SABIC Innovative Plastics NORYL PX500 PPE (Asia Pacific)

Category Polymer , Thermoplastic , Polyphenylene Ether/PPO
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Noryl
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics NORYL PX500 PPE (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Noryl PX500 is an unfilled modified polyphenylene ether resin capable of multiple conversion routes. This resin is designed for lower odor during conversion than many standard modified PPE resins. Noryl PX500 provides an exceptional balance of high heat performance and dimensional stability with flow and may be an excellent material candidate for IC tray applications.
Physical Properties Metric English Comments
Specific Gravity 1.06 g/cc
1.06 g/cc
ASTM D792
Density 1.06 g/cc
0.0383 lb/in³
ISO 1183
Moisture Absorption 0.0600 %
0.0600 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.23 %
0.23 %
ISO 62
Linear Mold Shrinkage, Flow 0.0080 - 0.0090 cm/cm

@Thickness 3.20 mm
0.0080 - 0.0090 in/in

@Thickness 0.126 in
SABIC Method
Linear Mold Shrinkage, Transverse 0.0080 - 0.0090 cm/cm

@Thickness 3.20 mm
0.0080 - 0.0090 in/in

@Thickness 0.126 in
SABIC Method
Melt Index of Compound 21 g/10 min

@Load 5.00 kg,
Temperature 320 °C
21 g/10 min

@Load 11.0 lb,
Temperature 608 °F
MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Hardness, Shore D 82
82
30S reading; ASTM D2240
Tensile Strength at Break 10.0 MPa
1450 psi
50 mm/min; ISO 527
56.0 MPa
8120 psi
Type I, 50 mm/min; ASTM D638
Tensile Strength, Yield 70.0 MPa
10200 psi
50 mm/min; ISO 527
71.0 MPa
10300 psi
Type I, 50 mm/min; ASTM D638
Elongation at Break 5.1 %
5.1 %
50 mm/min; ISO 527
35 %
35 %
Type I, 50 mm/min; ASTM D638
Elongation at Yield 5.1 %
5.1 %
50 mm/min; ISO 527
5.4 %
5.4 %
Type I, 50 mm/min; ASTM D638
Tensile Modulus 2.40 GPa
348 ksi
50 mm/min; ASTM D638
2.50 GPa
363 ksi
1 mm/min; ISO 527
Flexural Yield Strength 110 MPa
16000 psi
2 mm/min; ISO 178
Flexural Modulus 2.53 GPa
367 ksi
2 mm/min; ISO 178
2.59 GPa
376 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 0.800 J/cm
1.50 ft-lb/in
ASTM D256
Izod Impact, Notched (ISO) 8.00 kJ/m²
3.81 ft-lb/in²
80*10*4; ISO 180/1A
Charpy Impact, Notched 0.900 J/cm²
4.28 ft-lb/in²
Edgew 80*10*4 sp=62mm; ISO 179/1eA
Dart Drop, Total Energy 58.0 J

@Temperature 23.0 °C
42.8 ft-lb

@Temperature 73.4 °F
ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 71.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
39.4 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
71.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
39.4 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
CTE, linear, Transverse to Flow 79.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
43.9 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
79.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
43.9 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
Deflection Temperature at 1.8 MPa (264 psi) 169 °C
336 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
170 °C

@Thickness 3.20 mm
338 °F

@Thickness 0.126 in
unannealed; ASTM D648
Vicat Softening Point 192 °C
378 °F
Rate B/50; ASTM D1525
192 °C
378 °F
Rate B/50; ISO 306
193 °C
379 °F
Rate B/120; ISO 306