SABIC Innovative Plastics Xenoy® HX5600HP PBT+PC (Asia Pacific)
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate/Polybutylene Terephthalate (PBT) Blend, Unreinforced , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Xenoy® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Xenoy® HX5600HP PBT+PC (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Xenoy HX5600HP is PBT based semi-crystalline blend with balanced flow and impact properties. Improved chemical resistance against lab disinfectants and chemicals for healthcare enclosure and housing applications. Healthcare management of change, biocompatible (ISO10993 or USP Class VI). EtO, Gamma and Steam sterilizable.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.22 g/cc | 1.22 g/cc | ASTM D792 |
| Density | 1.22 g/cc | 0.0441 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.0500 % | 0.0500 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.40 % | 0.40 % | ISO 62 |
| Viscosity | 260000 cP | 260000 cP | Melt Viscosity, 260°C, 1500 sec-1; ISO 11443 |
| Linear Mold Shrinkage, Flow | 0.0070 - 0.011 cm/cm @Thickness 3.20 mm |
0.0070 - 0.011 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 11 g/10 min @Load 5.00 kg, Temperature 250 °C |
11 g/10 min @Load 11.0 lb, Temperature 482 °F |
ASTM D1238 |
| Melt Index of Compound | 10 g/10 min @Load 5.00 kg, Temperature 250 °C |
10 g/10 min @Load 11.0 lb, Temperature 482 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 52.0 MPa | 7540 psi | Type I, 50 mm/min; ASTM D638 |
| 55.0 MPa | 7980 psi | 50 mm/min; ISO 527 | |
| Tensile Strength, Yield | 50.0 MPa | 7250 psi | Type I, 50 mm/min; ASTM D638 |
| 50.0 MPa | 7250 psi | 50 mm/min; ISO 527 | |
| Elongation at Break | 100 % | 100 % | 50 mm/min; ISO 527 |
| 150 % | 150 % | Type I, 50 mm/min; ASTM D638 | |
| Elongation at Yield | 5.0 % | 5.0 % | Type I, 50 mm/min; ASTM D638 |
| 5.0 % | 5.0 % | 50 mm/min; ISO 527 | |
| Tensile Modulus | 2.05 GPa | 297 ksi | 1 mm/min; ISO 527 |
| 2.10 GPa | 305 ksi | 5 mm/min; ASTM D638 | |
| Flexural Yield Strength | 70.0 MPa | 10200 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 75.0 MPa | 10900 psi | 2 mm/min; ISO 178 | |
| Flexural Modulus | 2.00 GPa | 290 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 2.05 GPa | 297 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 7.50 J/cm | 14.1 ft-lb/in | ASTM D256 |
| 6.00 J/cm @Temperature -30.0 °C |
11.2 ft-lb/in @Temperature -22.0 °F |
ASTM D256 | |
| Izod Impact, Notched (ISO) | 55.0 kJ/m² | 26.2 ft-lb/in² | 80*10*4; ISO 180/1A |
| 25.0 kJ/m² @Temperature -30.0 °C |
11.9 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | NB @Temperature -40.0 °C |
NB @Temperature -40.0 °F |
80*10*4; ISO 180/1U |
| Charpy Impact Unnotched | NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
Edgew 80*10*3 sp=62mm; ISO 179/1eU |
| Charpy Impact, Notched | 6.00 J/cm² | 28.6 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| Dart Drop, Total Energy | 80.0 J @Temperature 23.0 °C |
59.0 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 90.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
50.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 90.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
50.0 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| 100 µm/m-°C @Temperature 23.0 - 60.0 °C |
55.6 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 90.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
50.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 90.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
50.0 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 105 °C | 221 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 80.0 °C | 176 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 80.0 °C @Thickness 3.20 mm |
176 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Vicat Softening Point | 123 °C | 253 °F | Rate B/120; ISO 306 |
| 125 °C | 257 °F | Rate B/50; ASTM D1525 | |
| 125 °C | 257 °F | Rate B/50; ISO 306 |
Users viewing this material also viewed the following:
- Niche Polymer PPCT20BK Copolymer PP, 20% Talc Filled
- Aremco Aremco-Seal™ FO-380 High Temperature Specialty Coatings Silicone, Ceramic Filled (discontinued **)
- NanoAmor 90%, OD: 1-2 nm COOH Functionalized Single Walled Carbon Nanotubes
- PolyOne Stat-Tech™ AS-10NCF/000 ABS - 10% Nickel Coated Carbon Fiber (discontinued **)
- SABIC Innovative Plastics LNP LUBRICOMP WL004 PBT (Europe-Africa-Middle East)
- Samyang Tribit® 1500G15 Polybutylene Terephthalate, 15% Glass Reinforced
- Total PPM H350 Polypropylene, Homopolymer Medical Grade
- A. Schulman POLYBATCH™ Tan LL60139/2 Concentrate Based In LLDPE
- Radici Radilene® R 30 IE 0 3036 B Low Density Polyethylene
Copyright © lookpolymers.com All Rights Reserved