SABIC Innovative Plastics Valox® SHF4930 PBT (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Valox®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Valox® SHF4930 PBT (Europe-Africa-Middle East).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Super high flow FR PBT grade with 15% Glass reinforced
Physical Properties Metric English Comments
Specific Gravity 1.54 g/cc
1.54 g/cc
ASTM D792
Density 1.54 g/cc
0.0556 lb/in³
ISO 1183
Filler Content 15 %
15 %
ASTM D229
Moisture Absorption 0.0700 %
0.0700 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.23 %
0.23 %
ISO 62
Viscosity 65000 cP
65000 cP
Melt Viscosity, 260°C, 1500 sec-1; ISO 11443
90000 cP
90000 cP
Melt Viscosity, 250°C, 1500 sec-1; ISO 11443
Linear Mold Shrinkage, Flow 0.0050 - 0.0080 cm/cm
0.0050 - 0.0080 in/in
on Tensile Bar; SABIC Method
0.0050 - 0.0080 cm/cm

@Thickness 3.20 mm
 0.0050 - 0.0080 in/in

@Thickness 0.126 in
 SABIC Method
Linear Mold Shrinkage, Transverse 0.0060 - 0.0090 cm/cm
0.0060 - 0.0090 in/in
on Tensile Bar; SABIC Method
Melt Flow 18 g/10 min

@Load 2.16 kg,
Temperature 250 °C
 18 g/10 min

@Load 4.76 lb,
Temperature 482 °F
 ASTM D1238
20 g/10 min

@Load 2.16 kg,
Temperature 250 °C
 20 g/10 min

@Load 4.76 lb,
Temperature 482 °F
 ISO 1133
Melt Index of Compound 16 g/10 min

@Load 2.16 kg,
Temperature 250 °C
 16 g/10 min

@Load 4.76 lb,
Temperature 482 °F
 MVR [cm^3/10 min]; ISO 1133
53 g/10 min

@Load 5.00 kg,
Temperature 250 °C
 53 g/10 min

@Load 11.0 lb,
Temperature 482 °F
 MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Hardness, Rockwell R 117
117
ISO 2039-2
Hardness, H358/30 190 MPa
27600 psi
ISO 2039-1
Tensile Strength at Break 80.0 MPa
11600 psi
Type I, 5 mm/min; ASTM D638
85.0 MPa
12300 psi
5 mm/min; ISO 527
Tensile Strength, Yield 80.0 MPa
11600 psi
Type I, 5 mm/min; ASTM D638
85.0 MPa
12300 psi
5 mm/min; ISO 527
Elongation at Break 2.0 %
2.0 %
Type I, 5 mm/min; ASTM D638
2.0 %
2.0 %
5 mm/min; ISO 527
3.0 %
3.0 %
Flexural Strain, break, 2 mm/min; ISO 178
Elongation at Yield 2.0 %
2.0 %
Type I, 5 mm/min; ASTM D638
2.0 %
2.0 %
5 mm/min; ISO 527
Tensile Modulus 6.20 GPa
899 ksi
1 mm/min; ISO 527
6.30 GPa
914 ksi
5 mm/min; ASTM D638
Flexural Strength 140 MPa
20300 psi
2 mm/min; ISO 178
Flexural Yield Strength 129 MPa
18700 psi
1.3 mm/min, 50 mm span; ASTM D790
140 MPa
20300 psi
2 mm/min; ISO 178
Flexural Modulus 5.17 GPa
750 ksi
1.3 mm/min, 50 mm span; ASTM D790
5.30 GPa
769 ksi
2 mm/min; ISO 178
Izod Impact, Notched 0.500 J/cm
0.937 ft-lb/in
ASTM D256
0.500 J/cm

@Temperature 0.000 °C
 0.937 ft-lb/in

@Temperature 32.0 °F
 ASTM D256
0.500 J/cm

@Temperature -30.0 °C
 0.937 ft-lb/in

@Temperature -22.0 °F
 ASTM D256
Izod Impact, Unnotched 3.10 J/cm
5.81 ft-lb/in
ASTM D4812
2.65 J/cm

@Temperature -30.0 °C
 4.96 ft-lb/in

@Temperature -22.0 °F
 ASTM D4812
Izod Impact, Notched (ISO) 6.00 kJ/m²
2.86 ft-lb/in²
80*10*4; ISO 180/1A
6.00 kJ/m²

@Temperature 0.000 °C
 2.86 ft-lb/in²

@Temperature 32.0 °F
 80*10*4; ISO 180/1A
6.00 kJ/m²

@Temperature -30.0 °C
 2.86 ft-lb/in²

@Temperature -22.0 °F
 80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 25.0 kJ/m²
11.9 ft-lb/in²
80*10*4; ISO 180/1U
19.0 kJ/m²

@Temperature -30.0 °C
 9.04 ft-lb/in²

@Temperature -22.0 °F
 80*10*4; ISO 180/1U
Charpy Impact Unnotched 2.90 J/cm²
13.8 ft-lb/in²
ISO 179/2C
2.30 J/cm²

@Temperature -30.0 °C
 10.9 ft-lb/in²

@Temperature -22.0 °F
 ISO 179/2C
Charpy Impact, Notched 0.600 J/cm²
2.86 ft-lb/in²
Edgew 80*10*4 sp=62mm; ISO 179/1eA
0.600 J/cm²
2.86 ft-lb/in²
ISO 179/2C
0.600 J/cm²

@Temperature -30.0 °C
 2.86 ft-lb/in²

@Temperature -22.0 °F
 ISO 179/2C
Dart Drop, Total Energy 55.0 J

@Temperature 23.0 °C
 40.6 ft-lb

@Temperature 73.4 °F
 ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 39.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 21.7 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
42.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 23.3 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
CTE, linear, Transverse to Flow 93.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 51.7 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
98.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 54.4 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 215 °C
419 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
215 °C

@Thickness 3.20 mm
 419 °F

@Thickness 0.126 in
 unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 195 °C
383 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
195 °C

@Thickness 3.20 mm
 383 °F

@Thickness 0.126 in
 unannealed; ASTM D648
Vicat Softening Point 195 °C
383 °F
Rate B/120; ISO 306
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+15 ohm-cm
>= 1.00e+15 ohm-cm
IEC 60093
Surface Resistance >= 1.00e+12 ohm
>= 1.00e+12 ohm
ROA; IEC 60093
Dielectric Strength 17.5 kV/mm

@Thickness 3.20 mm
 445 kV/in

@Thickness 0.126 in
 in oil; IEC 60243-1
27.0 kV/mm

@Thickness 1.50 mm
 686 kV/in

@Thickness 0.0591 in
 in oil; IEC 60243-1
27.5 kV/mm

@Thickness 1.60 mm
 699 kV/in

@Thickness 0.0630 in
 in oil; IEC 60243-1
40.0 kV/mm

@Thickness 0.800 mm
 1020 kV/in

@Thickness 0.0315 in
 in oil; IEC 60243-1
Dissipation Factor 0.016

@Frequency 1.00e+6 Hz
 0.016

@Frequency 1.00e+6 Hz
 IEC 60250
Comparative Tracking Index 275 V
275 V
IEC 60112
Hot Wire Ignition, HWI 15 - 30 sec
15 - 30 sec
UL 746A
High Amp Arc Ignition, HAI >= 120 arcs
>= 120 arcs
UL 746A