SABIC Innovative Plastics NORYL WCD915 PPE-TPE (Asia Pacific)
| Category | Polymer , Thermoplastic , Elastomer, TPE , Polyphenylene Ether/PPO |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Noryl |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics NORYL WCD915 PPE-TPE (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Flexible and non-halogenated flame retardant extrusion grade intended for evaluation in applications such as insulation materials. Flame retardant performance capable of meeting UL 1581 VW-1 requirement. 90C or 105C temperature rating as defined by UL 62 TPE category. 91 Shore A hardness. Processing typically conducted on standard extrusion equipment. UL 1581 tests conducted on 2.0 mm wire with 0.12 mm x 20 stranded copper conductor.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.03 g/cc | 1.03 g/cc | ASTM D792 |
| Melt Flow | 9.0 g/10 min @Load 10.0 kg, Temperature 250 °C |
9.0 g/10 min @Load 22.0 lb, Temperature 482 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 91 | 91 | 30S reading; ASTM D2240 |
| Tensile Strength at Break | 14.0 MPa | 2030 psi | 50 mm/min; ISO 527 |
| 15.0 MPa | 2180 psi | Type I, 50 mm/min; ASTM D638 | |
| 23.0 MPa | 3340 psi | after 7days @136°C; UL 1581 | |
| 24.0 MPa | 3480 psi | UL 1581 | |
| Elongation at Break | 155 % | 155 % | 50 mm/min; ISO 527 |
| 170 % | 170 % | Type I, 50 mm/min; ASTM D638 | |
| 230 % | 230 % | after 7days @136°C; UL 1581 | |
| 265 % | 265 % | UL 1581 | |
| Flexural Modulus | 0.0700 GPa | 10.2 ksi | 12.5 mm/min; ISO 178 |
| 0.100 GPa | 14.5 ksi | 12.5 mm/min, 100 mm span; ASTM D790 | |
| Heat Distortion | 5.0 % @Load 0.250 kg, Temperature 121 °C |
5.0 % @Load 0.551 lb, Temperature 250 °F |
UL 1581 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Brittleness Temperature | <= -40.0 °C | <= -40.0 °F | ASTM D746 |
| Oxygen Index | 28 % | 28 % | ISO 4589 |
| Glow Wire Test | 825 °C | 1520 °F | IEC 60695-2-13 |
| 960 °C @Thickness 3.00 mm |
1760 °F @Thickness 0.118 in |
IEC 60695-2-12 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 3.30e+16 ohm-cm | 3.30e+16 ohm-cm | ASTM D257 |
| Dielectric Constant | 2.6 @Frequency 1.00e+6 Hz |
2.6 @Frequency 1.00e+6 Hz |
ASTM D150 |
| Dielectric Strength | 22.0 kV/mm @Thickness 2.00 mm |
559 kV/in @Thickness 0.0787 in |
in oil; IEC 60243-1 |
| Dissipation Factor | 0.033 @Frequency 1.00e+6 Hz |
0.033 @Frequency 1.00e+6 Hz |
ASTM D150 |
| Comparative Tracking Index | 600 V | 600 V | IEC 60112 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Smoke Density on 0.5mm plaque, Flame, Ds, max | 115 | ASTM E 662 |
| Smoke Density on 0.5mm plaque, Non-flame, Ds, max | 49 | ASTM E 662 |
| VW-1 | Pass | UL 1581 |