SABIC Innovative Plastics NORYL HNA055 PPE+HIPS (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Noryl
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics NORYL HNA055 PPE+HIPS (Europe-Africa-Middle East).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
>PPE+PS-HI< Autoclavable engineering thermoplastic. Biocompatible per ISO10993 (color dependent).
Physical Properties Metric English Comments
Specific Gravity 1.08 g/cc
1.08 g/cc
ASTM D792
Density 1.08 g/cc
0.0390 lb/in³
ISO 1183
Moisture Absorption 0.0600 %
0.0600 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.23 %
0.23 %
ISO 62
Linear Mold Shrinkage, Flow 0.0060 - 0.0080 cm/cm

@Thickness 3.20 mm
0.0060 - 0.0080 in/in

@Thickness 0.126 in
SABIC Method
Melt Flow 6.2 g/10 min

@Load 5.00 kg,
Temperature 300 °C
6.2 g/10 min

@Load 11.0 lb,
Temperature 572 °F
ASTM D1238
Melt Index of Compound 5.0 g/10 min

@Load 5.00 kg,
Temperature 300 °C
5.0 g/10 min

@Load 11.0 lb,
Temperature 572 °F
MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 55.0 MPa
7980 psi
Type I, 50 mm/min; ASTM D638
57.0 MPa
8270 psi
50 mm/min; ISO 527
Tensile Strength, Yield 61.0 MPa
8850 psi
50 mm/min; ISO 527
67.0 MPa
9720 psi
Type I, 50 mm/min; ASTM D638
Elongation at Break 12.6 %
12.6 %
50 mm/min; ISO 527
16.3 %
16.3 %
Type I, 50 mm/min; ASTM D638
Elongation at Yield 3.8 %
3.8 %
50 mm/min; ISO 527
4.8 %
4.8 %
Type I, 50 mm/min; ASTM D638
Tensile Modulus 2.40 GPa
348 ksi
1 mm/min; ISO 527
3.24 GPa
470 ksi
5 mm/min; ASTM D638
Flexural Yield Strength 101 MPa
14600 psi
1.3 mm/min, 50 mm span; ASTM D790
107 MPa
15500 psi
2 mm/min; ISO 178
Flexural Modulus 2.49 GPa
361 ksi
2 mm/min; ISO 178
2.54 GPa
368 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 2.93 J/cm
5.49 ft-lb/in
ASTM D256
1.44 J/cm

@Temperature -30.0 °C
2.70 ft-lb/in

@Temperature -22.0 °F
ASTM D256
Izod Impact, Notched (ISO) 24.0 kJ/m²
11.4 ft-lb/in²
80*10*4; ISO 180/1A
14.0 kJ/m²

@Temperature -30.0 °C
6.66 ft-lb/in²

@Temperature -22.0 °F
80*10*4; ISO 180/1A
Charpy Impact, Notched 2.70 J/cm²
12.8 ft-lb/in²
Edgew 80*10*4 sp=62mm; ISO 179/1eA
Dart Drop, Total Energy 54.0 J

@Temperature 23.0 °C
39.8 ft-lb

@Temperature 73.4 °F
ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 86.6 µm/m-°C

@Temperature -40.0 - 40.0 °C
48.1 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
86.6 µm/m-°C

@Temperature -40.0 - 40.0 °C
48.1 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
CTE, linear, Transverse to Flow 92.5 µm/m-°C

@Temperature -40.0 - 40.0 °C
51.4 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
92.5 µm/m-°C

@Temperature -40.0 - 40.0 °C
51.4 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
Deflection Temperature at 1.8 MPa (264 psi) 147 °C
297 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
147 °C

@Thickness 3.20 mm
297 °F

@Thickness 0.126 in
unannealed; ASTM D648
Vicat Softening Point 168 °C
334 °F
Rate B/50; ASTM D1525
168 °C
334 °F
Rate B/50; ISO 306
169 °C
336 °F
Rate B/120; ISO 306