SABIC Innovative Plastics ULTEM 2410R PEI

Category Polymer , Thermoplastic , Polyetherimide (PEI)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name ULTEM
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics ULTEM 2410R PEI.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
40% Glass fiber filled, enhanced flow Polyetherimide (Tg 217C) with internal mold release. ECO Conforming, UL94 V0 and 5VA listing.
Physical Properties Metric English Comments
Specific Gravity 1.61 g/cc
1.61 g/cc
ASTM D792
Water Absorption 0.13 %

@Time 86400 sec
0.13 %

@Time 24.0 hour
ASTM D570
Moisture Absorption at Equilibrium 0.90 %
0.90 %
ASTM D570
Linear Mold Shrinkage, Flow 0.0010 - 0.0030 cm/cm

@Thickness 3.20 mm
0.0010 - 0.0030 in/in

@Thickness 0.126 in
SABIC Method
Melt Flow 5.5 g/10 min

@Load 6.60 kg,
Temperature 337 °C
5.5 g/10 min

@Load 14.6 lb,
Temperature 639 °F
ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell M 114
114
ASTM D785
Tensile Strength at Break 179 MPa
26000 psi
Type I, 5 mm/min; ASTM D638
Elongation at Break 2.5 %
2.5 %
Type I, 5 mm/min; ASTM D638
Tensile Modulus 11.72 GPa
1700 ksi
5 mm/min; ASTM D638
Flexural Strength 241 MPa
35000 psi
2.6 mm/min, 100 mm span; ASTM D790
Flexural Modulus 11.72 GPa
1700 ksi
2.6 mm/min, 100 mm span; ASTM D790
Izod Impact, Notched 1.12 J/cm
2.10 ft-lb/in
ASTM D256
4.80 J/cm

@Thickness 3.20 mm
8.99 ft-lb/in

@Thickness 0.126 in
ASTM D256
Izod Impact, Unnotched 4.27 J/cm
8.00 ft-lb/in
ASTM D4812
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 14.4 µm/m-°C

@Temperature -20.0 - 150 °C
8.00 µin/in-°F

@Temperature -4.00 - 302 °F
ASTM E 831
Deflection Temperature at 0.46 MPa (66 psi) 215 °C

@Thickness 6.40 mm
419 °F

@Thickness 0.252 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 212 °C

@Thickness 6.40 mm
414 °F

@Thickness 0.252 in
unannealed; ASTM D648
Vicat Softening Point 234 °C
453 °F
Rate B/50; ASTM D1525
Glass Transition Temp, Tg 217 °C
423 °F
UL RTI, Electrical 170 °C
338 °F
UL 746B
UL RTI, Mechanical with Impact 170 °C
338 °F
UL 746B
UL RTI, Mechanical without Impact 170 °C
338 °F
UL 746B
Flammability, UL94 V-0

@Thickness 0.250 mm
V-0

@Thickness 0.00984 in
UL 94
5VA

@Thickness 1.47 mm
5VA

@Thickness 0.0579 in
UL 94
Oxygen Index 54 %
54 %
ASTM D2863
Electrical Properties Metric English Comments
Volume Resistivity 1.50e+16 ohm-cm
1.50e+16 ohm-cm
ASTM D257
Dielectric Constant 3.7

@Frequency 1000 Hz
3.7

@Frequency 1000 Hz
ASTM D150
Dielectric Strength 24.0 kV/mm

@Thickness 1.60 mm
610 kV/in

@Thickness 0.0630 in
in oil; ASTM D149
Dissipation Factor 0.0020

@Frequency 1000 Hz
0.0020

@Frequency 1000 Hz
ASTM D150
Arc Resistance 120 - 180 sec
120 - 180 sec
Tungsten; ASTM D495
Comparative Tracking Index 0.00 - 100 V
0.00 - 100 V
UL 746A
Hot Wire Ignition, HWI >= 120 sec
>= 120 sec
UL 746A
High Amp Arc Ignition, HAI 0.00 - 15 arcs
0.00 - 15 arcs
UL 746A
High Voltage Arc-Tracking Rate, HVTR >= 150 mm/min
>= 5.91 in/min
UL 746A