SABIC Innovative Plastics Noryl V0150BT PPE+HIPS

Category Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Noryl
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Noryl V0150BT PPE+HIPS.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Noryl* V0150BT is an unfilled, injection moldable modified polyphenylene ether resin.. Designed for high heat resistance and thin wall FR performance, this resin delivers a UL94 V0 rating at 1.5 mm and a UL94 5Va rating at 2.0 mm. Noryl V0150BT is also halogen free according to VDE/DIN 472 part 815 and may be an excellent material candidate where flame resistance and high temperature resistance is required.This data was supplied by SABIC-IP for the Americas region.
Physical Properties Metric English Comments
Specific Gravity 1.11 g/cc
1.11 g/cc
ASTM D 792
Density 1.11 g/cc
0.0401 lb/in³
ISO 1183
Moisture Absorption at Equilibrium 0.12 %
0.12 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.45 %

@Temperature 23.0 °C
0.45 %

@Temperature 73.4 °F
ISO 62
Linear Mold Shrinkage, Flow 0.0050 - 0.0070 cm/cm
0.0050 - 0.0070 in/in
on tensile bar; SABIC Method
0.0050 - 0.0070 cm/cm

@Thickness 3.20 mm
0.0050 - 0.0070 in/in

@Thickness 0.126 in
SABIC Method
Melt Flow 8.0 g/10 min

@Load 5.00 kg,
Temperature 280 °C
8.0 g/10 min

@Load 11.0 lb,
Temperature 536 °F
ASTM D 1238
19 g/10 min

@Load 5.00 kg,
Temperature 300 °C
19 g/10 min

@Load 11.0 lb,
Temperature 572 °F
[cm^3/10 min] Melt Volume Rate; ISO 1133
Mechanical Properties Metric English Comments
Hardness, H358/30 100 MPa
14500 psi
ISO 2039-1
Tensile Strength at Break 50.0 MPa
7250 psi
50 mm/min; ISO 527
55.0 MPa
7980 psi
Type I, 50 mm/min; ASTM D 638
Tensile Strength, Yield 65.0 MPa
9430 psi
50 mm/min; ISO 527
70.0 MPa
10200 psi
Type I, 50 mm/min; ASTM D 638
Elongation at Break 7.0 %
7.0 %
Type I, 50 mm/min; ASTM D 638
10 %
10 %
50 mm/min; ISO 527
Elongation at Yield 4.0 %
4.0 %
Type I, 50 mm/min; ASTM D 638
4.5 %
4.5 %
50 mm/min; ISO 527
Tensile Modulus 2.40 GPa
348 ksi
1 mm/min; ISO 527
2.60 GPa
377 ksi
5 mm/min; ASTM D 638
Flexural Yield Strength 100 MPa
14500 psi
2 mm/min; ISO 178
105 MPa
15200 psi
1.3 mm/min, 50 mm span; ASTM D 790
Flexural Modulus 2.45 GPa
355 ksi
2 mm/min; ISO 178
2.65 GPa
384 ksi
1.3 mm/min, 50 mm span; ASTM D 790
Izod Impact, Notched 1.30 J/cm

@Temperature -30.0 °C
2.44 ft-lb/in

@Temperature -22.0 °F
ASTM D 256
2.00 J/cm

@Temperature 23.0 °C
3.75 ft-lb/in

@Temperature 73.4 °F
ASTM D 256
Izod Impact, Notched (ISO) 8.00 kJ/m²

@Temperature -40.0 °C
3.81 ft-lb/in²

@Temperature -40.0 °F
80*10*4; ISO 180/1A
14.0 kJ/m²

@Temperature -30.0 °C
6.66 ft-lb/in²

@Temperature -22.0 °F
80*10*4; ISO 180/1A
20.0 kJ/m²

@Temperature 23.0 °C
9.52 ft-lb/in²

@Temperature 73.4 °F
80*10*4; ISO 180/1A
Charpy Impact, Notched 0.700 J/cm²

@Temperature -30.0 °C
3.33 ft-lb/in²

@Temperature -22.0 °F
V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA
2.00 J/cm²

