SABIC Innovative Plastics Noryl GTX APS8740 PPE+PPS (Asia Pacific)

Category Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polyphenylene Sulfide (PPS)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name NORYL GTX
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Noryl GTX APS8740 PPE+PPS (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Noryl* APS8740 resin is a glass filled, high performance blend of PPE/PPS that exhibits an excellent balance of high-heat resistance, strength, flame retardant, and conductivity. This grade can be electro-statically painted or powder coated without the need for a conductive primer. The resin is injection moldable and only available in black.This data was supplied by SABIC-IP for the Asia Pacific region.
Physical Properties Metric English Comments
Specific Gravity 1.62 g/cc
1.62 g/cc
ASTM D 792
Density 1.62 g/cc
0.0585 lb/in³
ISO 1183
Moisture Absorption at Equilibrium 0.00 %
0.00 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.020 %

@Temperature 23.0 °C
0.020 %

@Temperature 73.4 °F
ISO 62
Linear Mold Shrinkage, Flow 0.0030 - 0.0080 cm/cm

@Thickness 3.20 mm
0.0030 - 0.0080 in/in

@Thickness 0.126 in
SABIC Method
Melt Flow 16 g/10 min

@Load 5.00 kg,
Temperature 300 °C
16 g/10 min

@Load 11.0 lb,
Temperature 572 °F
ASTM D 1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 79.0 MPa
11500 psi
Type I, 5 mm/min; ASTM D 638
89.0 MPa
12900 psi
5 mm/min; ISO 527
Tensile Strength, Yield 79.0 MPa
11500 psi
Type I, 5 mm/min; ASTM D 638
89.0 MPa
12900 psi
5 mm/min; ISO 527
Elongation at Break 0.60 %
0.60 %
Type I, 5 mm/min; ASTM D 638
0.60 %
0.60 %
5 mm/min; ISO 527
Elongation at Yield 0.60 %
0.60 %
Type I, 5 mm/min; ASTM D 638
0.60 %
0.60 %
5 mm/min; ISO 527
Tensile Modulus 14.99 GPa
2174 ksi
1 mm/min; ISO 527
16.3 GPa
2360 ksi
5 mm/min; ASTM D 638
Flexural Yield Strength 118 MPa
17100 psi
1.3 mm/min, 50 mm span; ASTM D 790
Flexural Modulus 12.74 GPa
1848 ksi
1.3 mm/min, 50 mm span; ASTM D 790
13.64 GPa
1978 ksi
2 mm/min; ISO 178
Izod Impact, Notched 0.340 J/cm

@Temperature 23.0 °C
0.637 ft-lb/in

@Temperature 73.4 °F
ASTM D 256
0.370 J/cm

@Temperature -30.0 °C
0.693 ft-lb/in

@Temperature -22.0 °F
ASTM D 256
Izod Impact, Notched (ISO) 3.00 kJ/m²

@Temperature 23.0 °C
1.43 ft-lb/in²

@Temperature 73.4 °F
80*10*4; ISO 180/1A
4.00 kJ/m²

@Temperature -30.0 °C
1.90 ft-lb/in²

@Temperature -22.0 °F
80*10*4; ISO 180/1A
Charpy Impact, Notched 0.400 J/cm²

@Temperature 23.0 °C
1.90 ft-lb/in²

@Temperature 73.4 °F
V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA
Impact Test 3.00 J

@Temperature 23.0 °C
2.21 ft-lb

@Temperature 73.4 °F
Instrumented Impact Total Energy; ASTM D 3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 27.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
15.0 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
27.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
15.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
CTE, linear, Transverse to Flow 27.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
15.0 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
49.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
27.2 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
Deflection Temperature at 1.8 MPa (264 psi) 231 °C
448 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
234 °C

@Thickness 3.20 mm
453 °F

@Thickness 0.126 in
unannealed; ASTM D 648
Vicat Softening Point 231 °C
448 °F
Rate B/50; ASTM D 1525
233 °C
451 °F
Rate B/120; ISO 306
Flammability, UL94 HB

@Thickness 2.00 mm
HB

@Thickness 0.0787 in
UL 94
HB

@Thickness 2.00 mm
HB

@Thickness 0.0787 in
UL 94 by SABIC-IP
V-2

@Thickness 0.500 mm
V-2

@Thickness 0.0197 in
UL 94
V-2

@Thickness 0.500 mm
V-2

@Thickness 0.0197 in
UL 94 by SABIC-IP
V-1

@Thickness 0.500 mm
V-1

@Thickness 0.0197 in
UL 94 by SABIC-IP
V-1

@Thickness 0.500 mm
V-1

@Thickness 0.0197 in
UL 94
V-0

@Thickness 2.00 mm
V-0

@Thickness 0.0787 in
UL 94 by SABIC-IP
V-0

@Thickness 2.00 mm
V-0

@Thickness 0.0787 in
UL 94
5VB

@Thickness 0.500 mm
5VB

@Thickness 0.0197 in
UL 94 by SABIC-IP
5VA

@Thickness 0.500 mm
5VA

@Thickness 0.0197 in
UL 94 by SABIC-IP
Electrical Properties Metric English Comments
Volume Resistivity 25000 ohm-cm
25000 ohm-cm
ASTM D 257
25000 ohm-cm
25000 ohm-cm
IEC 60093
Comparative Tracking Index 100 V
100 V
IEC 60112