SABIC Innovative Plastics Ultem 1010FV PEI

Category Polymer , Thermoplastic , Polyetherimide (PEI)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name ULTEM
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Ultem 1010FV PEI.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Transparent, enhanced flow Polyetherimide (Tg 217C). ECO Conforming, UL94 V0 and 5VA listing; color dependant, see UL Yellow Card. US FDA and EU Food Contant compliant, NSF 51 listing.This data was supplied by SABIC-IP for the Americas region.
Physical Properties Metric English Comments
Specific Gravity 1.27 g/cc
1.27 g/cc
ASTM D 792
Density 1.27 g/cc
0.0459 lb/in³
ISO 1183
Moisture Absorption at Equilibrium 0.70 %
0.70 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 1.25 %

@Temperature 23.0 °C
1.25 %

@Temperature 73.4 °F
ISO 62
Linear Mold Shrinkage, Flow 0.0050 - 0.0070 cm/cm

@Thickness 3.20 mm
0.0050 - 0.0070 in/in

@Thickness 0.126 in
SABIC Method
Melt Flow 17.8 g/10 min

@Load 6.60 kg,
Temperature 337 °C
17.8 g/10 min

@Load 14.6 lb,
Temperature 639 °F
ASTM D 1238
25 g/10 min

@Load 5.00 kg,
Temperature 220 °C
25 g/10 min

@Load 11.0 lb,
Temperature 428 °F
[cm^3/10 min] Melt Volume Rate; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 85.0 MPa
12300 psi
5 mm/min; ISO 527
105 MPa
15200 psi
Type I, 5 mm/min; ASTM D 638
Tensile Strength, Yield 105 MPa
15200 psi
5 mm/min; ISO 527
110 MPa
16000 psi
Type I, 5 mm/min; ASTM D 638
Elongation at Break 60 %
60 %
Type I, 5 mm/min; ASTM D 638
60 %
60 %
5 mm/min; ISO 527
Elongation at Yield 6.0 %
6.0 %
5 mm/min; ISO 527
7.0 %
7.0 %
Type I, 5 mm/min; ASTM D 638
Tensile Modulus 3.20 GPa
464 ksi
1 mm/min; ISO 527
3.58 GPa
519 ksi
5 mm/min; ASTM D 638
Flexural Yield Strength 160 MPa
23200 psi
2 mm/min; ISO 178
174 MPa
25200 psi
1.3 mm/min, 50 mm span; ASTM D 790
Flexural Modulus 3.30 GPa
479 ksi
2 mm/min; ISO 178
3.42 GPa
496 ksi
1.3 mm/min, 50 mm span; ASTM D 790
Izod Impact, Notched 0.320 J/cm

@Temperature 23.0 °C
0.599 ft-lb/in

@Temperature 73.4 °F
ASTM D 256
0.350 J/cm

@Temperature -30.0 °C
0.656 ft-lb/in

@Temperature -22.0 °F
ASTM D 256
Izod Impact, Unnotched 13.35 J/cm

@Temperature 23.0 °C
25.01 ft-lb/in

@Temperature 73.4 °F
ASTM D 4812
Izod Impact, Notched (ISO) 5.00 kJ/m²

@Temperature 23.0 °C
2.38 ft-lb/in²

@Temperature 73.4 °F
80*10*4; ISO 180/1A
5.00 kJ/m²

@Temperature -30.0 °C
2.38 ft-lb/in²

@Temperature -22.0 °F
80*10*4; ISO 180/1A
Charpy Impact, Notched 0.300 J/cm²

@Temperature 23.0 °C
1.43 ft-lb/in²

@Temperature 73.4 °F
V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA
Impact Test 33.0 J

@Temperature 23.0 °C
24.3 ft-lb

@Temperature 73.4 °F
Instrumented Impact Total Energy; ASTM D 3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 50.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
27.8 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
55.8 µm/m-°C

@Temperature -20.0 - 150 °C
31.0 µin/in-°F

@Temperature -4.00 - 302 °F
ASTM E 831
CTE, linear, Transverse to Flow 50.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
27.8 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
50.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
27.8 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
Deflection Temperature at 1.8 MPa (264 psi) 193 °C
379 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
198 °C

@Thickness 6.40 mm
388 °F

@Thickness 0.252 in
unannealed; ASTM D 648
Vicat Softening Point 211 °C
412 °F
Rate B/50; ISO 306
212 °C
414 °F
Rate B/120; ISO 306
218 °C
424 °F
Rate B/50; ASTM D 1525
Glass Transition Temp, Tg 217 °C
423 °F
UL RTI, Electrical 170 °C
338 °F
UL 746B
UL RTI, Mechanical with Impact 170 °C
338 °F
UL 746B
UL RTI, Mechanical without Impact 170 °C
338 °F
UL 746B
Flammability, UL94 V-2

@Thickness 0.710 mm
V-2

@Thickness 0.0280 in
UL 94
V-1

@Thickness 0.750 mm
V-1

@Thickness 0.0295 in
UL 94
V-0

@Thickness 0.750 mm
V-0

@Thickness 0.0295 in
UL 94
5VA

@Thickness 3.00 mm
5VA

@Thickness 0.118 in
UL 94
NBS Smoke Density 2.0

@Time 240 sec
2.0

@Time 0.0667 hour
Flaming, Ds; ASTM E 662
Oxygen Index 44 %
44 %
LOI; ASTM D 2863
Optical Properties Metric English Comments
Transmission, Visible 90 %
90 %
transparent; thickness not quantified
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+17 ohm-cm
1.00e+17 ohm-cm
ASTM D 257
Dielectric Constant 3.15

@Frequency 1000 Hz
3.15

@Frequency 1000 Hz
ASTM D 150
Dielectric Strength 27.9 kV/mm

@Thickness 1.60 mm
709 kV/in

@Thickness 0.0630 in
in oil; ASTM D 149
32.6 kV/mm

@Thickness 1.60 mm
828 kV/in

@Thickness 0.0630 in
in air; ASTM D 149
Dissipation Factor 0.0013

@Frequency 1000 Hz
0.0013

@Frequency 1000 Hz
ASTM D 150
0.0025

@Frequency 2.45e+9 Hz
0.0025

@Frequency 2.45e+9 Hz
ASTM D 150
Arc Resistance 120 - 180 sec
120 - 180 sec
Tungsten, PLC code 5; ASTM D 495
Comparative Tracking Index 100 - 175 V
100 - 175 V
PLC code 4; UL 746A
Hot Wire Ignition, HWI 60 - 120 sec
60 - 120 sec
PLC code 1; UL 746A
High Amp Arc Ignition, HAI 15 - 30 arcs
15 - 30 arcs
surface, PLC code 3; UL 746A
High Voltage Arc-Tracking Rate, HVTR 25.4 - 80.0 mm/min
1.00 - 3.15 in/min
PLC code 2; UL 746A