SABIC Innovative Plastics Valox® K4560 PBT (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Valox®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Valox® K4560 PBT (Europe-Africa-Middle East).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
30% glass reinforced PBT. Impact modified, high flow, hydrolytically stable.
Physical Properties Metric English Comments
Specific Gravity 1.50 g/cc
1.50 g/cc
ASTM D792
Filler Content 30 %
30 %
glass; ISO 3451
Linear Mold Shrinkage, Flow 0.0060 - 0.0080 cm/cm

@Thickness 3.20 mm
0.0060 - 0.0080 in/in

@Thickness 0.126 in
SABIC Method
Linear Mold Shrinkage, Transverse 0.010 - 0.012 cm/cm

@Thickness 3.20 mm
0.010 - 0.012 in/in

@Thickness 0.126 in
SABIC Method
Melt Index of Compound 12 g/10 min

@Load 2.16 kg,
Temperature 250 °C
12 g/10 min

@Load 4.76 lb,
Temperature 482 °F
MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 96.0 MPa
13900 psi
Type I, 50 mm/min; ASTM D638
102 MPa
14800 psi
Type I, 5 mm/min; ASTM D638
107 MPa
15500 psi
Type I, 5 mm/min; ASTM D638
110 MPa
16000 psi
Type I, 5 mm/min; ASTM D638
112 MPa
16200 psi
Type I, 5 mm/min; ASTM D638
115 MPa
16700 psi
Type I, 5 mm/min; ASTM D638
120 MPa
17400 psi
5 mm/min; ISO 527
Tensile Strength, Yield 112 MPa
16200 psi
Type I, 5 mm/min; ASTM D638
Elongation at Break 2.2 %
2.2 %
Type I, 5 mm/min; ASTM D638
2.5 %
2.5 %
Type I, 5 mm/min; ASTM D638
3.0 %
3.0 %
Type I, 5 mm/min; ASTM D638
4.0 %
4.0 %
Type I, 5 mm/min; ASTM D638
4.0 %
4.0 %
Flexural Strain, 1.3 mm/min, 50 mm span; ASTM D790
4.2 %
4.2 %
Flexural Strain, 1.3 mm/min, 50 mm span; ASTM D790
4.2 %
4.2 %
Flexural Strain, 1.3 mm/min, 50 mm span; ASTM D790
4.5 %
4.5 %
Flexural Strain, 1.3 mm/min, 50 mm span; ASTM D790
Elongation at Yield 3.0 %
3.0 %
Type I, 5 mm/min; ASTM D638
4.0 %
4.0 %
Type I, 5 mm/min; ASTM D638
Tensile Modulus 8.84 GPa
1280 ksi
5 mm/min; ASTM D638
Flexural Strength 173 MPa
25100 psi
1.3 mm/min, 50 mm span; ASTM D790
175 MPa
25400 psi
2 mm/min; ISO 178
Flexural Modulus 7.10 GPa
1030 ksi
1.3 mm/min, 50 mm span; ASTM D790
7.20 GPa
1040 ksi
1.3 mm/min, 50 mm span; ASTM D790
7.40 GPa
1070 ksi
2 mm/min; ISO 178
7.40 GPa
1070 ksi
1.3 mm/min, 50 mm span; ASTM D790
7.50 GPa
1090 ksi
1.3 mm/min, 50 mm span; ASTM D790
8.00 GPa
1160 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 0.960 J/cm
1.80 ft-lb/in
ASTM D256
Izod Impact, Unnotched 8.17 J/cm
15.3 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 11.0 kJ/m²
5.23 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 52.0 kJ/m²
24.7 ft-lb/in²
80*10*4; ISO 180/1U
Dart Drop, Total Energy 6.00 J
4.43 ft-lb
ASTM D3763
7.00 J
5.16 ft-lb
ASTM D3763
8.00 J
5.90 ft-lb
ASTM D3763
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 220 °C

@Thickness 3.20 mm
428 °F

@Thickness 0.126 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 200 °C

@Thickness 3.20 mm
392 °F

@Thickness 0.126 in
unannealed; ASTM D648
Vicat Softening Point 204 °C
399 °F
Rate B/120; ISO 306