SABIC Innovative Plastics Ultem HATX100 PEI+PCE (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , Polyetherimide (PEI) , Polyetherimide (PEI) + PCE
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name ULTEM
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Ultem HATX100 PEI+PCE (Europe-Africa-Middle East).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Higher impact, high flow Polyetherimide blend. ECO Conforming. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO 10993 or USP Class VI), food contact compliant.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
Physical Properties Metric English Comments
Specific Gravity 1.21 g/cc
1.21 g/cc
ASTM D 792
Density 1.21 g/cc
0.0437 lb/in³
ISO 1183
Moisture Absorption at Equilibrium 0.25 %
0.25 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.50 %

@Temperature 23.0 °C
0.50 %

@Temperature 73.4 °F
ISO 62
Linear Mold Shrinkage, Flow 0.0050 - 0.0070 cm/cm

@Thickness 3.20 mm
0.0050 - 0.0070 in/in

@Thickness 0.126 in
SABIC Method
Melt Flow 6.0 g/10 min

@Load 6.60 kg,
Temperature 295 °C
6.0 g/10 min

@Load 14.6 lb,
Temperature 563 °F
ASTM D 1238
35 g/10 min

@Load 5.00 kg,
Temperature 220 °C
35 g/10 min

@Load 11.0 lb,
Temperature 428 °F
[cm^3/10 min] Melt Volume Rate; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 55.0 MPa
7980 psi
5 mm/min; ISO 527
58.0 MPa
8410 psi
Type I, 5 mm/min; ASTM D 638
Tensile Strength, Yield 65.0 MPa
9430 psi
5 mm/min; ISO 527
68.0 MPa
9860 psi
Type I, 5 mm/min; ASTM D 638
Elongation at Break 30 %
30 %
5 mm/min; ISO 527
80 %
80 %
Type I, 5 mm/min; ASTM D 638
Elongation at Yield 7.0 %
7.0 %
5 mm/min; ISO 527
20 %
20 %
Type I, 5 mm/min; ASTM D 638
Tensile Modulus 2.00 GPa
290 ksi
5 mm/min; ASTM D 638
2.35 GPa
341 ksi
1 mm/min; ISO 527
Flexural Yield Strength 90.0 MPa
13100 psi
2 mm/min; ISO 178
106 MPa
15400 psi
1.3 mm/min, 50 mm span; ASTM D 790
Flexural Modulus 2.00 GPa
290 ksi
1.3 mm/min, 50 mm span; ASTM D 790
2.40 GPa
348 ksi
2 mm/min; ISO 178
Izod Impact, Notched 4.27 J/cm

@Temperature 23.0 °C
8.00 ft-lb/in

@Temperature 73.4 °F
ASTM D 256
Izod Impact, Unnotched 20.82 J/cm

@Temperature 23.0 °C
39.00 ft-lb/in

@Temperature 73.4 °F
ASTM D 4812
Izod Impact, Notched (ISO) 13.0 kJ/m²

@Temperature -30.0 °C
6.19 ft-lb/in²

@Temperature -22.0 °F
80*10*4; ISO 180/1A
15.0 kJ/m²

@Temperature 23.0 °C
7.14 ft-lb/in²

@Temperature 73.4 °F
80*10*4; ISO 180/1A
Charpy Impact, Notched 1.90 J/cm²

@Temperature 23.0 °C
9.04 ft-lb/in²

@Temperature 73.4 °F
V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA
Impact Test 25.0 J

@Temperature 23.0 °C
18.4 ft-lb

@Temperature 73.4 °F
Instrumented Impact Total Energy; ASTM D 3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 60.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
33.3 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
60.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
33.3 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
CTE, linear, Transverse to Flow 60.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
33.3 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
60.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
33.3 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
Deflection Temperature at 1.8 MPa (264 psi) 150 °C
302 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
157 °C

@Thickness 6.40 mm
315 °F

@Thickness 0.252 in
unannealed; ASTM D 648
Vicat Softening Point 170 °C
338 °F
Rate B/50; ASTM D 1525
170 °C
338 °F
Rate B/50; ISO 306
175 °C
347 °F
Rate B/120; ISO 306
Flammability, UL94 HB

@Thickness 0.760 mm
HB

@Thickness 0.0299 in
UL 94