SABIC Innovative Plastics NORYL GTX6601 PPE+PA66 (Asia Pacific)
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Polyphenylene Ether/PPO |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Noryl |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics NORYL GTX6601 PPE+PA66 (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PPE+PA Unfilled GTX
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.10 g/cc | 1.10 g/cc | ASTM D792 |
| Water Absorption | 0.50 % @Time 86400 sec |
0.50 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.012 - 0.014 cm/cm @Thickness 3.20 mm |
0.012 - 0.014 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 8.9 g/10 min @Load 5.00 kg, Temperature 280 °C |
8.9 g/10 min @Load 11.0 lb, Temperature 536 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 51.0 MPa | 7400 psi | SABIC - Japan Method |
| Elongation at Break | 110 % | 110 % | SABIC - Japan Method |
| Flexural Strength | 73.0 MPa | 10600 psi | ASTM D790 |
| Flexural Modulus | 1.86 GPa | 270 ksi | ASTM D790 |
| Izod Impact, Notched | 6.47 J/cm | 12.1 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 80.0 - 90.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
44.4 - 50.0 µin/in-°F @Temperature -22.0 - 86.0 °F |
TMA |
| Deflection Temperature at 1.8 MPa (264 psi) | 195 °C @Thickness 6.40 mm |
383 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- SABIC PP 5703P Polypropylene Homopolymer for Injection Molding
- Polymer Resources TP-FRG7.5 Polybutylene Terephthalate, 7 1/2 % Glass Reinforced, Flame Retardant
- NOVA Chemicals Sclair® 8107 UV8D Butene LLDPE Rotational Molding Resin
- Palm Labs Adhesives TURBO-LOCK SERIES 17-OR Anaerobic Thread Locking Compound
- Gouda Vuurvast GI 34 Insulating Refractory Brick
- Samsung Cheil Industries Starex® SG-302 Expandable Polystyrene (EPS) High Expansion
- TSE Industries Millathane® E34 Millable Polyether Polyurethane Rubber with 0.50 PHR Zinc Stearate
- Ensinger Tecast Vekton™ 6PA Black Unfilled Cast Nylon 6 (PA6)
- DSM Arnitel® UM551-V 55 Shore D, Flame Retardant (halogen-, phosphorous-free) Copolyester Elastomer (North America)
Copyright © lookpolymers.com All Rights Reserved