@Temperature 23.0 °C
9.52 ft-lb/in²

@Temperature 73.4 °F
V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA
Impact Test 50.0 J

@Temperature 23.0 °C
36.9 ft-lb

@Temperature 73.4 °F
Instrumented Impact Total Energy; ASTM D 3763
Taber Abrasion, mg/1000 Cycles 35

@Load 1.00 kg
35

@Load 2.20 lb
CS-17; SABIC Method
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 70.0 µm/m-°C

@Temperature 23.0 - 80.0 °C
38.9 µin/in-°F

@Temperature 73.4 - 176 °F
ISO 11359-2
73.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
40.6 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
CTE, linear, Transverse to Flow 70.0 µm/m-°C

@Temperature 23.0 - 80.0 °C
38.9 µin/in-°F

@Temperature 73.4 - 176 °F
ISO 11359-2
71.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
39.4 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
Deflection Temperature at 0.46 MPa (66 psi) 135 °C
275 °F
Edgew 120*10*4 sp=100mm; ISO 75/Be
Deflection Temperature at 1.8 MPa (264 psi) 120 °C
248 °F
Edgew 120*10*4 sp=100mm; ISO 75/Ae
125 °C

@Thickness 3.20 mm
257 °F

@Thickness 0.126 in
unannealed; ASTM D 648
Vicat Softening Point 145 °C
293 °F
Rate B/50; ASTM D 1525
145 °C
293 °F
Rate B/50; ISO 306
150 °C
302 °F
Rate B/120; ISO 306
155 °C
311 °F
Rate A/50; ISO 306
UL RTI, Electrical 110 °C
230 °F
UL 746B
UL RTI, Mechanical with Impact 105 °C
221 °F
UL 746B
UL RTI, Mechanical without Impact 115 °C
239 °F
UL 746B
Flammability, UL94 V-0

@Thickness 1.50 mm
V-0

@Thickness 0.0591 in
UL 94
5VA

@Thickness 2.00 mm
5VA

@Thickness 0.0787 in
UL 94
Oxygen Index 36 %
36 %
LOI; ISO 4589
Glow Wire Test 775 °C

@Thickness 1.00 mm
1430 °F

@Thickness 0.0394 in
Glow Wire Ignitability Temperature; IEC 60695-2-13
775 °C

@Thickness 2.00 mm
1430 °F

@Thickness 0.0787 in
Glow Wire Ignitability Temperature; IEC 60695-2-13
775 °C

@Thickness 3.00 mm
1430 °F

@Thickness 0.118 in
Glow Wire Ignitability Temperature; IEC 60695-2-13
960 °C

@Thickness 1.00 mm
1760 °F

@Thickness 0.0394 in
Glow Wire Flammability Index; IEC 60695-2-12
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+15 ohm-cm
1.00e+15 ohm-cm
IEC 60093
Surface Resistance >= 1.00e+15 ohm
>= 1.00e+15 ohm
ROA; IEC 60093
Dielectric Constant 2.5

@Frequency 1.00e+6 Hz
2.5

@Frequency 1.00e+6 Hz
IEC 60250
2.6

@Frequency 50.0 - 60.0 Hz
2.6

@Frequency 50.0 - 60.0 Hz
IEC 60250
Dielectric Strength 16.0 kV/mm

@Thickness 3.20 mm
406 kV/in

@Thickness 0.126 in
in oil; IEC 60243-1
Dissipation Factor 0.0040

@Frequency 1.00e+6 Hz
0.0040

@Frequency 1.00e+6 Hz
IEC 60250
0.0080

@Frequency 50.0 - 60.0 Hz
0.0080

@Frequency 50.0 - 60.0 Hz
IEC 60250
Comparative Tracking Index >= 250 V
>= 250 V
IEC 60112
Descriptive Properties Value Comments
Ball Pressure Test, 125°C +/- 2°C PASSES
IEC 60695-10-2