SABIC Innovative Plastics ULTEM 2100 PEI (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , Polyetherimide (PEI)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name ULTEM
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics ULTEM 2100 PEI (Europe-Africa-Middle East).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
10% Glass fiber filled, standard flow Polyetherimide (Tg 217C). Resin is RoHS compliant. UL94 V0 and 5VA listing.
Physical Properties Metric English Comments
Density 1.34 g/cc
0.0484 lb/in³
ISO 1183
Moisture Absorption 0.600 %
0.600 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 1.0 %
1.0 %
ISO 62
Linear Mold Shrinkage, Flow 0.0040 - 0.0060 cm/cm
0.0040 - 0.0060 in/in
on Tensile Bar; SABIC Method
Melt Index of Compound 9.0 g/10 min

@Load 5.00 kg,
Temperature 360 °C
9.0 g/10 min

@Load 11.0 lb,
Temperature 680 °F
MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Hardness, H358/30 140 MPa
20300 psi
ISO 2039-1
Tensile Strength at Break 115 MPa
16700 psi
5 mm/min; ISO 527
Elongation at Break 4.0 %
4.0 %
5 mm/min; ISO 527
Tensile Modulus 4.50 GPa
653 ksi
1 mm/min; ISO 527
Flexural Strength 185 MPa
26800 psi
2 mm/min; ISO 178
Flexural Modulus 4.50 GPa
653 ksi
2 mm/min; ISO 178
Izod Impact, Unnotched (ISO) 30.0 kJ/m²
14.3 ft-lb/in²
80*10*4; ISO 180/1U
30.0 kJ/m²

@Temperature -30.0 °C
14.3 ft-lb/in²

@Temperature -22.0 °F
80*10*4; ISO 180/1U
Charpy Impact, Notched 0.700 J/cm²
3.33 ft-lb/in²
ISO 179/2C
Taber Abrasion, mg/1000 Cycles 15
15
CS-17, 1 kg; SABIC Method
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 26.0 µm/m-°C

@Temperature 23.0 - 150 °C
14.4 µin/in-°F

@Temperature 73.4 - 302 °F
ISO 11359-2
CTE, linear, Transverse to Flow 60.0 µm/m-°C

@Temperature 23.0 - 150 °C
33.3 µin/in-°F

@Temperature 73.4 - 302 °F
ISO 11359-2
Thermal Conductivity 0.240 W/m-K
1.67 BTU-in/hr-ft²-°F
ISO 8302
Deflection Temperature at 0.46 MPa (66 psi) 210 °C
410 °F
Edgew 120*10*4 sp=100mm; ISO 75/Be
Deflection Temperature at 1.8 MPa (264 psi) 205 °C
401 °F
Edgew 120*10*4 sp=100mm; ISO 75/Ae
Vicat Softening Point 212 °C
414 °F
Rate B/50; ISO 306
217 °C
423 °F
Rate B/120; ISO 306
223 °C
433 °F
Rate A/50; ISO 306
Glass Transition Temp, Tg 217 °C
423 °F
UL RTI, Electrical 170 °C
338 °F
UL 746B
UL RTI, Mechanical with Impact 170 °C
338 °F
UL 746B
UL RTI, Mechanical without Impact 170 °C
338 °F
UL 746B
Flammability, UL94 V-0

@Thickness 0.410 mm
V-0

@Thickness 0.0161 in
UL 94
5VA

@Thickness 1.90 mm
5VA

@Thickness 0.0748 in
UL 94
Oxygen Index 46 %
46 %
ISO 4589
Glow Wire Test 960 °C

@Thickness 3.20 mm
1760 °F

@Thickness 0.126 in
IEC 60695-2-12
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+15 ohm-cm
1.00e+15 ohm-cm
IEC 60093
Surface Resistance >= 1.00e+15 ohm
>= 1.00e+15 ohm
ROA; IEC 60093
Dielectric Constant 2.9

@Frequency 1.00e+6 Hz
2.9

@Frequency 1.00e+6 Hz
IEC 60250
3.0

@Frequency 50.0 - 60.0 Hz
3.0

@Frequency 50.0 - 60.0 Hz
IEC 60250
Dielectric Strength 15.0 kV/mm

@Thickness 3.20 mm
381 kV/in

@Thickness 0.126 in
in oil; IEC 60243-1
27.0 kV/mm

@Thickness 1.60 mm
686 kV/in

@Thickness 0.0630 in
in oil; IEC 60243-1
34.0 kV/mm

@Thickness 0.800 mm
864 kV/in

@Thickness 0.0315 in
in oil; IEC 60243-1
Dissipation Factor 0.00090

@Frequency 50.0 - 60.0 Hz
0.00090

@Frequency 50.0 - 60.0 Hz
IEC 60250
0.0025

@Frequency 1.00e+6 Hz
0.0025

@Frequency 1.00e+6 Hz
IEC 60250
0.0046

@Frequency 2.45e+9 Hz
0.0046

@Frequency 2.45e+9 Hz
IEC 60250
Comparative Tracking Index >= 100 V
>= 100 V
IEC 60112
150 V
150 V
IEC 60112
Descriptive Properties Value Comments
Ball Pressure Test, 125°C +/- 2°C PASSES
IEC 60695-10-2
Copyright © lookpolymers.com All Rights Reserved