SABIC Innovative Plastics NORYL PX1390 PPE+PS (Asia Pacific)

Category Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Noryl
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics NORYL PX1390 PPE+PS (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Automotive applications, primarily. Excellent electrical properties, easy processability, high heat, 295F (146C) DTUL.
Physical Properties Metric English Comments
Specific Gravity 1.06 g/cc
1.06 g/cc
ASTM D792
Water Absorption 0.10 %

@Time 86400 sec
0.10 %

@Time 24.0 hour
ASTM D570
Linear Mold Shrinkage, Flow 0.0050 - 0.0070 cm/cm

@Thickness 3.20 mm
0.0050 - 0.0070 in/in

@Thickness 0.126 in
SABIC Method
Mechanical Properties Metric English Comments
Tensile Strength, Yield 62.0 MPa
8990 psi
Type I, 50 mm/min; ASTM D638
Elongation at Break 30 %
30 %
Type I, 50 mm/min; ASTM D638
Flexural Yield Strength 99.0 MPa
14400 psi
2.6 mm/min, 100 mm span; ASTM D790
Flexural Modulus 2.27 GPa
329 ksi
2.6 mm/min, 100 mm span; ASTM D790
Izod Impact, Notched 2.88 J/cm
5.40 ft-lb/in
ASTM D256
1.60 J/cm

@Temperature -40.0 °C
3.00 ft-lb/in

@Temperature -40.0 °F
ASTM D256
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 72.0 µm/m-°C

@Temperature 0.000 - 100 °C
40.0 µin/in-°F

@Temperature 32.0 - 212 °F
ASTM E 831
Deflection Temperature at 0.46 MPa (66 psi) 154 °C

@Thickness 6.40 mm
309 °F

@Thickness 0.252 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 146 °C

@Thickness 6.40 mm
295 °F

@Thickness 0.252 in
unannealed; ASTM D648
UL RTI, Electrical 50.0 °C
122 °F
UL 746B
UL RTI, Mechanical with Impact 50.0 °C
122 °F
UL 746B
UL RTI, Mechanical without Impact 50.0 °C
122 °F
UL 746B
Flammability, UL94 HB

@Thickness 0.710 mm
HB

@Thickness 0.0280 in
UL 94