SABIC Innovative Plastics SABIC PPCOMPOUND 8620 PP
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | SABIC PPCOMPOUND |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics SABIC PPCOMPOUND 8620 PP.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
SABIC® PPcompound 8620 is a mineral filled, impact modified polypropylene TPO. This material combines scratch resistance and good flow with exterior automotive weathering stability. It was originally designed for painted or unpainted automotive bumper fascia applications where a combination of high stiffness and cold temperature ductility is required. The IMDS is 209747700.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.03 g/cc | 1.03 g/cc | ASTM D792 |
| Density | 1.03 g/cc | 0.0372 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0040 cm/cm | 0.0040 in/in | 48 hrs @ 23°C, flow; SABIC Method |
| 0.0050 cm/cm | 0.0050 in/in | 1 hr @ 80°C, flow; SABIC Method | |
| 0.0060 cm/cm | 0.0060 in/in | 30 min @ 120°C, flow; SABIC Method | |
| Linear Mold Shrinkage, Transverse | 0.0070 cm/cm | 0.0070 in/in | 48 hrs @ 23°C, xflow; SABIC Method |
| 0.0080 cm/cm | 0.0080 in/in | 1 hr @ 80°C, xflow; SABIC Method | |
| 0.0090 cm/cm | 0.0090 in/in | 30 min @ 120°C, xflow; SABIC Method | |
| Melt Flow | 23 g/10 min @Load 2.16 kg, Temperature 230 °C |
23 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 54 | 54 | ISO 868 |
| Tensile Strength at Break | 11.0 MPa | 1600 psi | 50 mm/min, 1A; ISO 527 |
| 12.0 MPa | 1740 psi | Type I, 50 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 17.0 MPa | 2470 psi | Type I, 50 mm/min; ASTM D638 |
| 17.0 MPa | 2470 psi | 50 mm/min; ISO 527 | |
| Elongation at Break | 39 % | 39 % | 50 mm/min; ISO 527 |
| 101 % | 101 % | Type I, 50 mm/min; ASTM D638 | |
| Elongation at Yield | 4.4 % | 4.4 % | 50 mm/min; ISO 527 |
| 5.0 % | 5.0 % | Type I, 50 mm/min; ASTM D638 | |
| Tensile Modulus | 1.68 GPa | 244 ksi | 1 mm/min; ISO 527 |
| 1.90 GPa | 276 ksi | 50 mm/min; ASTM D638 | |
| Flexural Modulus | 1.38 GPa | 200 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 1.74 GPa | 252 ksi | 2 mm/min, 64mm span; ISO 178 | |
| Izod Impact, Notched | 5.41 J/cm | 10.1 ft-lb/in | 63.5*12.7*3.2mm, Cut; ASTM D256 |
| Izod Impact, Unnotched | NB | NB | 63.5*12.7*3.2mm, Cut; ASTM D4812 |
| Izod Impact, Notched (ISO) | 49.0 kJ/m² | 23.3 ft-lb/in² | 80*10*4mm, Cut; ISO 180/1A |
| 6.00 kJ/m² @Temperature -30.0 °C |
2.86 ft-lb/in² @Temperature -22.0 °F |
80*10*4mm, Cut; ISO 180/1A | |
| 25.0 kJ/m² @Temperature 0.000 °C |
11.9 ft-lb/in² @Temperature 32.0 °F |
80*10*4mm, Cut; ISO 180/1A | |
| Charpy Impact, Notched | 5.80 J/cm² | 27.6 ft-lb/in² | 80*10*4mm, Cut; ISO 179/1eA |
| 0.700 J/cm² @Temperature -30.0 °C |
3.33 ft-lb/in² @Temperature -22.0 °F |
80*10*4mm, Cut; ISO 179/1eA | |
| 2.50 J/cm² @Temperature 0.000 °C |
11.9 ft-lb/in² @Temperature 32.0 °F |
80*10*4mm, Cut; ISO 179/1eA | |
| Dart Drop, Total Energy | 16.0 J @Temperature 23.0 °C |
11.8 ft-lb @Temperature 73.4 °F |
Instrumented Impact Energy @ peak, 6.6 m/s; ASTM D3763 |
| 17.0 J @Temperature 0.000 °C |
12.5 ft-lb @Temperature 32.0 °F |
Instrumented Impact Energy @ peak @ 2.2 m/s; ASTM D3763 | |
| 21.0 J @Temperature -30.0 °C |
15.5 ft-lb @Temperature -22.0 °F |
Instrumented Impact Energy @ peak, -30°C @ 2.2 m/s; ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 41.0 µm/m-°C @Temperature -30.0 - 100 °C |
22.8 µin/in-°F @Temperature -22.0 - 212 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 167 µm/m-°C @Temperature -30.0 - 100 °C |
92.8 µin/in-°F @Temperature -22.0 - 212 °F |
ISO 11359-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 100 °C | 212 °F | 80*10*4mm, Cut; ISO 75-1&2 |
| 98.0 °C @Thickness 3.20 mm |
208 °F @Thickness 0.126 in |
ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 56.0 °C | 133 °F | 80*10*4mm, Cut; ISO 75-1&2 |
| 52.0 °C @Thickness 3.20 mm |
126 °F @Thickness 0.126 in |
ASTM D648 | |
| Vicat Softening Point | 123 °C | 253 °F | 10N, 50°C/hr; ISO 306 |