SABIC Innovative Plastics NORYL PKN4752 PPE+PS (Asia Pacific)
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Noryl |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics NORYL PKN4752 PPE+PS (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PPE+PS. Translucent. FDA compliant. High heat. Extrusion. Microwavable. Food, electrical/electronic packaging uses.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.08 g/cc | 1.08 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0060 - 0.0090 cm/cm @Thickness 3.20 mm |
0.0060 - 0.0090 in/in @Thickness 0.126 in |
SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 73.0 MPa | 10600 psi | Type I, 50 mm/min; ASTM D638 |
| Tensile Strength, Yield | 86.0 MPa | 12500 psi | Type I, 50 mm/min; ASTM D638 |
| Elongation at Break | 15 % | 15 % | Type I, 50 mm/min; ASTM D638 |
| Elongation at Yield | 6.0 % | 6.0 % | Type I, 50 mm/min; ASTM D638 |
| Tensile Modulus | 3.00 GPa | 435 ksi | 50 mm/min; ASTM D638 |
| Flexural Yield Strength | 136 MPa | 19700 psi | 2.6 mm/min, 100 mm span; ASTM D790 |
| 144 MPa | 20900 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 2.94 GPa | 426 ksi | 2.6 mm/min, 100 mm span; ASTM D790 |
| 3.15 GPa | 457 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.320 J/cm | 0.599 ft-lb/in | ASTM D256 |
| Dart Drop, Total Energy | 6.00 J @Temperature 23.0 °C |
4.43 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 63.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
35.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| CTE, linear, Transverse to Flow | 55.8 µm/m-°C @Temperature -40.0 - 40.0 °C |
31.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| Deflection Temperature at 0.46 MPa (66 psi) | 160 °C @Thickness 3.20 mm |
320 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 151 °C @Thickness 3.20 mm |
304 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| 151 °C @Thickness 6.40 mm |
304 °F @Thickness 0.252 in |
unannealed; ASTM D648 | |
| Vicat Softening Point | 173 °C | 343 °F | Rate B/50; ASTM D1525 |
Users viewing this material also viewed the following:
- Multibase Nylex™ 2185 HFX Natural Polyamide + PP
- Albis Plastics Tedur® L V 9300-1 PPS, 40% Glass Fiber/Glass Bead (discontinued **)
- Shakespeare FL-8 Fluorocarbon PVDF Fishing Line, 30 lb
- UBE UBESTA® 3030U Nylon 12 (After Hexane for 500 hours)
- EMS-Grivory Grivory® TSG-50 PA666-GF50
- Engineered Plastics EPPC 2014B Polycarbonate
- 3M Scotchcal™ 1000LF-114 Graphic Film
- Amco Amalloy® B1017 Polymer Alloy
- Arkema Group Orgalloy® P 60AD Nylon (Conditioned)
- Sax Polymers SAXALEN PPH121GK30 Polypropylene Homopolymer, 30% Glass Filled
Copyright © lookpolymers.com All Rights Reserved