SABIC Innovative Plastics Noryl GTX VP7133 PPE+PA (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polyester, TP , Polyphenylene Ether/PPO |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | NORYL GTX |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Noryl GTX VP7133 PPE+PA (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Noryl GTX VP7133 is an unfilled extrusion grade which offers high heat resistance in combination with high meltstrength.The material is especially designed for thermal break profiles which are used in aluminium windows and door assemblies.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.10 g/cc | 0.0397 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 1.2 % | 1.2 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 3.5 % @Temperature 23.0 °C |
3.5 % @Temperature 73.4 °F |
ISO 62 |
| Linear Mold Shrinkage, Flow | 0.012 - 0.020 cm/cm | 0.012 - 0.020 in/in | on tensile bar; SABIC Method |
| Melt Flow | 6.0 g/10 min @Load 10.0 kg, Temperature 280 °C |
6.0 g/10 min @Load 22.0 lb, Temperature 536 °F |
[cm^3/10 min] Melt Volume Rate; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 60.0 MPa | 8700 psi | 50 mm/min; ISO 527 |
| Tensile Strength, Yield | 75.0 MPa | 10900 psi | 50 mm/min; ISO 527 |
| Elongation at Break | 20 % | 20 % | 50 mm/min; ISO 527 |
| Elongation at Yield | 5.0 % | 5.0 % | 50 mm/min; ISO 527 |
| Tensile Modulus | 2.60 GPa | 377 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 100 MPa | 14500 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 2.50 GPa | 363 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² @Temperature 23.0 °C |
2.86 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| 6.00 kJ/m² @Temperature -30.0 °C |
2.86 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
80*10*4; ISO 180/1U | |
| Charpy Impact Unnotched | NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
Edgew 80*10*4 sp=62mm; ISO 179/1eU |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
Edgew 80*10*4 sp=62mm; ISO 179/1eU | |
| Charpy Impact, Notched | 0.500 J/cm² @Temperature 23.0 °C |
2.38 ft-lb/in² @Temperature 73.4 °F |
V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| 0.500 J/cm² @Temperature -30.0 °C |
2.38 ft-lb/in² @Temperature -22.0 °F |
V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 80.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
44.4 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 70.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
38.9 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Thermal Conductivity | 0.230 W/m-K | 1.60 BTU-in/hr-ft²-°F | ASTM E 1530 |
| Deflection Temperature at 0.46 MPa (66 psi) | 195 °C | 383 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 120 °C | 248 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| Vicat Softening Point | 210 °C | 410 °F | Rate B/50; ISO 306 |
| 215 °C | 419 °F | Rate B/120; ISO 306 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Ball Pressure Test, 125°C +/- 2°C | pass | IEC 60695-10-2 |