SABIC Innovative Plastics NORYL RN0612 PPE+HIPS (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Noryl
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics NORYL RN0612 PPE+HIPS (Europe-Africa-Middle East).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Noryl RN0612 is an unfilled Post Consumer recycle (PCR) based injection moldable modified polyphenylene ether resin comprising at least 30% PCR styrenic series resin content. Designed for good dimensional stability and high flow, this resin also uses non-chlorinated, non-brominated FR additives with a specific density of 1.1 g/cm^3. Noryl RN0612 may be an excellent material candidate for flat panel TV enclosure applications requiring good rheological properties, heat resistance, hydrolysis resistance and low density.
Physical Properties Metric English Comments
Specific Gravity 1.11 g/cc
1.11 g/cc
ASTM D792
Density 1.11 g/cc
0.0401 lb/in³
ISO 1183
Melt Index of Compound 13 g/10 min

@Load 1.20 kg,
Temperature 280 °C
13 g/10 min

@Load 2.65 lb,
Temperature 536 °F
MVR [cm^3/10 min]; ISO 1133
34 g/10 min

@Load 2.16 kg,
Temperature 280 °C
34 g/10 min

@Load 4.76 lb,
Temperature 536 °F
MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 42.0 MPa
6090 psi
50 mm/min; ISO 527
43.0 MPa
6240 psi
Type I, 50 mm/min; ASTM D638
Tensile Strength, Yield 42.0 MPa
6090 psi
50 mm/min; ISO 527
43.0 MPa
6240 psi
Type I, 50 mm/min; ASTM D638
Elongation at Break 15 %
15 %
Type I, 50 mm/min; ASTM D638
17 %
17 %
50 mm/min; ISO 527
Elongation at Yield 1.0 %
1.0 %
Type I, 50 mm/min; ASTM D638
1.0 %
1.0 %
50 mm/min; ISO 527
Tensile Modulus 2.10 GPa
305 ksi
50 mm/min; ASTM D638
2.10 GPa
305 ksi
1 mm/min; ISO 527
Flexural Yield Strength 60.0 MPa
8700 psi
1.3 mm/min, 50 mm span; ASTM D790
64.0 MPa
9280 psi
2 mm/min; ISO 178
Flexural Modulus 2.10 GPa
305 ksi
1.3 mm/min, 50 mm span; ASTM D790
2.10 GPa
305 ksi
2 mm/min; ISO 178
Izod Impact, Notched 0.520 J/cm
0.974 ft-lb/in
ASTM D256
0.410 J/cm

@Temperature -30.0 °C
0.768 ft-lb/in

@Temperature -22.0 °F
ASTM D256
Izod Impact, Notched (ISO) 5.00 kJ/m²
2.38 ft-lb/in²
80*10*4; ISO 180/1A
4.00 kJ/m²

@Temperature -30.0 °C
1.90 ft-lb/in²

@Temperature -22.0 °F
80*10*4; ISO 180/1A
Charpy Impact, Notched 0.400 J/cm²
1.90 ft-lb/in²
Edgew 80*10*4 sp=62mm; ISO 179/1eA
0.300 J/cm²

@Temperature -30.0 °C
1.43 ft-lb/in²

@Temperature -22.0 °F
Edgew 80*10*4 sp=62mm; ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 94.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
52.2 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
94.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
52.2 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
CTE, linear, Transverse to Flow 96.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
53.3 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
96.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
53.3 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 90.0 °C

@Thickness 3.20 mm
194 °F

@Thickness 0.126 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 74.0 °C
165 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
78.0 °C

@Thickness 3.20 mm
172 °F

@Thickness 0.126 in
unannealed; ASTM D648
Vicat Softening Point 95.0 °C
203 °F
Rate B/50; ASTM D1525
95.0 °C
203 °F
Rate B/50; ISO 306
98.0 °C
208 °F
Rate B/120; ISO 306
UL RTI, Electrical 65.0 °C
149 °F
UL 746B
UL RTI, Mechanical with Impact 65.0 °C
149 °F
UL 746B
UL RTI, Mechanical without Impact 65.0 °C
149 °F
UL 746B
Flammability, UL94 V-1

@Thickness 1.50 mm
V-1

@Thickness 0.0591 in
UL 94
V-0

@Thickness 3.00 mm
V-0

@Thickness 0.118 in
UL 94
Glow Wire Test 725 °C
1340 °F
IEC 60695-2-13
725 °C
1340 °F
IEC 60695-2-13
725 °C
1340 °F
IEC 60695-2-13
960 °C

@Thickness 1.00 mm
1760 °F

@Thickness 0.0394 in
IEC 60695-2-12
Electrical Properties Metric English Comments
Volume Resistivity 3.00e+16 ohm-cm
3.00e+16 ohm-cm
ASTM D257
3.00e+16 ohm-cm
3.00e+16 ohm-cm
IEC 60093
Surface Resistance 1.00e+16 ohm
1.00e+16 ohm
ASTM D257
1.00e+16 ohm
1.00e+16 ohm
ROA; IEC 60093
Dielectric Constant 2.76

@Frequency 1.00e+6 Hz
2.76

@Frequency 1.00e+6 Hz
ASTM D150
2.8

@Frequency 1.00e+6 Hz
2.8

@Frequency 1.00e+6 Hz
IEC 60250
Dissipation Factor 0.0035

@Frequency 1.00e+6 Hz
0.0035

@Frequency 1.00e+6 Hz
ASTM D150
0.0035

@Frequency 1.00e+6 Hz
0.0035

@Frequency 1.00e+6 Hz
IEC 60250
Comparative Tracking Index 250 V
250 V
IEC 60112
250 - 400 V
250 - 400 V
UL 746A
Hot Wire Ignition, HWI 15 - 30 sec
15 - 30 sec
UL 746A