SABIC Innovative Plastics NORYL PVX0901 PPE+PS (Asia Pacific)

Category Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Noryl
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics NORYL PVX0901 PPE+PS (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Multi purpose V1 grade
Physical Properties Metric English Comments
Specific Gravity 1.10 g/cc
1.10 g/cc
ASTM D792
Density 1.10 g/cc
0.0397 lb/in³
ISO 1183
Moisture Absorption 0.0400 %
0.0400 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.24 %
0.24 %
ISO 62
Linear Mold Shrinkage, Flow 0.0050 - 0.0070 cm/cm

@Thickness 3.20 mm
0.0050 - 0.0070 in/in

@Thickness 0.126 in
SABIC Method
Melt Flow 50 g/10 min

@Load 5.00 kg,
Temperature 280 °C
50 g/10 min

@Load 11.0 lb,
Temperature 536 °F
ASTM D1238
Melt Index of Compound 52 g/10 min

@Load 5.00 kg,
Temperature 280 °C
52 g/10 min

@Load 11.0 lb,
Temperature 536 °F
MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 44.0 MPa
6380 psi
50 mm/min; ISO 527
45.0 MPa
6530 psi
Type I, 50 mm/min; ASTM D638
Tensile Strength, Yield 59.0 MPa
8560 psi
50 mm/min; ISO 527
60.0 MPa
8700 psi
Type I, 50 mm/min; ASTM D638
Elongation at Break 6.6 %
6.6 %
Type I, 50 mm/min; ASTM D638
8.8 %
8.8 %
50 mm/min; ISO 527
Elongation at Yield 3.3 %
3.3 %
Type I, 50 mm/min; ASTM D638
3.3 %
3.3 %
50 mm/min; ISO 527
Tensile Modulus 2.44 GPa
354 ksi
1 mm/min; ISO 527
2.50 GPa
363 ksi
5 mm/min; ASTM D638
Flexural Yield Strength 86.0 MPa
12500 psi
1.3 mm/min, 50 mm span; ASTM D790
95.0 MPa
13800 psi
2 mm/min; ISO 178
Flexural Modulus 2.30 GPa
334 ksi
1.3 mm/min, 50 mm span; ASTM D790
2.45 GPa
355 ksi
2 mm/min; ISO 178
Izod Impact, Notched 1.75 J/cm
3.28 ft-lb/in
ASTM D256
0.800 J/cm

@Temperature -30.0 °C
1.50 ft-lb/in

@Temperature -22.0 °F
ASTM D256
Izod Impact, Notched (ISO) 13.0 kJ/m²
6.19 ft-lb/in²
80*10*4; ISO 180/1A
10.0 kJ/m²

@Temperature -30.0 °C
4.76 ft-lb/in²

@Temperature -22.0 °F
80*10*4; ISO 180/1A
Charpy Impact, Notched 1.20 J/cm²
5.71 ft-lb/in²
Edgew 80*10*4 sp=62mm; ISO 179/1eA
Dart Drop, Total Energy 37.0 J

@Temperature 23.0 °C
27.3 ft-lb

@Temperature 73.4 °F
ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 74.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
41.1 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
75.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
41.7 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
CTE, linear, Transverse to Flow 78.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
43.3 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
81.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
45.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
Deflection Temperature at 1.8 MPa (264 psi) 89.0 °C
192 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
92.0 °C

@Thickness 3.20 mm
198 °F

@Thickness 0.126 in
unannealed; ASTM D648
92.0 °C

@Thickness 6.40 mm
198 °F

@Thickness 0.252 in
unannealed; ASTM D648
Vicat Softening Point 109 °C
228 °F
Rate B/120; ISO 306
116 °C
241 °F
Rate B/50; ASTM D1525
116 °C
241 °F
Rate B/50; ISO 306
Flammability, UL94 V-1

@Thickness 1.50 mm
V-1

@Thickness 0.0591 in
UL 94 by SABIC-IP