SABIC Innovative Plastics NORYL PPX PPX7200 PPE+PP+PS (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polypropylene (PP) , Polystyrene (PS)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Noryl PPX
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics NORYL PPX PPX7200 PPE+PP+PS (Europe-Africa-Middle East).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PP+PPE+PS. Improved chemical resistance and surface aesthetics in injection molded applications. NSF61-capable. UL-94 HB listed.
Physical Properties Metric English Comments
Specific Gravity 0.990 g/cc
0.990 g/cc
ASTM D792
Density 0.990 g/cc
0.0358 lb/in³
ISO 1183
Moisture Absorption 0.0200 %
0.0200 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.050 %
0.050 %
ISO 62
Linear Mold Shrinkage, Flow 0.0060 - 0.0080 cm/cm

@Thickness 3.20 mm
0.0060 - 0.0080 in/in

@Thickness 0.126 in
SABIC Method
Linear Mold Shrinkage, Transverse 0.0060 - 0.0080 cm/cm

@Thickness 3.20 mm
0.0060 - 0.0080 in/in

@Thickness 0.126 in
SABIC Method
Melt Flow 16 g/10 min

@Load 5.00 kg,
Temperature 260 °C
16 g/10 min

@Load 11.0 lb,
Temperature 500 °F
ASTM D1238
Melt Index of Compound 18 g/10 min

@Load 5.00 kg,
Temperature 260 °C
18 g/10 min

@Load 11.0 lb,
Temperature 500 °F
MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 27.0 MPa
3920 psi
Type I, 50 mm/min; ASTM D638
28.0 MPa
4060 psi
50 mm/min; ISO 527
Tensile Strength, Yield 33.0 MPa
4790 psi
Type I, 50 mm/min; ASTM D638
34.0 MPa
4930 psi
50 mm/min; ISO 527
Elongation at Break 115 %
115 %
50 mm/min; ISO 527
130 %
130 %
Type I, 50 mm/min; ASTM D638
Elongation at Yield 8.2 %
8.2 %
50 mm/min; ISO 527
10 %
10 %
Type I, 50 mm/min; ASTM D638
Tensile Modulus 1.24 GPa
180 ksi
50 mm/min; ASTM D638
1.67 GPa
242 ksi
1 mm/min; ISO 527
Flexural Yield Strength 48.0 MPa
6960 psi
1.3 mm/min, 50 mm span; ASTM D790
48.0 MPa
6960 psi
2 mm/min; ISO 178
Flexural Modulus 1.44 GPa
209 ksi
1.3 mm/min, 50 mm span; ASTM D790
1.60 GPa
232 ksi
2 mm/min; ISO 178
Izod Impact, Notched 1.49 J/cm
2.79 ft-lb/in
ASTM D256
Izod Impact, Unnotched 14.41 J/cm
27.00 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 14.0 kJ/m²
6.66 ft-lb/in²
80*10*4; ISO 180/1A
8.00 kJ/m²

@Temperature -30.0 °C
3.81 ft-lb/in²

@Temperature -22.0 °F
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) NB
NB
80*10*4; ISO 180/1U
NB

@Temperature -30.0 °C
NB

@Temperature -22.0 °F
80*10*4; ISO 180/1U
Charpy Impact Unnotched NB
NB
Edgew 80*10*4 sp=62mm; ISO 179/1eU
8.00 J/cm²

@Temperature -30.0 °C
38.1 ft-lb/in²

@Temperature -22.0 °F
Edgew 80*10*4 sp=62mm; ISO 179/1eU
Charpy Impact, Notched 1.20 J/cm²
5.71 ft-lb/in²
Edgew 80*10*4 sp=62mm; ISO 179/1eA
0.600 J/cm²

@Temperature -30.0 °C
2.86 ft-lb/in²

@Temperature -22.0 °F
Edgew 80*10*4 sp=62mm; ISO 179/1eA
Dart Drop, Total Energy 36.0 J

@Temperature 23.0 °C
26.6 ft-lb

@Temperature 73.4 °F
ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 99.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
55.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
99.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
55.0 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
CTE, linear, Transverse to Flow 108 µm/m-°C

@Temperature -40.0 - 40.0 °C
60.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
108 µm/m-°C

@Temperature -40.0 - 40.0 °C
60.0 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 110 °C

@Thickness 3.20 mm
230 °F

@Thickness 0.126 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 73.0 °C
163 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
71.0 °C

@Thickness 3.20 mm
160 °F

@Thickness 0.126 in
unannealed; ASTM D648
Vicat Softening Point 103 °C
217 °F
Rate B/50; ISO 306
107 °C
225 °F
Rate B/120; ISO 306
146 °C
295 °F
Rate B/50; ASTM D1525