SABIC Innovative Plastics XYLEX X7503 PC+POLYESTER (Asia Pacific)

Category Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate/PET Polyester Blend , Polyester, TP , Polyethylene Terephthalate (PET)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Xylex
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics XYLEX X7503 PC+POLYESTER (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PC-Siloxane copolymer + Polyester alloy, High Impact, Transparent
Physical Properties Metric English Comments
Specific Gravity 1.20 g/cc
1.20 g/cc
ASTM D792
Density 1.20 g/cc
0.0434 lb/in³
ISO 1183
Moisture Absorption 0.200 %
0.200 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.50 %
0.50 %
ISO 62
Linear Mold Shrinkage, Flow 0.0060 - 0.0080 cm/cm

@Thickness 3.20 mm
0.0060 - 0.0080 in/in

@Thickness 0.126 in
SABIC Method
Melt Flow 8.0 g/10 min

@Load 2.16 kg,
Temperature 265 °C
8.0 g/10 min

@Load 4.76 lb,
Temperature 509 °F
ASTM D1238
Melt Index of Compound 8.0 g/10 min

@Load 2.16 kg,
Temperature 265 °C
8.0 g/10 min

@Load 4.76 lb,
Temperature 509 °F
MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 54.0 MPa
7830 psi
50 mm/min; ISO 527
55.0 MPa
7980 psi
Type I, 50 mm/min; ASTM D638
Tensile Strength, Yield 57.0 MPa
8270 psi
Type I, 50 mm/min; ASTM D638
58.0 MPa
8410 psi
50 mm/min; ISO 527
Elongation at Break 100 %
100 %
Type I, 50 mm/min; ASTM D638
100 %
100 %
50 mm/min; ISO 527
Elongation at Yield 5.0 %
5.0 %
Type I, 50 mm/min; ASTM D638
6.0 %
6.0 %
50 mm/min; ISO 527
Tensile Modulus 2.10 GPa
305 ksi
5 mm/min; ASTM D638
2.10 GPa
305 ksi
1 mm/min; ISO 527
Flexural Yield Strength 84.0 MPa
12200 psi
2 mm/min; ISO 178
86.0 MPa
12500 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 1.90 GPa
276 ksi
1.3 mm/min, 50 mm span; ASTM D790
2.10 GPa
305 ksi
2 mm/min; ISO 178
Izod Impact, Notched 9.20 J/cm
17.2 ft-lb/in
ASTM D256
7.50 J/cm

@Temperature -30.0 °C
14.1 ft-lb/in

@Temperature -22.0 °F
ASTM D256
Izod Impact, Notched (ISO) 68.0 kJ/m²
32.4 ft-lb/in²
80*10*4; ISO 180/1A
17.0 kJ/m²

@Temperature -30.0 °C
8.09 ft-lb/in²

@Temperature -22.0 °F
80*10*4; ISO 180/1A
Charpy Impact, Notched 7.00 J/cm²
33.3 ft-lb/in²
Edgew 80*10*4 sp=62mm; ISO 179/1eA
Dart Drop, Total Energy 71.0 J

@Temperature 23.0 °C
52.4 ft-lb

@Temperature 73.4 °F
ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 70.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
38.9 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
77.0 µm/m-°C

@Temperature 23.0 - 60.0 °C
42.8 µin/in-°F

@Temperature 73.4 - 140 °F
ISO 11359-2
CTE, linear, Transverse to Flow 70.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
38.9 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
78.0 µm/m-°C

@Temperature 23.0 - 60.0 °C
43.3 µin/in-°F

@Temperature 73.4 - 140 °F
ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 124 °C
255 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
124 °C

@Thickness 3.20 mm
255 °F

@Thickness 0.126 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 110 °C
230 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
110 °C

@Thickness 3.20 mm
230 °F

@Thickness 0.126 in
unannealed; ASTM D648
Vicat Softening Point 130 °C
266 °F
Rate B/50; ISO 306
132 °C
270 °F
Rate B/120; ISO 306
132 °C
270 °F
Rate B/50; ASTM D1525
Flammability, UL94 V-2

@Thickness 3.00 mm
V-2

@Thickness 0.118 in
UL 94
Optical Properties Metric English Comments
Haze 2.0 %

@Thickness 2.54 mm
2.0 %

@Thickness 0.100 in
ASTM D1003
Transmission, Visible 86 %
86 %
2.54 mm; ASTM D1003