SABIC Innovative Plastics Valox® V9561 PET (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , Polyester, TP , Polyethylene Terephthalate (PET)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Valox®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Valox® V9561 PET (Europe-Africa-Middle East).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Flame retardant PET, 30% Glass fiber filled. Offering a good balance in CTI , GWIT , High Heat and mechanical performances.
Physical Properties Metric English Comments
Specific Gravity 1.74 g/cc
1.74 g/cc
ASTM D792
Density 1.74 g/cc
0.0629 lb/in³
ISO 1183
Filler Content 36 %
36 %
ASTM D229
Moisture Absorption 0.250 %
0.250 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.050 %
0.050 %
ISO 62
Viscosity 260000 cP
260000 cP
Melt Viscosity, 260°C, 1500 sec-1; ISO 11443
Linear Mold Shrinkage, Flow 0.0010 - 0.0030 cm/cm
0.0010 - 0.0030 in/in
on Tensile Bar; SABIC Method
Melt Flow 30 g/10 min

@Load 5.00 kg,
Temperature 265 °C
30 g/10 min

@Load 11.0 lb,
Temperature 509 °F
ASTM D1238
30 g/10 min

@Load 5.00 kg,
Temperature 266 °C
30 g/10 min

@Load 11.0 lb,
Temperature 511 °F
ASTM D1238
Melt Index of Compound 33 g/10 min

@Load 5.00 kg,
Temperature 280 °C
33 g/10 min

@Load 11.0 lb,
Temperature 536 °F
MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Hardness, Rockwell R 118
118
ISO 2039-2
Hardness, H358/30 265 MPa
38400 psi
ISO 2039-1
Tensile Strength at Break 143 MPa
20700 psi
5 mm/min; ISO 527
145 MPa
21000 psi
Type I, 5 mm/min; ASTM D638
Tensile Strength, Yield 143 MPa
20700 psi
5 mm/min; ISO 527
145 MPa
21000 psi
Type I, 5 mm/min; ASTM D638
Elongation at Break 2.0 %
2.0 %
5 mm/min; ISO 527
2.2 %
2.2 %
Type I, 5 mm/min; ASTM D638
2.3 %
2.3 %
Flexural Strain, break, 2 mm/min; ISO 178
Elongation at Yield 2.0 %
2.0 %
5 mm/min; ISO 527
2.2 %
2.2 %
Type I, 5 mm/min; ASTM D638
Tensile Modulus 13.0 GPa
1890 ksi
1 mm/min; ISO 527
13.0 GPa
1890 ksi
5 mm/min; ASTM D638
Flexural Strength 190 MPa
27600 psi
2 mm/min; ISO 178
Flexural Yield Strength 190 MPa
27600 psi
2 mm/min; ISO 178
Flexural Modulus 10.75 GPa
1559 ksi
2 mm/min; ISO 178
Izod Impact, Notched 0.600 J/cm
1.12 ft-lb/in
ASTM D256
0.600 J/cm

@Temperature -30.0 °C
1.12 ft-lb/in

@Temperature -22.0 °F
ASTM D256
0.600 J/cm

@Temperature 0.000 °C
1.12 ft-lb/in

@Temperature 32.0 °F
ASTM D256
Izod Impact, Unnotched 5.50 J/cm
10.3 ft-lb/in
ASTM D4812
4.25 J/cm

@Temperature -30.0 °C
7.96 ft-lb/in

@Temperature -22.0 °F
ASTM D4812
Izod Impact, Notched (ISO) 6.00 kJ/m²
2.86 ft-lb/in²
80*10*4; ISO 180/1A
6.00 kJ/m²

@Temperature 0.000 °C
2.86 ft-lb/in²

@Temperature 32.0 °F
80*10*4; ISO 180/1A
6.00 kJ/m²

@Temperature -30.0 °C
2.86 ft-lb/in²

@Temperature -22.0 °F
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 35.0 kJ/m²
16.7 ft-lb/in²
80*10*4; ISO 180/1U
35.0 kJ/m²

@Temperature -30.0 °C
16.7 ft-lb/in²

@Temperature -22.0 °F
80*10*4; ISO 180/1U
Charpy Impact Unnotched 3.50 J/cm²
16.7 ft-lb/in²
ISO 179/2C
3.00 J/cm²

@Temperature -30.0 °C
14.3 ft-lb/in²

@Temperature -22.0 °F
ISO 179/2C
Charpy Impact, Notched 0.700 J/cm²
3.33 ft-lb/in²
Edgew 80*10*4 sp=62mm; ISO 179/1eA
0.700 J/cm²
3.33 ft-lb/in²
ISO 179/2C
0.600 J/cm²

@Temperature -30.0 °C
2.86 ft-lb/in²

@Temperature -22.0 °F
ISO 179/2C
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 19.0 µm/m-°C

@Temperature 23.0 - 80.0 °C
10.6 µin/in-°F

@Temperature 73.4 - 176 °F
ISO 11359-2
CTE, linear, Transverse to Flow 67.0 µm/m-°C

@Temperature 23.0 - 80.0 °C
37.2 µin/in-°F

@Temperature 73.4 - 176 °F
ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 245 °C
473 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
Deflection Temperature at 1.8 MPa (264 psi) 200 °C
392 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
Vicat Softening Point 235 °C
455 °F
Rate B/50; ASTM D1525
235 °C
455 °F
Rate B/50; ISO 306
235 °C
455 °F
Rate B/120; ISO 306
255 °C
491 °F
Rate A/50; ISO 306
255 °C
491 °F
Rate A/50; ASTM D1525
UL RTI, Electrical 150 °C
302 °F
UL 746B
UL RTI, Mechanical with Impact 90.0 °C
194 °F
UL 746B
UL RTI, Mechanical without Impact 150 °C
302 °F
UL 746B
Flammability, UL94 V-0

@Thickness 0.800 mm
V-0

@Thickness 0.0315 in
UL 94 by SABIC-IP
Glow Wire Test 800 °C
1470 °F
IEC 60695-2-13
800 °C
1470 °F
IEC 60695-2-13
800 °C
1470 °F
IEC 60695-2-13
960 °C

@Thickness 1.00 - 3.00 mm
1760 °F

@Thickness 0.0394 - 0.118 in
IEC 60695-2-12
Electrical Properties Metric English Comments
Comparative Tracking Index 200 V
200 V
IEC 60112
175 - 250 V
175 - 250 V
UL 746A
Hot Wire Ignition, HWI >= 120 sec
>= 120 sec
UL 746A
High Amp Arc Ignition, HAI 15 - 30 arcs
15 - 30 arcs
UL 746A
Descriptive Properties Value Comments
Ball Pressure Test, 125°C +/- 2°C pass
IEC 60695-10-2
Copyright © lookpolymers.com All Rights Reserved