SABIC Innovative Plastics Noryl GTX GTX965 PPE+PA66
| Category | Polymer , Thermoplastic , Polyester, TP , Polyphenylene Ether/PPO |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | NORYL GTX |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Noryl GTX GTX965 PPE+PA66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
NORYL GTX965 is a mineral reinforced PPE/PA blend. It offers excellent surface appearance, processability and dimensional stability at elevated temperatures. The best molding condition for good appearance is 540 F (melt) and 170 - 190 F (mold).This data was supplied by SABIC-IP for the Americas region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.25 g/cc | 1.25 g/cc | ASTM D 792 |
| Density | 1.25 g/cc | 0.0452 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 0.10 % | 0.10 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 1.1 % @Temperature 23.0 °C |
1.1 % @Temperature 73.4 °F |
ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0080 - 0.012 cm/cm | 0.0080 - 0.012 in/in | on tensile bar; SABIC Method |
| 0.0080 - 0.010 cm/cm @Thickness 3.20 mm |
0.0080 - 0.010 in/in @Thickness 0.126 in |
SABIC Method | |
| Linear Mold Shrinkage, Transverse | 0.0070 - 0.0090 cm/cm @Thickness 3.20 mm |
0.0070 - 0.0090 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 11 g/10 min @Load 5.00 kg, Temperature 280 °C |
11 g/10 min @Load 11.0 lb, Temperature 536 °F |
[cm^3/10 min] Melt Volume Rate; ISO 1133 |
| 12.7 g/10 min @Load 5.00 kg, Temperature 280 °C |
12.7 g/10 min @Load 11.0 lb, Temperature 536 °F |
ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 60.0 MPa | 8700 psi | Type I, 5 mm/min; ASTM D 638 |
| 60.0 MPa | 8700 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 60.0 MPa | 8700 psi | 5 mm/min; ISO 527 |
| 61.0 MPa | 8850 psi | Type I, 5 mm/min; ASTM D 638 | |
| Elongation at Break | 7.0 % | 7.0 % | 5 mm/min; ISO 527 |
| 9.0 % | 9.0 % | Type I, 5 mm/min; ASTM D 638 | |
| Elongation at Yield | 3.0 % | 3.0 % | 5 mm/min; ISO 527 |
| 4.0 % | 4.0 % | Type I, 5 mm/min; ASTM D 638 | |
| Tensile Modulus | 3.66 GPa | 531 ksi | 5 mm/min; ASTM D 638 |
| 4.10 GPa | 595 ksi | 1 mm/min; ISO 527 | |
| Flexural Yield Strength | 100 MPa | 14500 psi | 2 mm/min; ISO 178 |
| 105 MPa | 15200 psi | 1.3 mm/min, 50 mm span; ASTM D 790 | |
| Flexural Modulus | 3.90 GPa | 566 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| 4.00 GPa | 580 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.430 J/cm @Temperature -30.0 °C |
0.806 ft-lb/in @Temperature -22.0 °F |
ASTM D 256 |
| 0.530 J/cm @Temperature 23.0 °C |
0.993 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 | |
| Izod Impact, Unnotched | 5.30 J/cm @Temperature 23.0 °C |
9.93 ft-lb/in @Temperature 73.4 °F |
ASTM D 4812 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m² @Temperature 23.0 °C |
1.90 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| 4.00 kJ/m² @Temperature -30.0 °C |
1.90 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | 47.0 kJ/m² @Temperature -30.0 °C |
22.4 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1U |
| 55.0 kJ/m² @Temperature 23.0 °C |
26.2 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U | |
| Charpy Impact Unnotched | 5.50 J/cm² @Temperature -30.0 °C |
26.2 ft-lb/in² @Temperature -22.0 °F |
Edgew 80*10*4 sp=62mm; ISO 179/1eU |
| 6.50 J/cm² @Temperature 23.0 °C |
30.9 ft-lb/in² @Temperature 73.4 °F |
Edgew 80*10*4 sp=62mm; ISO 179/1eU | |
| Charpy Impact, Notched | 0.300 J/cm² @Temperature -30.0 °C |
1.43 ft-lb/in² @Temperature -22.0 °F |
V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| 0.400 J/cm² @Temperature 23.0 °C |
1.90 ft-lb/in² @Temperature 73.4 °F |
V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA | |
| Impact Test | 7.00 J @Temperature 23.0 °C |
5.16 ft-lb @Temperature 73.4 °F |
Instrumented Impact Total Energy; ASTM D 3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 42.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
23.3 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 50.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
27.8 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 45.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
25.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 50.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
27.8 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 200 °C | 392 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 204 °C @Thickness 3.20 mm |
399 °F @Thickness 0.126 in |
unannealed; ASTM D 648 | |
| Vicat Softening Point | 195 °C | 383 °F | Rate B/50; ISO 306 |
| 200 °C | 392 °F | Rate B/120; ISO 306 | |
| 204 °C | 399 °F | Rate B/50; ASTM D 1525 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Ball Pressure Test, 75°C +/- 2°C | Pass | IEC 60695-10-2 |