SABIC Innovative Plastics ULTEM 1100 PEI (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , Polyetherimide (PEI)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name ULTEM
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics ULTEM 1100 PEI (Europe-Africa-Middle East).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Standard flow Polyetherimide (Tg 217C). UL94 V0, V2 and 5VA listing.
Physical Properties Metric English Comments
Density 1.37 g/cc
0.0495 lb/in³
ISO 1183
Moisture Absorption 0.650 %
0.650 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 1.2 %
1.2 %
ISO 62
Linear Mold Shrinkage, Flow 0.0040 - 0.0060 cm/cm
0.0040 - 0.0060 in/in
on Tensile Bar; SABIC Method
Melt Index of Compound 12 g/10 min

@Load 5.00 kg,
Temperature 340 °C
12 g/10 min

@Load 11.0 lb,
Temperature 644 °F
MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 85.0 MPa
12300 psi
50 mm/min; ISO 527
Tensile Strength, Yield 110 MPa
16000 psi
50 mm/min; ISO 527
Elongation at Break 10 %
10 %
50 mm/min; ISO 527
Elongation at Yield 6.0 %
6.0 %
50 mm/min; ISO 527
Tensile Modulus 3.50 GPa
508 ksi
1 mm/min; ISO 527
Flexural Yield Strength 140 MPa
20300 psi
2 mm/min; ISO 178
Flexural Modulus 3.30 GPa
479 ksi
2 mm/min; ISO 178
Izod Impact, Notched (ISO) 4.00 kJ/m²
1.90 ft-lb/in²
80*10*4; ISO 180/1A
4.00 kJ/m²

@Temperature -30.0 °C
1.90 ft-lb/in²

@Temperature -22.0 °F
80*10*4; ISO 180/1A
Taber Abrasion, mg/1000 Cycles 10
10
CS-17, 1 kg; SABIC Method
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 50.0 µm/m-°C

@Temperature 23.0 - 150 °C
27.8 µin/in-°F

@Temperature 73.4 - 302 °F
ISO 11359-2
CTE, linear, Transverse to Flow 50.0 µm/m-°C

@Temperature 23.0 - 150 °C
27.8 µin/in-°F

@Temperature 73.4 - 302 °F
ISO 11359-2
Thermal Conductivity 0.260 W/m-K
1.80 BTU-in/hr-ft²-°F
ISO 8302
Deflection Temperature at 0.46 MPa (66 psi) 200 °C
392 °F
Edgew 120*10*4 sp=100mm; ISO 75/Be
Deflection Temperature at 1.8 MPa (264 psi) 185 °C
365 °F
Edgew 120*10*4 sp=100mm; ISO 75/Ae
Vicat Softening Point 200 °C
392 °F
Rate B/50; ISO 306
205 °C
401 °F
Rate B/120; ISO 306
210 °C
410 °F
Rate A/50; ISO 306
Glass Transition Temp, Tg 217 °C
423 °F
UL RTI, Electrical 170 °C
338 °F
UL 746B
UL RTI, Mechanical with Impact 170 °C
338 °F
UL 746B
UL RTI, Mechanical without Impact 170 °C
338 °F
UL 746B
Flammability, UL94 V-2

@Thickness 0.400 mm
V-2

@Thickness 0.0157 in
UL 94
V-0

@Thickness 0.750 mm
V-0

@Thickness 0.0295 in
UL 94
5VA

@Thickness 3.00 mm
5VA

@Thickness 0.118 in
UL 94
Oxygen Index 47 %
47 %
ISO 4589
Glow Wire Test 960 °C

@Thickness 3.20 mm
1760 °F

@Thickness 0.126 in
IEC 60695-2-12
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+15 ohm-cm
1.00e+15 ohm-cm
IEC 60093
Surface Resistance >= 1.00e+15 ohm
>= 1.00e+15 ohm
ROA; IEC 60093
Dielectric Constant 3.5

@Frequency 50.0 - 60.0 Hz
3.5

@Frequency 50.0 - 60.0 Hz
IEC 60250
Dielectric Strength 17.2 kV/mm

@Thickness 3.20 mm
437 kV/in

@Thickness 0.126 in
in oil; IEC 60243-1
Dissipation Factor 0.0016

@Frequency 50.0 - 60.0 Hz
0.0016

@Frequency 50.0 - 60.0 Hz
IEC 60250
Comparative Tracking Index >= 100 V
>= 100 V
IEC 60112
175 V
175 V
IEC 60112
Descriptive Properties Value Comments
Ball Pressure Test, 125°C +/- 2°C PASSES
IEC 60695-10-2