SABIC Innovative Plastics XYLEX FXY330DF PC+POLYESTER (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate/PET Polyester Blend , Polyester, TP , Polyethylene Terephthalate (PET)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Xylex
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics XYLEX FXY330DF PC+POLYESTER (Europe-Africa-Middle East).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Polyester+PC alloy. Diffusion Effect. Color package may affect performance.
Physical Properties Metric English Comments
Specific Gravity 1.17 g/cc
1.17 g/cc
ASTM D792
Density 1.17 g/cc
0.0423 lb/in³
ISO 1183
Moisture Absorption 0.270 %
0.270 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.70 %
0.70 %
ISO 62
Linear Mold Shrinkage, Flow 0.0050 - 0.0070 cm/cm

@Thickness 3.20 mm
 0.0050 - 0.0070 in/in

@Thickness 0.126 in
 SABIC Method
Linear Mold Shrinkage, Transverse 0.0040 - 0.0060 cm/cm

@Thickness 3.20 mm
 0.0040 - 0.0060 in/in

@Thickness 0.126 in
 SABIC Method
Melt Flow 15 g/10 min

@Load 2.16 kg,
Temperature 265 °C
 15 g/10 min

@Load 4.76 lb,
Temperature 509 °F
 ASTM D1238
Melt Index of Compound 13 g/10 min

@Load 2.16 kg,
Temperature 265 °C
 13 g/10 min

@Load 4.76 lb,
Temperature 509 °F
 MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 49.0 MPa
7110 psi
Type I, 50 mm/min; ASTM D638
50.0 MPa
7250 psi
50 mm/min; ISO 527
Tensile Strength, Yield 47.0 MPa
6820 psi
Type I, 50 mm/min; ASTM D638
49.0 MPa
7110 psi
50 mm/min; ISO 527
Elongation at Break 170 %
170 %
Type I, 50 mm/min; ASTM D638
>= 200 %
>= 200 %
50 mm/min; ISO 527
Elongation at Yield 5.0 %
5.0 %
Type I, 50 mm/min; ASTM D638
>= 5.0 %
>= 5.0 %
50 mm/min; ISO 527
Tensile Modulus 1.44 GPa
209 ksi
50 mm/min; ASTM D638
1.58 GPa
229 ksi
1 mm/min; ISO 527
Flexural Yield Strength 67.0 MPa
9720 psi
1.3 mm/min, 50 mm span; ASTM D790
77.0 MPa
11200 psi
2 mm/min; ISO 178
Flexural Modulus 1.50 GPa
218 ksi
1.3 mm/min, 50 mm span; ASTM D790
1.60 GPa
232 ksi
2 mm/min; ISO 178
Izod Impact, Notched 0.700 J/cm
1.31 ft-lb/in
ASTM D256
0.550 J/cm

@Temperature -30.0 °C
 1.03 ft-lb/in

@Temperature -22.0 °F
 ASTM D256
0.640 J/cm

@Temperature 0.000 °C
 1.20 ft-lb/in

@Temperature 32.0 °F
 ASTM D256
Izod Impact, Notched (ISO) 7.00 kJ/m²
3.33 ft-lb/in²
80*10*4; ISO 180/1A
4.00 kJ/m²

@Temperature -30.0 °C
 1.90 ft-lb/in²

@Temperature -22.0 °F
 80*10*4; ISO 180/1A
Charpy Impact, Notched 0.700 J/cm²
3.33 ft-lb/in²
Edgew 80*10*4 sp=62mm; ISO 179/1eA
Dart Drop, Total Energy 60.0 J

@Temperature 23.0 °C
 44.3 ft-lb

@Temperature 73.4 °F
 ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 89.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 49.4 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
90.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 50.0 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
CTE, linear, Transverse to Flow 90.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 50.0 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
94.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 52.2 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
Deflection Temperature at 1.8 MPa (264 psi) 78.0 °C
172 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
72.0 °C

@Thickness 3.20 mm
 162 °F

@Thickness 0.126 in
 unannealed; ASTM D648
Vicat Softening Point 90.0 °C
194 °F
Rate B/50; ASTM D1525
92.0 °C
198 °F
Rate B/50; ISO 306
93.0 °C
199 °F
Rate B/120; ISO 306