SABIC Innovative Plastics Xenoy® X6320 PBT+PC (Asia Pacific)
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate/Polybutylene Terephthalate (PBT) Blend, Unreinforced , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Xenoy® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Xenoy® X6320 PBT+PC (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
X6320 is a mineral filled PBT/PC resin developed for automotive painted doorhandles. Key advantages are excellent surface finish, easy processing and paint quality.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.33 g/cc | 1.33 g/cc | ASTM D792 |
| Density | 1.33 g/cc | 0.0480 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.0600 % | 0.0600 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.12 % | 0.12 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0080 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0080 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 20 g/10 min @Load 5.00 kg, Temperature 250 °C |
20 g/10 min @Load 11.0 lb, Temperature 482 °F |
ASTM D1238 |
| Melt Index of Compound | 16 g/10 min @Load 5.00 kg, Temperature 250 °C |
16 g/10 min @Load 11.0 lb, Temperature 482 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 41.0 MPa | 5950 psi | Type I, 5 mm/min; ASTM D638 |
| 43.0 MPa | 6240 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 63.0 MPa | 9140 psi | Type I, 5 mm/min; ASTM D638 |
| 63.0 MPa | 9140 psi | 5 mm/min; ISO 527 | |
| 64.0 MPa | 9280 psi | SABIC - Japan Method | |
| Elongation at Break | 25.4 % | 25.4 % | 5 mm/min; ISO 527 |
| 50 % | 50 % | SABIC - Japan Method | |
| 55.8 % | 55.8 % | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Yield | 4.0 % | 4.0 % | Type I, 5 mm/min; ASTM D638 |
| 4.3 % | 4.3 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 3.86 GPa | 560 ksi | 1 mm/min; ISO 527 |
| 3.89 GPa | 564 ksi | 5 mm/min; ASTM D638 | |
| Flexural Strength | 111 MPa | 16100 psi | ASTM D790 |
| Flexural Yield Strength | 106 MPa | 15400 psi | 2 mm/min; ISO 178 |
| 107 MPa | 15500 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 3.54 GPa | 513 ksi | 2 mm/min; ISO 178 |
| 3.55 GPa | 515 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| 3.75 GPa | 544 ksi | ASTM D790 | |
| Izod Impact, Notched | 0.450 J/cm | 0.843 ft-lb/in | ASTM D256 |
| 0.450 J/cm @Temperature -30.0 °C |
0.843 ft-lb/in @Temperature -22.0 °F |
ASTM D256 | |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² | 2.38 ft-lb/in² | 80*10*4; ISO 180/1A |
| 5.00 kJ/m² @Temperature -30.0 °C |
2.38 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |
| Charpy Impact, Notched | 0.400 J/cm² | 1.90 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| 0.400 J/cm² @Temperature -30.0 °C |
1.90 ft-lb/in² @Temperature -22.0 °F |
Edgew 80*10*4 sp=62mm; ISO 179/1eA | |
| Dart Drop, Total Energy | 65.0 J @Temperature 23.0 °C |
47.9 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 59.9 µm/m-°C @Temperature -40.0 - 40.0 °C |
33.3 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| 61.5 µm/m-°C @Temperature -40.0 - 60.0 °C |
34.2 µin/in-°F @Temperature -40.0 - 140 °F |
ASTM E 831 | |
| CTE, linear, Transverse to Flow | 68.4 µm/m-°C @Temperature -40.0 - 40.0 °C |
38.0 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| 70.2 µm/m-°C @Temperature -40.0 - 60.0 °C |
39.0 µin/in-°F @Temperature -40.0 - 140 °F |
ASTM E 831 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 106 °C | 223 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 121 °C @Thickness 3.20 mm |
250 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| 135 °C @Thickness 6.40 mm |
275 °F @Thickness 0.252 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 78.0 °C | 172 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 88.0 °C @Thickness 3.20 mm |
190 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| 115 °C @Thickness 6.40 mm |
239 °F @Thickness 0.252 in |
unannealed; ASTM D648 | |
| Vicat Softening Point | 137 °C | 279 °F | Rate B/50; ISO 306 |
| 139 °C | 282 °F | Rate B/120; ISO 306 | |
| 139 °C | 282 °F | Rate B/50; ASTM D1525 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Ball Pressure Test, 75°C +/- 2°C | Pass | IEC 60695-10-2 |
Users viewing this material also viewed the following:
- Pyrotek T-67B Fiberseal Blanket
- SolVin 375MD Polyvinyl Chloride Medium Viscosity Paste
- UBE UBEPOL BR230 Non-Oil Extended Synthetic Rubber Vulcanizate (Cured 50 Minutes at 145°C)
- CP-Polymer-Technik Wellamid® 6000 GVS 10/20 HWCP 10% Glass Fiber and 20% Glass Sphere Nylon 6, Heat Stabilized, Dry
- AK Steel ASTM A 1011, Class 1 Formable, Grade 60K Hot Rolled Carbon Steel, Medium/High Strength Low Alloy Steel (HSLA)
- DuPont Performance Polymers Zytel® 80G14A NC010A Nylon 66 (Unverified Data**)
- ExxonMobil Escorene® UL-7560 EVA Copolymer, Adhesive and Sealant Grade (discontinued **)
Copyright © lookpolymers.com All Rights Reserved