- SABIC Innovative Plastics NORYL N1250 PPE+HIPS (Asia Pacific)
SABIC Innovative Plastics NORYL N1250 PPE+HIPS (Asia Pacific)
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Noryl |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics NORYL N1250 PPE+HIPS (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Noryl* N1250 is an unfilled, injection moldable modified polyphenylene ether resin. Designed for good dimensional stability and good flow , this resin also uses non-chlorinated, non-brominated FR additives to achieve a V0 UL94 rating at 0.75 mm and V0-5VA at 2.5 mm with a specific density of 1.11 g/cm^3. Noryl N1250 has a heat Vicat resistance of 137 deg C and it may be an excellent material candidate for application requiring electrically insuNoryl* N1250 is an unfilled, injection moldable modified polyphenylene ether resin. Designed for good dimensional stability and good flow , this resin also uses non-chlorinated, non-brominated FR additives to achieve a V0 UL94 rating at 0.75 mm and V
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.10 g/cc | 1.10 g/cc | ASTM D792 |
| Density | 1.10 g/cc | 0.0397 lb/in³ | ISO 1183 |
| Water Absorption | 0.070 % @Time 86400 sec |
0.070 % @Time 24.0 hour |
ASTM D570 |
| Moisture Absorption | 0.0500 % | 0.0500 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.25 % | 0.25 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0050 cm/cm @Time 86400 sec |
0.0050 in/in @Time 24.0 hour |
ISO 294 |
| 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
SABIC Method | |
| Melt Index of Compound | 12 g/10 min @Load 5.00 kg, Temperature 280 °C |
12 g/10 min @Load 11.0 lb, Temperature 536 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 55.0 MPa | 7980 psi | 50 mm/min; ISO 527 |
| 62.0 MPa | 8990 psi | Type I, 50 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 68.0 MPa | 9860 psi | SABIC - Japan Method |
| 75.0 MPa | 10900 psi | 50 mm/min; ISO 527 | |
| 79.0 MPa | 11500 psi | Type I, 50 mm/min; ASTM D638 | |
| Elongation at Break | 8.0 % | 8.0 % | 50 mm/min; ISO 527 |
| 15 % | 15 % | Type I, 50 mm/min; ASTM D638 | |
| 45 % | 45 % | SABIC - Japan Method | |
| Elongation at Yield | 4.5 % | 4.5 % | 50 mm/min; ISO 527 |
| 5.0 % | 5.0 % | Type I, 50 mm/min; ASTM D638 | |
| Tensile Modulus | 2.62 GPa | 380 ksi | 1 mm/min; ISO 527 |
| 2.72 GPa | 395 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 107 MPa | 15500 psi | ASTM D790 |
| Flexural Yield Strength | 109 MPa | 15800 psi | 2 mm/min; ISO 178 |
| 122 MPa | 17700 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 2.53 GPa | 367 ksi | 2 mm/min; ISO 178 |
| 2.54 GPa | 368 ksi | ASTM D790 | |
| 3.00 GPa | 435 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.910 J/cm | 1.70 ft-lb/in | ASTM D256 |
| Izod Impact, Notched (ISO) | 8.00 kJ/m² | 3.81 ft-lb/in² | 80*10*4; ISO 180/1A |
| 6.00 kJ/m² @Temperature -30.0 °C |
2.86 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |
| Charpy Impact, Notched | 0.700 J/cm² | 3.33 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 70.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
38.9 µin/in-°F @Temperature -22.0 - 86.0 °F |
TMA |
| CTE, linear, Parallel to Flow | 61.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
33.9 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 68.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
37.8 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 136 °C @Thickness 6.40 mm |
277 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 119 °C | 246 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 125 °C @Thickness 6.40 mm |
257 °F @Thickness 0.252 in |
unannealed; ASTM D648 | |
| Vicat Softening Point | 139 °C | 282 °F | Rate B/120; ISO 306 |
| UL RTI, Electrical | 110 °C | 230 °F | UL 746B |
| UL RTI, Mechanical with Impact | 105 °C | 221 °F | UL 746B |
| UL RTI, Mechanical without Impact | 110 °C | 230 °F | UL 746B |
| Flammability, UL94 | V-2 @Thickness 0.400 mm |
V-2 @Thickness 0.0157 in |
UL 94 by SABIC-IP |
| V-0 @Thickness 0.750 mm |
V-0 @Thickness 0.0295 in |
UL 94 | |
| 5VB @Thickness 2.50 mm |
5VB @Thickness 0.0984 in |
UL 94 by SABIC-IP | |
| 5VA @Thickness 2.50 mm |
5VA @Thickness 0.0984 in |
UL 94 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Strength | 49.0 kV/mm @Thickness 3.20 mm |
1240 kV/in @Thickness 0.126 in |
in oil; IEC 60243-1 |
| Comparative Tracking Index | 250 V | 250 V | IEC 60112 |
| Hot Wire Ignition, HWI | >= 120 sec | >= 120 sec | UL 746A |
| High Amp Arc Ignition, HAI | >= 120 arcs | >= 120 arcs | UL 746A |
| High Voltage Arc-Tracking Rate, HVTR | >= 150 mm/min | >= 5.91 in/min | UL 746A |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Ball Pressure Test, 125°C +/- 2°C | Pass | IEC 60695-10-2 |
Users viewing this material also viewed the following: