SABIC Innovative Plastics SABIC PPCOMPOUND 55T1030 PP
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | SABIC PPCOMPOUND |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics SABIC PPCOMPOUND 55T1030 PP.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
SABIC® PPcompound 55T1030 is a general purpose, talc filled, heat stabilized copolymer polypropylene compound. This compound exhibits very high impact, and is suitable for multiple processing methods, including injection molding. The IMDS ID is 16160823.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.14 g/cc | 1.14 g/cc | ASTM D792 |
| Density | 1.13 g/cc | 0.0408 lb/in³ | ISO 1183 |
| Melt Flow | 4.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
4.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 68 | 68 | ISO 868 |
| Tensile Strength at Break | 16.0 MPa | 2320 psi | Type I, 50 mm/min; ASTM D638 |
| 18.0 MPa | 2610 psi | 50 mm/min, 1A; ISO 527 | |
| Tensile Strength, Yield | 21.0 MPa | 3050 psi | Type I, 50 mm/min; ASTM D638 |
| 24.0 MPa | 3480 psi | 50 mm/min; ISO 527 | |
| Elongation at Break | 45.6 % | 45.6 % | Type I, 50 mm/min; ASTM D638 |
| 80 % | 80 % | 50 mm/min; ISO 527 | |
| Elongation at Yield | 3.4 % | 3.4 % | Type I, 50 mm/min; ASTM D638 |
| 3.4 % | 3.4 % | 50 mm/min; ISO 527 | |
| Tensile Modulus | 2.09 GPa | 303 ksi | 50 mm/min; ASTM D638 |
| 2.52 GPa | 365 ksi | 1 mm/min; ISO 527 | |
| Flexural Modulus | 2.30 GPa | 334 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 2.81 GPa | 408 ksi | 2 mm/min, 64mm span; ISO 178 | |
| Izod Impact, Notched | 1.40 J/cm | 2.62 ft-lb/in | 63.5*12.7*3.2mm, Cut; ASTM D256 |
| Izod Impact, Unnotched | 10.68 J/cm | 20.01 ft-lb/in | 63.5*12.7*3.2mm, Cut; ASTM D4812 |
| Izod Impact, Notched (ISO) | 13.0 kJ/m² | 6.19 ft-lb/in² | 80*10*4mm, Cut; ISO 180/1A |
| 3.00 kJ/m² @Temperature -30.0 °C |
1.43 ft-lb/in² @Temperature -22.0 °F |
80*10*4mm, Cut; ISO 180/1A | |
| 6.00 kJ/m² @Temperature 0.000 °C |
2.86 ft-lb/in² @Temperature 32.0 °F |
80*10*4mm, Cut; ISO 180/1A | |
| Charpy Impact, Notched | 1.30 J/cm² | 6.19 ft-lb/in² | 80*10*4mm, Cut; ISO 179/1eA |
| 0.100 J/cm² @Temperature -30.0 °C |
0.476 ft-lb/in² @Temperature -22.0 °F |
80*10*4mm, Cut; ISO 179/1eA | |
| Dart Drop, Total Energy | 18.0 J @Temperature 23.0 °C |
13.3 ft-lb @Temperature 73.4 °F |
Instrumented Impact Energy @ peak, 6.6 m/s; ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 63.0 µm/m-°C @Temperature -30.0 - 100 °C |
35.0 µin/in-°F @Temperature -22.0 - 212 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 94.0 µm/m-°C @Temperature -30.0 - 100 °C |
52.2 µin/in-°F @Temperature -22.0 - 212 °F |
ISO 11359-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 120 °C | 248 °F | 80*10*4mm, Cut; ISO 75-1&2 |
| 114 °C @Thickness 3.20 mm |
237 °F @Thickness 0.126 in |
ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 64.0 °C | 147 °F | 80*10*4mm, Cut; ISO 75-1&2 |
| 60.0 °C @Thickness 3.20 mm |
140 °F @Thickness 0.126 in |
ASTM D648 | |
| Vicat Softening Point | 150 °C | 302 °F | 10N, 50°C/hr; ISO 306 |