SABIC Innovative Plastics NORYL PVX0800 PPE

Category Polymer , Thermoplastic , Polyphenylene Ether/PPO
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Noryl
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics NORYL PVX0800 PPE.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
NORYL* PVX0800 resin is a high flow, V0 = 1.5 mm grade, suitable for a variety of electronics applications.
Physical Properties Metric English Comments
Specific Gravity 1.11 g/cc
1.11 g/cc
ASTM D792
Moisture Absorption 0.0700 %
0.0700 %
23°C / 50% RH; ISO 62
Viscosity 98000 cP
98000 cP
Melt Viscosity, 280°C, 1500 sec-1; ISO 11443
Melt Flow 6.0 g/10 min

@Load 5.00 kg,
Temperature 230 °C
6.0 g/10 min

@Load 11.0 lb,
Temperature 446 °F
ASTM D1238
Melt Index of Compound 22 g/10 min

@Load 5.00 kg,
Temperature 260 °C
22 g/10 min

@Load 11.0 lb,
Temperature 500 °F
MVR [cm^3/10 min]; ISO 1133
47 g/10 min

@Load 5.00 kg,
Temperature 280 °C
47 g/10 min

@Load 11.0 lb,
Temperature 536 °F
MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 42.0 MPa
6090 psi
50 mm/min; ISO 527
43.0 MPa
6240 psi
Type I, 50 mm/min; ASTM D638
Tensile Strength, Yield 53.0 MPa
7690 psi
50 mm/min; ISO 527
57.0 MPa
8270 psi
Type I, 50 mm/min; ASTM D638
Elongation at Break 15 %
15 %
Type I, 50 mm/min; ASTM D638
26.6 %
26.6 %
50 mm/min; ISO 527
Elongation at Yield 2.7 %
2.7 %
50 mm/min; ISO 527
3.0 %
3.0 %
Type I, 50 mm/min; ASTM D638
Tensile Modulus 2.58 GPa
374 ksi
1 mm/min; ISO 527
2.67 GPa
387 ksi
50 mm/min; ASTM D638
Flexural Yield Strength 83.0 MPa
12000 psi
2 mm/min; ISO 178
86.0 MPa
12500 psi
1.3 mm/min, 50 mm span; ASTM D790
88.0 MPa
12800 psi
6.4 mm; ASTM D790
Flexural Modulus 2.39 GPa
347 ksi
2 mm/min; ISO 178
2.70 GPa
392 ksi
1.3 mm/min, 50 mm span; ASTM D790
2.70 GPa
392 ksi
6.4 mm; ASTM D790
Izod Impact, Notched 2.50 J/cm
4.68 ft-lb/in
ASTM D256
1.00 J/cm

@Temperature -30.0 °C
1.87 ft-lb/in

@Temperature -22.0 °F
ASTM D256
Izod Impact, Notched (ISO) 10.0 kJ/m²
4.76 ft-lb/in²
80*10*4; ISO 180/1A
7.00 kJ/m²

@Temperature -30.0 °C
3.33 ft-lb/in²

@Temperature -22.0 °F
80*10*4; ISO 180/1A
Charpy Impact Unnotched 0.600 J/cm²

@Temperature -30.0 °C
2.86 ft-lb/in²

@Temperature -22.0 °F
Edgew 80*10*4 sp=62mm; ISO 179/1eU
Charpy Impact, Notched 1.00 J/cm²
4.76 ft-lb/in²
Edgew 80*10*4 sp=62mm; ISO 179/1eA
Dart Drop, Total Energy 30.0 J

@Temperature 23.0 °C
22.1 ft-lb

@Temperature 73.4 °F
ASTM D3763
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 88.0 °C

@Thickness 3.20 mm
190 °F

@Thickness 0.126 in
unannealed; ASTM D648
92.0 °C

@Thickness 6.40 mm
198 °F

@Thickness 0.252 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 79.0 °C
174 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
78.0 °C

@Thickness 3.20 mm
172 °F

@Thickness 0.126 in
unannealed; ASTM D648
82.0 °C

@Thickness 6.40 mm
180 °F

@Thickness 0.252 in
unannealed; ASTM D648
Vicat Softening Point 98.0 °C
208 °F
Rate B/50; ASTM D1525
UL RTI, Electrical 65.0 °C
149 °F
UL 746B
UL RTI, Mechanical with Impact 65.0 °C
149 °F
UL 746B
UL RTI, Mechanical without Impact 65.0 °C
149 °F
UL 746B
Flammability, UL94 V-0

@Thickness 1.50 mm
V-0

@Thickness 0.0591 in
UL 94 by SABIC-IP
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+16 ohm-cm
1.00e+16 ohm-cm
IEC 60093
Comparative Tracking Index 250 V
250 V
IEC 60112
Hot Wire Ignition, HWI 30 - 60 sec
30 - 60 sec
UL 746A
High Amp Arc Ignition, HAI 15 - 30 arcs
15 - 30 arcs
UL 746A