SABIC Innovative Plastics Ultem 1100R PEI (Asia Pacific)

Category Polymer , Thermoplastic , Polyetherimide (PEI)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name ULTEM
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Ultem 1100R PEI (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Standard flow Polyetherimide (Tg 217C) with internal mold release. ECO Conforming.This data was supplied by SABIC-IP for the Asia Pacific region.
Physical Properties Metric English Comments
Specific Gravity 1.36 g/cc
1.36 g/cc
ASTM D 792
Linear Mold Shrinkage, Flow 0.0050 - 0.0070 cm/cm

@Thickness 3.20 mm
0.0050 - 0.0070 in/in

@Thickness 0.126 in
SABIC Method
Melt Flow 11.2 g/10 min

@Load 6.60 kg,
Temperature 337 °C
11.2 g/10 min

@Load 14.6 lb,
Temperature 639 °F
ASTM D 1238
Mechanical Properties Metric English Comments
Tensile Strength, Yield 110 MPa
16000 psi
Type I, 5 mm/min; ASTM D 638
Elongation at Break 70 %
70 %
Type I, 5 mm/min; ASTM D 638
Tensile Modulus 3.72 GPa
540 ksi
5 mm/min; ASTM D 638
Flexural Yield Strength 165 MPa
23900 psi
2.6 mm/min, 100 mm span; ASTM D 790
Flexural Modulus 3.51 GPa
509 ksi
2.6 mm/min, 100 mm span; ASTM D 790
Izod Impact, Notched 0.370 J/cm

@Temperature 23.0 °C
0.693 ft-lb/in

@Temperature 73.4 °F
ASTM D 256
15.48 J/cm

@Thickness 3.20 mm
29.00 ft-lb/in

@Thickness 0.126 in
reverse notched; ASTM D 256
Gardner Impact 21.0 J

@Temperature 23.0 °C
15.5 ft-lb

@Temperature 73.4 °F
ASTM D 3029
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 198 °C

@Thickness 6.40 mm
388 °F

@Thickness 0.252 in
unannealed; ASTM D 648
Glass Transition Temp, Tg 217 °C
423 °F