SABIC Innovative Plastics Xenoy® X5300WX PBT+PC (Asia Pacific)

Category Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate/Polybutylene Terephthalate (PBT) Blend, Unreinforced , Polyester, TP , Polybutylene Terephthalate (PBT)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Xenoy®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Xenoy® X5300WX PBT+PC (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Unreinforced, opaque PBT+PC alloy. Chemical resistance and good mechanical performance. UV-stabilized. Excellent weatherability.
Physical Properties Metric English Comments
Specific Gravity 1.23 g/cc
1.23 g/cc
ASTM D792
Density 1.23 g/cc
0.0444 lb/in³
ISO 1183
Moisture Absorption 0.150 %
0.150 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.50 %
0.50 %
ISO 62
Linear Mold Shrinkage, Flow 0.0070 - 0.0090 cm/cm

@Thickness 3.20 mm
 0.0070 - 0.0090 in/in

@Thickness 0.126 in
 SABIC Method
Melt Flow 26 g/10 min

@Load 5.00 kg,
Temperature 266 °C
 26 g/10 min

@Load 11.0 lb,
Temperature 511 °F
 ASTM D1238
Melt Index of Compound 25 g/10 min

@Load 5.00 kg,
Temperature 265 °C
 25 g/10 min

@Load 11.0 lb,
Temperature 509 °F
 MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 51.0 MPa
7400 psi
Type I, 50 mm/min; ASTM D638
51.0 MPa
7400 psi
50 mm/min; ISO 527
Tensile Strength, Yield 62.0 MPa
8990 psi
Type I, 50 mm/min; ASTM D638
62.0 MPa
8990 psi
50 mm/min; ISO 527
Elongation at Break 110 %
110 %
Type I, 50 mm/min; ASTM D638
110 %
110 %
50 mm/min; ISO 527
Elongation at Yield 5.0 %
5.0 %
Type I, 50 mm/min; ASTM D638
5.0 %
5.0 %
50 mm/min; ISO 527
Tensile Modulus 2.25 GPa
326 ksi
1 mm/min; ISO 527
2.55 GPa
370 ksi
50 mm/min; ASTM D638
Flexural Yield Strength 87.0 MPa
12600 psi
2 mm/min; ISO 178
96.0 MPa
13900 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 2.18 GPa
316 ksi
2 mm/min; ISO 178
2.48 GPa
360 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 7.47 J/cm
14.0 ft-lb/in
ASTM D256
1.80 J/cm

@Temperature -30.0 °C
 3.37 ft-lb/in

@Temperature -22.0 °F
 ASTM D256
Izod Impact, Notched (ISO) 50.0 kJ/m²
23.8 ft-lb/in²
80*10*4; ISO 180/1A
15.0 kJ/m²

@Temperature -30.0 °C
 7.14 ft-lb/in²

@Temperature -22.0 °F
 80*10*4; ISO 180/1A
Charpy Impact, Notched 4.50 J/cm²
21.4 ft-lb/in²
Edgew 80*10*4 sp=62mm; ISO 179/1eA
Dart Drop, Total Energy 71.0 J

@Temperature 23.0 °C
 52.4 ft-lb

@Temperature 73.4 °F
 ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 70.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 38.9 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
70.2 µm/m-°C

@Temperature -40.0 - 40.0 °C
 39.0 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
CTE, linear, Transverse to Flow 75.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 41.7 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
75.6 µm/m-°C

@Temperature -40.0 - 40.0 °C
 42.0 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
Deflection Temperature at 0.46 MPa (66 psi) 101 °C

@Thickness 3.20 mm
 214 °F

@Thickness 0.126 in
 unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 89.0 °C
192 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
87.0 °C

@Thickness 3.20 mm
 189 °F

@Thickness 0.126 in
 unannealed; ASTM D648
88.0 °C

@Thickness 6.40 mm
 190 °F

@Thickness 0.252 in
 unannealed; ASTM D648
Vicat Softening Point 120 °C
248 °F
Rate B/50; ISO 306
124 °C
255 °F
Rate B/120; ISO 306
135 °C
275 °F
Rate B/50; ASTM D1525