SABIC Innovative Plastics Xenoy® XD549S PBT+PC (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate/Polybutylene Terephthalate (PBT) Blend, Unreinforced , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Xenoy® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Xenoy® XD549S PBT+PC (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Xenoy XD549S is an automotive grade, designed for thin wall (2.5 mm.) direct gated exterior parts. The material has an excellent flow. Xenoy XD549S can be painted with primerless solvent or waterbased paint systems. This grade has similar performance as CL300.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.21 g/cc | 0.0437 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 0.15 % | 0.15 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.50 % @Temperature 23.0 °C |
0.50 % @Temperature 73.4 °F |
ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0070 - 0.011 cm/cm | 0.0070 - 0.011 in/in | on tensile bar; SABIC Method |
| Melt Flow | 13 g/10 min @Load 2.16 kg, Temperature 250 °C |
13 g/10 min @Load 4.76 lb, Temperature 482 °F |
[cm^3/10 min] Melt Volume Rate; ISO 1133 |
| 14 g/10 min @Load 2.16 kg, Temperature 250 °C |
14 g/10 min @Load 4.76 lb, Temperature 482 °F |
ISO 1133 | |
| 37 g/10 min @Load 5.00 kg, Temperature 250 °C |
37 g/10 min @Load 11.0 lb, Temperature 482 °F |
[cm^3/10 min] Melt Volume Rate; ISO 1133 | |
| 40 g/10 min @Load 5.00 kg, Temperature 250 °C |
40 g/10 min @Load 11.0 lb, Temperature 482 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, H358/30 | 95.0 MPa | 13800 psi | ISO 2039-1 |
| Tensile Strength at Break | 45.0 MPa | 6530 psi | 50 mm/min; ISO 527 |
| Tensile Strength, Yield | 50.0 MPa | 7250 psi | 50 mm/min; ISO 527 |
| Elongation at Break | 100 % | 100 % | 50 mm/min; ISO 527 |
| Elongation at Yield | 4.5 % | 4.5 % | 50 mm/min; ISO 527 |
| Tensile Modulus | 2.10 GPa | 305 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 78.0 MPa | 11300 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 2.00 GPa | 290 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 25.0 kJ/m² @Temperature -30.0 °C |
11.9 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A |
| 26.0 kJ/m² @Temperature -40.0 °C |
12.4 ft-lb/in² @Temperature -40.0 °F |
80*10*4; ISO 180/1A | |
| 30.0 kJ/m² @Temperature -10.0 °C |
14.3 ft-lb/in² @Temperature 14.0 °F |
80*10*4; ISO 180/1A | |
| 49.0 kJ/m² @Temperature 23.0 °C |
23.3 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A | |
| Taber Abrasion, mg/1000 Cycles | 30 @Load 1.00 kg |
30 @Load 2.20 lb |
CS-17; SABIC Method |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 86.0 µm/m-°C @Temperature 23.0 - 80.0 °C |
47.8 µin/in-°F @Temperature 73.4 - 176 °F |
ISO 11359-2 |
| Thermal Conductivity | 0.180 W/m-K | 1.25 BTU-in/hr-ft²-°F | ISO 8302 |
| Deflection Temperature at 0.46 MPa (66 psi) | 100 °C | 212 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be |
| Deflection Temperature at 1.8 MPa (264 psi) | 75.0 °C | 167 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| Vicat Softening Point | 123 °C | 253 °F | Rate B/50; ISO 306 |
| 127 °C | 261 °F | Rate B/120; ISO 306 | |
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
UL 94 by SABIC-IP |
| Flame Spread | 50.0 mm/min @Thickness 1.00 mm |
1.97 in/min @Thickness 0.0394 in |
FMVSS 302 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+14 ohm-cm | >= 1.00e+14 ohm-cm | IEC 60093 |
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | ROA; IEC 60093 |
| Dielectric Constant | 3.1 @Frequency 1.00e+6 Hz |
3.1 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 3.3 @Frequency 50.0 - 60.0 Hz |
3.3 @Frequency 50.0 - 60.0 Hz |
IEC 60250 | |
| Dielectric Strength | 17.0 kV/mm @Thickness 3.20 mm |
432 kV/in @Thickness 0.126 in |
in oil; IEC 60243-1 |
| Dissipation Factor | 0.0020 @Frequency 50.0 - 60.0 Hz |
0.0020 @Frequency 50.0 - 60.0 Hz |
IEC 60250 |
| 0.020 @Frequency 1.00e+6 Hz |
0.020 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Ball Pressure Test, 75°C +/- 2°C | PASSES | IEC 60695-10-2 |
Users viewing this material also viewed the following:
- Quadrant EPP Cestilene™ HD 1000 R Polyethylene
- Latrobe Lescalloy® UT-18 VAC-ARC ; 2.125 in. round High Strength Alloy Steel
- Spartech E65060 General Purpose PVC
- Techmer ES Plaslube® PC-50/TF/22 BK223 Polycarbonate
- Master Bond MasterSil 153Med Silicone Paste for Medical Applications
- A. Schulman POLYFORT™ FPP 809 Talc Filled Homopolymer Polypropylene
- Constellium ALPLAN® 6061 Rolled Precision Aluminum Plate, Milled Both Sides
- DuPont Performance Polymers Hytrel® 8238 TPC-ET (Unverified Data**)
- SABIC Innovative Plastics NORYL FN215X PPE+PS
Copyright © lookpolymers.com All Rights Reserved