SABIC Innovative Plastics Valox® 451E PBT (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Valox®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Valox® 451E PBT (Europe-Africa-Middle East).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
VALOX 451E is 20% glass reinforced, flame retardant PBT injection moulding resin.
Physical Properties Metric English Comments
Specific Gravity 1.54 g/cc
1.54 g/cc
ASTM D792
Density 1.54 g/cc
0.0556 lb/in³
ISO 1183
Filler Content 20 %
20 %
ASTM D229
Moisture Absorption 0.0800 %
0.0800 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.27 %
0.27 %
ISO 62
Viscosity 100000 cP
100000 cP
Melt Viscosity, 260°C, 1500 sec-1; ISO 11443
Linear Mold Shrinkage, Flow 0.0040 - 0.0080 cm/cm
0.0040 - 0.0080 in/in
on Tensile Bar; SABIC Method
0.0040 - 0.010 cm/cm

@Thickness 3.20 mm
 0.0040 - 0.010 in/in

@Thickness 0.126 in
 SABIC Method
Linear Mold Shrinkage, Transverse 0.0060 - 0.0090 cm/cm
0.0060 - 0.0090 in/in
on Tensile Bar; SABIC Method
0.0080 - 0.012 cm/cm

@Thickness 3.20 mm
 0.0080 - 0.012 in/in

@Thickness 0.126 in
 SABIC Method
Melt Flow 17 g/10 min

@Load 2.16 kg,
Temperature 250 °C
 17 g/10 min

@Load 4.76 lb,
Temperature 482 °F
 ASTM D1238
110 g/10 min

@Load 5.00 kg,
Temperature 266 °C
 110 g/10 min

@Load 11.0 lb,
Temperature 511 °F
 ASTM D1238
Melt Index of Compound 12 g/10 min

@Load 2.16 kg,
Temperature 250 °C
 12 g/10 min

@Load 4.76 lb,
Temperature 482 °F
 MVR [cm^3/10 min]; ISO 1133
55 g/10 min

@Load 5.00 kg,
Temperature 250 °C
 55 g/10 min

@Load 11.0 lb,
Temperature 482 °F
 MVR [cm^3/10 min]; ISO 1133
85 g/10 min

@Load 5.00 kg,
Temperature 265 °C
 85 g/10 min

@Load 11.0 lb,
Temperature 509 °F
 MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Hardness, Rockwell R 120
120
ISO 2039-2
Hardness, H358/30 117 MPa
17000 psi
ISO 2039-1
Tensile Strength at Break 110 MPa
16000 psi
Type I, 5 mm/min; ASTM D638
110 MPa
16000 psi
5 mm/min; ISO 527
Tensile Strength, Yield 110 MPa
16000 psi
Type I, 5 mm/min; ASTM D638
110 MPa
16000 psi
5 mm/min; ISO 527
Elongation at Break 2.0 %
2.0 %
Type I, 5 mm/min; ASTM D638
2.0 %
2.0 %
5 mm/min; ISO 527
3.0 %
3.0 %
Flexural Strain, break, 2 mm/min; ISO 178
Elongation at Yield 2.0 %
2.0 %
Type I, 5 mm/min; ASTM D638
2.0 %
2.0 %
5 mm/min; ISO 527
Tensile Modulus 7.90 GPa
1150 ksi
5 mm/min; ASTM D638
8.00 GPa
1160 ksi
1 mm/min; ISO 527
Flexural Strength 154 MPa
22300 psi
1.3 mm/min, 50 mm span; ASTM D790
160 MPa
23200 psi
2 mm/min; ISO 178
Flexural Yield Strength 154 MPa
22300 psi
1.3 mm/min, 50 mm span; ASTM D790
160 MPa
23200 psi
2 mm/min; ISO 178
Flexural Modulus 6.10 GPa
885 ksi
1.3 mm/min, 50 mm span; ASTM D790
6.60 GPa
957 ksi
2 mm/min; ISO 178
Izod Impact, Notched 0.600 J/cm
1.12 ft-lb/in
ASTM D256
0.600 J/cm

