SABIC Innovative Plastics Valox® IQ8280SF PBT+PET (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , PET + PBT Unreinforced , Polyethylene Terephthalate (PET)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Valox®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Valox® IQ8280SF PBT+PET (Europe-Africa-Middle East).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Valox iQ8280SF resin is an environmentally responsible, low carbon footprint, and sustainable resin. Valox iQ8280SF resin offer Super High Flow characteristics combined with high modulus and excellent surface aesthetics.
Physical Properties Metric English Comments
Specific Gravity 1.66 g/cc
1.66 g/cc
ASTM D792
Density 1.65 g/cc
0.0596 lb/in³
ISO 1183
Moisture Absorption 0.140 %
0.140 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.070 %
0.070 %
ISO 62
Linear Mold Shrinkage, Flow 0.0030 - 0.0060 cm/cm

@Thickness 3.20 mm
0.0030 - 0.0060 in/in

@Thickness 0.126 in
SABIC Method
Melt Flow 43 g/10 min

@Load 2.16 kg,
Temperature 265 °C
43 g/10 min

@Load 4.76 lb,
Temperature 509 °F
ASTM D1238
Melt Index of Compound 35 g/10 min

@Load 2.16 kg,
Temperature 265 °C
35 g/10 min

@Load 4.76 lb,
Temperature 509 °F
MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Hardness, Rockwell R 120
120
ASTM D785
120
120
ISO 2039-2
Tensile Strength at Break 95.0 MPa
13800 psi
Type I, 5 mm/min; ASTM D638
115 MPa
16700 psi
5 mm/min; ISO 527
Tensile Strength, Yield 95.0 MPa
13800 psi
Type I, 5 mm/min; ASTM D638
115 MPa
16700 psi
5 mm/min; ISO 527
Elongation at Break 1.7 %
1.7 %
5 mm/min; ISO 527
2.0 %
2.0 %
Type I, 5 mm/min; ASTM D638
Elongation at Yield 1.7 %
1.7 %
5 mm/min; ISO 527
2.0 %
2.0 %
Type I, 5 mm/min; ASTM D638
Tensile Modulus 15.0 GPa
2180 ksi
5 mm/min; ASTM D638
15.0 GPa
2180 ksi
1 mm/min; ISO 527
Flexural Yield Strength 195 MPa
28300 psi
1.3 mm/min, 50 mm span; ASTM D790
195 MPa
28300 psi
2 mm/min; ISO 178
Flexural Modulus 12.1 GPa
1750 ksi
1.3 mm/min, 50 mm span; ASTM D790
12.2 GPa
1770 ksi
2 mm/min; ISO 178
Izod Impact, Notched 0.850 J/cm
1.59 ft-lb/in
ASTM D256
0.780 J/cm

@Temperature -30.0 °C
1.46 ft-lb/in

@Temperature -22.0 °F
ASTM D256
Izod Impact, Unnotched 7.00 J/cm
13.1 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 7.00 kJ/m²
3.33 ft-lb/in²
80*10*4; ISO 180/1A
7.00 kJ/m²

@Temperature -30.0 °C
3.33 ft-lb/in²

@Temperature -22.0 °F
80*10*4; ISO 180/1A
Charpy Impact, Notched 1.80 J/cm²
8.57 ft-lb/in²
Edgew 80*10*4 sp=62mm; ISO 179/1eA
Dart Drop, Total Energy 5.00 J

@Temperature 23.0 °C
3.69 ft-lb

@Temperature 73.4 °F
ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 17.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
9.44 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
17.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
9.44 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
CTE, linear, Transverse to Flow 69.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
38.3 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
69.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
38.3 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 218 °C
424 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
Deflection Temperature at 1.8 MPa (264 psi) 200 °C
392 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
197 °C

@Thickness 3.20 mm
387 °F

@Thickness 0.126 in
unannealed; ASTM D648
Vicat Softening Point 194 °C
381 °F
Rate B/120; ISO 306
195 °C
383 °F
Rate B/50; ASTM D1525
195 °C
383 °F
Rate B/50; ISO 306