SABIC Innovative Plastics Valox® 325FC PBT (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Valox®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Valox® 325FC PBT (Europe-Africa-Middle East).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Commercial, VALOX 325FC is compliant with food contact regulations. VALOX 325FC is a general purpose, unreinforced PBT injection moulding resin which contains internal mold release. This new 325FC grade is a good processable resin that exhibits faster and more economical cycle times.
Physical Properties Metric English Comments
Specific Gravity 1.31 g/cc
1.31 g/cc
ASTM D792
Density 1.31 g/cc
0.0473 lb/in³
ISO 1183
Moisture Absorption 0.0800 %
0.0800 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.34 %
0.34 %
ISO 62
Viscosity 165000 cP
165000 cP
Melt Viscosity, 260°C, 1500 sec-1; ISO 11443
Linear Mold Shrinkage, Flow 0.020 - 0.026 cm/cm
0.020 - 0.026 in/in
on Tensile Bar; SABIC Method
Linear Mold Shrinkage, Transverse 0.0090 - 0.018 cm/cm
0.0090 - 0.018 in/in
on Tensile Bar; SABIC Method
Melt Index of Compound 20 g/10 min

@Load 2.16 kg,
Temperature 250 °C
 20 g/10 min

@Load 4.76 lb,
Temperature 482 °F
 MVR [cm^3/10 min]; ISO 1133
50 g/10 min

@Load 5.00 kg,
Temperature 250 °C
 50 g/10 min

@Load 11.0 lb,
Temperature 482 °F
 MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Hardness, Rockwell R 117
117
ISO 2039-2
Hardness, H358/30 145 MPa
21000 psi
ISO 2039-1
Tensile Strength at Break 60.0 MPa
8700 psi
Type I, 50 mm/min; ASTM D638
60.0 MPa
8700 psi
50 mm/min; ISO 527
Tensile Strength, Yield 60.0 MPa
8700 psi
Type I, 50 mm/min; ASTM D638
60.0 MPa
8700 psi
50 mm/min; ISO 527
Elongation at Break 15 %
15 %
Type I, 50 mm/min; ASTM D638
15 %
15 %
50 mm/min; ISO 527
Elongation at Yield 7.0 %
7.0 %
Type I, 50 mm/min; ASTM D638
10 %
10 %
50 mm/min; ISO 527
Tensile Modulus 2.50 GPa
363 ksi
50 mm/min; ASTM D638
2.55 GPa
370 ksi
1 mm/min; ISO 527
Flexural Yield Strength 85.0 MPa
12300 psi
2 mm/min; ISO 178
Flexural Modulus 2.40 GPa
348 ksi
2 mm/min; ISO 178
Izod Impact, Notched 0.380 J/cm
0.712 ft-lb/in
ASTM D256
0.360 J/cm

@Temperature 0.000 °C
 0.674 ft-lb/in

@Temperature 32.0 °F
 ASTM D256
0.360 J/cm

@Temperature -30.0 °C
 0.674 ft-lb/in

@Temperature -22.0 °F
 ASTM D256
Izod Impact, Unnotched NB
NB
ASTM D4812
NB

@Temperature -30.0 °C
 NB

@Temperature -22.0 °F
 ASTM D4812
Izod Impact, Notched (ISO) 4.00 kJ/m²
1.90 ft-lb/in²
80*10*4; ISO 180/1A
4.00 kJ/m²

@Temperature 0.000 °C
 1.90 ft-lb/in²

@Temperature 32.0 °F
 80*10*4; ISO 180/1A
4.00 kJ/m²

@Temperature -30.0 °C
 1.90 ft-lb/in²

@Temperature -22.0 °F
 80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) NB
NB
80*10*4; ISO 180/1U
100 kJ/m²

@Temperature -30.0 °C
 47.6 ft-lb/in²

@Temperature -22.0 °F
 80*10*4; ISO 180/1U
Charpy Impact Unnotched NB
NB
ISO 179/2C
8.00 J/cm²

@Temperature -30.0 °C
 38.1 ft-lb/in²

@Temperature -22.0 °F
 ISO 179/2C
Charpy Impact, Notched 0.400 J/cm²
1.90 ft-lb/in²
ISO 179/2C
0.400 J/cm²

@Temperature -30.0 °C
 1.90 ft-lb/in²

@Temperature -22.0 °F
 ISO 179/2C
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 150 °C
302 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
Deflection Temperature at 1.8 MPa (264 psi) 50.0 °C
122 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
Vicat Softening Point 185 °C
365 °F
Rate B/50; ASTM D1525
185 °C
365 °F
Rate B/50; ISO 306
185 °C
365 °F
Rate B/120; ISO 306
220 °C
428 °F
Rate A/50; ISO 306
220 °C
428 °F
Rate A/50; ASTM D1525
Descriptive Properties Value Comments
Ball Pressure Test, 125°C +/- 2°C PASSES
IEC 60695-10-2