SABIC Innovative Plastics XYLEX X7507 PC+POLYESTER (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate/PET Polyester Blend , Polyester, TP , Polyethylene Terephthalate (PET)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Xylex
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics XYLEX X7507 PC+POLYESTER (Europe-Africa-Middle East).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
F-1 weathering certified in natural color, specially designed for Pool & Spa applications. Currently available in natural color only.
Physical Properties Metric English Comments
Specific Gravity 1.20 g/cc
1.20 g/cc
ASTM D792
Density 1.20 g/cc
0.0434 lb/in³
ISO 1183
Moisture Absorption 0.120 %
0.120 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.32 %
0.32 %
ISO 62
Linear Mold Shrinkage, Flow 0.0050 - 0.0080 cm/cm

@Thickness 3.20 mm
 0.0050 - 0.0080 in/in

@Thickness 0.126 in
 SABIC Method
Melt Flow 8.0 g/10 min

@Load 2.16 kg,
Temperature 265 °C
 8.0 g/10 min

@Load 4.76 lb,
Temperature 509 °F
 ASTM D1238
Melt Index of Compound 5.0 g/10 min

@Load 2.16 kg,
Temperature 265 °C
 5.0 g/10 min

@Load 4.76 lb,
Temperature 509 °F
 MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 59.0 MPa
8560 psi
50 mm/min; ISO 527
65.0 MPa
9430 psi
Type I, 50 mm/min; ASTM D638
Tensile Strength, Yield 61.0 MPa
8850 psi
Type I, 50 mm/min; ASTM D638
62.0 MPa
8990 psi
50 mm/min; ISO 527
Elongation at Break 110 %
110 %
50 mm/min; ISO 527
130 %
130 %
Type I, 50 mm/min; ASTM D638
Elongation at Yield 5.4 %
5.4 %
50 mm/min; ISO 527
6.0 %
6.0 %
Type I, 50 mm/min; ASTM D638
Tensile Modulus 2.30 GPa
334 ksi
5 mm/min; ASTM D638
2.66 GPa
386 ksi
1 mm/min; ISO 527
Flexural Yield Strength 92.0 MPa
13300 psi
2 mm/min; ISO 178
96.0 MPa
13900 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 2.18 GPa
316 ksi
2 mm/min; ISO 178
2.32 GPa
336 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 9.90 J/cm
18.5 ft-lb/in
ASTM D256
2.00 J/cm

@Temperature -30.0 °C
 3.75 ft-lb/in

@Temperature -22.0 °F
 ASTM D256
Izod Impact, Notched (ISO) 9.00 kJ/m²
4.28 ft-lb/in²
80*10*4; ISO 180/1A
6.00 kJ/m²

@Temperature -30.0 °C
 2.86 ft-lb/in²

@Temperature -22.0 °F
 80*10*4; ISO 180/1A
Charpy Impact, Notched 2.00 J/cm²
9.52 ft-lb/in²
Edgew 80*10*4 sp=62mm; ISO 179/1eA
Dart Drop, Total Energy 79.0 J

@Temperature 23.0 °C
 58.3 ft-lb

@Temperature 73.4 °F
 ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 60.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 33.3 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
60.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 33.3 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
CTE, linear, Transverse to Flow 63.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 35.0 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
70.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 38.9 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
Deflection Temperature at 1.8 MPa (264 psi) 105 °C
221 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
104 °C

@Thickness 3.20 mm
 219 °F

@Thickness 0.126 in
 unannealed; ASTM D648
Vicat Softening Point 125 °C
257 °F
Rate B/50; ASTM D1525
125 °C
257 °F
Rate B/50; ISO 306
127 °C
261 °F
Rate B/120; ISO 306
Optical Properties Metric English Comments
Haze 1.6 %

@Thickness 2.54 mm
 1.6 %

@Thickness 0.100 in
 ASTM D1003
Transmission, Visible >= 85 %
>= 85 %
2.54 mm; ASTM D1003