SABIC Innovative Plastics Xenoy® 5220 PBT+PC (Asia Pacific)

Category Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate/Polybutylene Terephthalate (PBT) Blend, Unreinforced , Polyester, TP , Polybutylene Terephthalate (PBT)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Xenoy®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Xenoy® 5220 PBT+PC (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Unreinforced, polycarbonate-based polymer blend, excellent chemical resistance and impact.This data was supplied by SABIC-IP for the Asia Pacific region.
Physical Properties Metric English Comments
Specific Gravity 1.21 g/cc
1.21 g/cc
ASTM D 792
Water Absorption 0.12 %

@Time 86400 sec
 0.12 %

@Time 24.0 hour
 ASTM D 570
Linear Mold Shrinkage, Flow 0.0080 - 0.010 cm/cm

@Thickness 3.20 mm
 0.0080 - 0.010 in/in

@Thickness 0.126 in
 SABIC Method
Linear Mold Shrinkage, Transverse 0.0080 - 0.010 cm/cm
0.0080 - 0.010 in/in
on tensile bar; SABIC Method
Mechanical Properties Metric English Comments
Hardness, Rockwell R 112
112
ASTM D 785
Tensile Strength at Break 58.0 MPa
8410 psi
Type I, 50 mm/min; ASTM D 638
Tensile Strength, Yield 53.0 MPa
7690 psi
Type I, 50 mm/min; ASTM D 638
Elongation at Break 120 %
120 %
Type I, 50 mm/min; ASTM D 638
Flexural Yield Strength 84.0 MPa
12200 psi
1.3 mm/min, 50 mm span; ASTM D 790
Flexural Modulus 2.04 GPa
296 ksi
1.3 mm/min, 50 mm span; ASTM D 790
Izod Impact, Notched 2.99 J/cm

@Temperature -40.0 °C
 5.60 ft-lb/in

@Temperature -40.0 °F
 ASTM D 256
7.10 J/cm

@Temperature 23.0 °C
 13.3 ft-lb/in

@Temperature 73.4 °F
 ASTM D 256
Izod Impact, Unnotched 32.04 J/cm

@Temperature 23.0 °C
 60.02 ft-lb/in

@Temperature 73.4 °F
 ASTM D 4812
Gardner Impact 54.0 J

@Temperature 23.0 °C
 39.8 ft-lb

@Temperature 73.4 °F
 ASTM D 3029
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 77.4 µm/m-°C

@Temperature -40.0 - 40.0 °C
 43.0 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
90.0 µm/m-°C

@Temperature -40.0 - 95.0 °C
 50.0 µin/in-°F

@Temperature -40.0 - 203 °F
 ASTM E 831
110 µm/m-°C

@Temperature 60.0 - 138 °C
 61.1 µin/in-°F

@Temperature 140 - 280 °F
 ASTM E 831
Deflection Temperature at 0.46 MPa (66 psi) 106 °C

@Thickness 6.40 mm
 223 °F

@Thickness 0.252 in
 unannealed; ASTM D 648
Deflection Temperature at 1.8 MPa (264 psi) 98.0 °C

@Thickness 6.40 mm
 208 °F

@Thickness 0.252 in
 unannealed; ASTM D 648
UL RTI, Electrical 75.0 °C
167 °F
UL 746B
UL RTI, Mechanical with Impact 75.0 °C
167 °F
UL 746B
UL RTI, Mechanical without Impact 75.0 °C
167 °F
UL 746B
Flammability, UL94 HB

@Thickness 1.47 mm
 HB

@Thickness 0.0579 in
 UL 94
Electrical Properties Metric English Comments
Volume Resistivity 2.40e+16 ohm-cm
2.40e+16 ohm-cm
ASTM D 257
Dielectric Constant 2.99

@Frequency 100 Hz
 2.99

@Frequency 100 Hz
 ASTM D 150
3.04

@Frequency 1.00e+6 Hz
 3.04

@Frequency 1.00e+6 Hz
 ASTM D 150
Dielectric Strength 20.7 kV/mm

@Thickness 3.20 mm
 526 kV/in

@Thickness 0.126 in
 in air; ASTM D 149
Dissipation Factor 0.0020

@Frequency 100 Hz
 0.0020

@Frequency 100 Hz
 ASTM D 150
0.019

@Frequency 1.00e+6 Hz
 0.019

@Frequency 1.00e+6 Hz
 ASTM D 150
Arc Resistance 120 - 180 sec
120 - 180 sec
Tungsten, PLC code 5; ASTM D 495
Comparative Tracking Index 400 - 600 V
400 - 600 V
PLC code 1; UL 746A
Hot Wire Ignition, HWI 15 - 30 sec
15 - 30 sec
PLC code 3; UL 746A
High Amp Arc Ignition, HAI >= 120 arcs
>= 120 arcs
surface, PLC code 0; UL 746A
High Voltage Arc-Tracking Rate, HVTR 0.000 - 10.0 mm/min
0.000 - 0.394 in/min
PLC code 0; UL 746A