0.126 in |
SABIC Method | |
| Linear Mold Shrinkage, Transverse | 0.0080 - 0.011 cm/cm @Thickness 3.20 mm |
0.0080 - 0.011 in/in @Thickness 0.126 in |
SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 118 | 118 | ASTM D785 |
| Tensile Strength at Break | 56.0 MPa | 8120 psi | Type I, 50 mm/min; ASTM D638 |
| Tensile Strength, Yield | 59.0 MPa | 8560 psi | Type I, 50 mm/min; ASTM D638 |
| Elongation at Break | 52 % | 52 % | Type I, 50 mm/min; ASTM D638 |
| Elongation at Yield | 9.0 % | 9.0 % | Type I, 50 mm/min; ASTM D638 |
| Flexural Yield Strength | 89.0 MPa | 12900 psi | 2.6 mm/min, 100 mm span; ASTM D790 |
| Flexural Modulus | 2.24 GPa | 325 ksi | 2.6 mm/min, 100 mm span; ASTM D790 |
| Izod Impact, Notched | 2.72 J/cm | 5.10 ft-lb/in | ASTM D256 |
| 0.530 J/cm @Temperature -40.0 °C |
0.993 ft-lb/in @Temperature -40.0 °F |
ASTM D256 | |
| 1.17 J/cm @Temperature -30.0 °C |
2.19 ft-lb/in @Temperature -22.0 °F |
ASTM D256 | |
| Izod Impact, Unnotched | 32.04 J/cm | 60.02 ft-lb/in | ASTM D4812 |
| 32.04 J/cm @Temperature -30.0 °C |
60.02 ft-lb/in @Temperature -22.0 °F |
ASTM D4812 | |
| 32.04 J/cm @Temperature -40.0 °C |
60.02 ft-lb/in @Temperature -40.0 °F |
ASTM D4812 | |
| Dart Drop, Total Energy | 46.0 J | 33.9 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| 19.0 J @Temperature -40.0 °C |
14.0 ft-lb @Temperature -40.0 °F |
Instrumented Impact Energy @ peak; ASTM D3763 | |
| 36.0 J @Temperature -30.0 °C |
26.6 ft-lb @Temperature -22.0 °F |
Instrumented Impact Energy @ peak; ASTM D3763 | |
| Taber Abrasion, mg/1000 Cycles | 19 | 19 | CS-17, 1 kg; ASTM D1044 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 90.0 µm/m-°C @Temperature -20.0 - 150 °C |
50.0 µin/in-°F @Temperature -4.00 - 302 °F |
ASTM E 831 |
| Deflection Temperature at 0.46 MPa (66 psi) | 155 °C @Thickness 6.40 mm |
311 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 127 °C @Thickness 6.40 mm |
261 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| Vicat Softening Point | 232 °C | 450 °F | Rate B/50; ASTM D1525 |
| UL RTI, Electrical | 50.0 °C | 122 °F | UL 746B |
| UL RTI, Mechanical with Impact | 50.0 °C | 122 °F | UL 746B |
| UL RTI, Mechanical without Impact | 50.0 °C | 122 °F | UL 746B |
| Flammability, UL94 | HB @Thickness 1.49 mm |
HB @Thickness 0.0587 in |
UL 94 |
Users viewing this material also viewed the following:
- 3M Dyneon™ CC085 PTFE, PPS-Filled (discontinued **)
- Loxim 830 02T V0 Polypropylene Compound, 30% Talc Filled, Flame Retardant
- Haynes Hastelloy® C-22® alloy, 12.7-50.8 mm thick bar, solution heat treated
- A. Schulman PP 1467-01 Polypropylene Medium Impact Polypropylene
- DuPont Performance Polymers Hytrel® HTR8341C BK320 Polyester Elastomer TPC-ET (Unverified Data**)
- AK Steel TRAN-COR® H-0 CARLITE® Grain Oriented Electrical Steel
- AlphaGary Evoprene™ 029 Standard SBS Thermoplastic Elastomer Compound
- BASF Ultramid® 8281 HS PA6 (Dry)
- 3M 477 Vinyl Tape
- Unipetrol C5 Fraction
Copyright © lookpolymers.com All Rights Reserved