@Temperature 0.000 °C
 1.12 ft-lb/in

@Temperature 32.0 °F
 ASTM D256
0.600 J/cm

@Temperature -30.0 °C
 1.12 ft-lb/in

@Temperature -22.0 °F
 ASTM D256
Izod Impact, Unnotched 3.50 J/cm
6.56 ft-lb/in
ASTM D4812
3.20 J/cm

@Temperature -30.0 °C
 5.99 ft-lb/in

@Temperature -22.0 °F
 ASTM D4812
Izod Impact, Notched (ISO) 6.00 kJ/m²
2.86 ft-lb/in²
80*10*4; ISO 180/1A
6.00 kJ/m²

@Temperature 0.000 °C
 2.86 ft-lb/in²

@Temperature 32.0 °F
 80*10*4; ISO 180/1A
6.00 kJ/m²

@Temperature -30.0 °C
 2.86 ft-lb/in²

@Temperature -22.0 °F
 80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 25.0 kJ/m²
11.9 ft-lb/in²
80*10*4; ISO 180/1U
25.0 kJ/m²

@Temperature -30.0 °C
 11.9 ft-lb/in²

@Temperature -22.0 °F
 80*10*4; ISO 180/1U
Charpy Impact Unnotched 3.00 J/cm²
14.3 ft-lb/in²
ISO 179/2C
3.50 J/cm²
16.7 ft-lb/in²
Edgew 80*10*4 sp=62mm; ISO 179/1eU
2.80 J/cm²

@Temperature -30.0 °C
 13.3 ft-lb/in²

@Temperature -22.0 °F
 ISO 179/2C
4.50 J/cm²

@Temperature -30.0 °C
 21.4 ft-lb/in²

@Temperature -22.0 °F
 Edgew 80*10*4 sp=62mm; ISO 179/1eU
Charpy Impact, Notched 0.700 J/cm²
3.33 ft-lb/in²
Edgew 80*10*4 sp=62mm; ISO 179/1eA
0.700 J/cm²
3.33 ft-lb/in²
ISO 179/2C
0.500 J/cm²

@Temperature -30.0 °C
 2.38 ft-lb/in²

@Temperature -22.0 °F
 Edgew 80*10*4 sp=62mm; ISO 179/1eA
0.700 J/cm²

@Temperature -30.0 °C
 3.33 ft-lb/in²

@Temperature -22.0 °F
 ISO 179/2C
Dart Drop, Total Energy 6.00 J

@Temperature 23.0 °C
 4.43 ft-lb

@Temperature 73.4 °F
 ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 23.8 µm/m-°C

@Temperature 23.0 - 150 °C
 13.2 µin/in-°F

@Temperature 73.4 - 302 °F
 ISO 11359-2
26.1 µm/m-°C

@Temperature -40.0 - 40.0 °C
 14.5 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
30.9 µm/m-°C

@Temperature -40.0 - 40.0 °C
 17.2 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+15 ohm-cm
>= 1.00e+15 ohm-cm
ASTM D257
>= 1.00e+15 ohm-cm
>= 1.00e+15 ohm-cm
IEC 60093
Surface Resistance >= 1.00e+15 ohm
>= 1.00e+15 ohm
ROA; IEC 60093
Dielectric Constant 3.3

@Frequency 1.00e+6 Hz
 3.3

@Frequency 1.00e+6 Hz
 IEC 60250
3.3

@Frequency 50.0 - 60.0 Hz
 3.3

@Frequency 50.0 - 60.0 Hz
 IEC 60250
Dielectric Strength 15.0 kV/mm

@Thickness 3.20 mm
 381 kV/in

@Thickness 0.126 in
 in oil; IEC 60243-1
21.0 kV/mm

@Thickness 1.60 mm
 533 kV/in

@Thickness 0.0630 in
 in oil; IEC 60243-1
22.0 kV/mm

@Thickness 0.800 mm
 559 kV/in

@Thickness 0.0315 in
 in oil; IEC 60243-1
Dissipation Factor 0.0010

@Frequency 50.0 - 60.0 Hz
 0.0010

@Frequency 50.0 - 60.0 Hz
 IEC 60250
0.010

@Frequency 1.00e+6 Hz
 0.010

@Frequency 1.00e+6 Hz
 IEC 60250
Comparative Tracking Index 175 V
175 V
IEC 60112