SABIC M200024 Linear Low Density Polyethylene for Injection Molding

Category Polymer , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE), Injection Molded
Manufacturer SABIC
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC M200024 Linear Low Density Polyethylene for Injection Molding.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Product Description: M200024 is a Linear Low Density Polyethylene grade with a narrow molecular weight distribution suitable for injection molding applications. It has been designed to give good flow properties with low temperature toughness, stress crack resistance and high gloss.Typical Applications: M200024 is recommended for housewares, trash cans, lids for large industrial containers, automotive parts, etc.Information provided by SABIC.
Physical Properties Metric English Comments
Density 0.924 g/cc
0.0334 lb/in³
load density; ASTM D1505
ESCR 100% Igepal® 6.0 hour
6.0 hour
F50; ASTM D1693B
ESCR 10% Igepal® 3.0 hour
3.0 hour
F50; ASTM D1693B
Melt Flow 20 g/10 min

@Load 2.16 kg,
Temperature 190 °C
20 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Shore D 50
50
ASTM D2240
Tensile Strength at Break 12.0 MPa
1740 psi
ASTM D638
Tensile Strength, Yield 10.0 MPa
1450 psi
ASTM D638
Elongation at Break >= 500 %
>= 500 %
ASTM D638
Flexural Strength 9.00 MPa
1310 psi
ASTM D790
Flexural Modulus 0.200 GPa
29.0 ksi
ASTM D790
1% Secant Modulus 230 MPa
33400 psi
ASTM D638
Izod Impact, Notched 5.00 J/cm
9.37 ft-lb/in
ASTM D256
Thermal Properties Metric English Comments
Vicat Softening Point 92.0 °C
198 °F
ASTM D1525
Brittleness Temperature <= -75.0 °C
<= -103 °F
ASTM D746
Processing Properties Metric English Comments
Mold Temperature 15.0 - 60.0 °C
59.0 - 140 °F
Injection Pressure 60.0 - 100 MPa