SABIC M40060 Series High Density Polyethylene for Injection Molding

Category Polymer , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Injection Molded
Manufacturer SABIC
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC M40060 Series High Density Polyethylene for Injection Molding.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Product Description: M40060 is a high density polyethylene grade with a narrow molecular weight distribution suitable for injection molding applications. It has been designed to provide good rigidity, excellent toughness and low warpage. M40060 is also available with UV stabilizer as M40060S.Typical Applications: M40060 series grades are recommended for industrial pails, shipping containers and other parts requiring a balance of toughness and rigidity.Information provided by SABIC.
Physical Properties Metric English Comments
Density 0.960 g/cc
0.0347 lb/in³
ASTM D1505
ESCR 100% Igepal® 6.0 hour
6.0 hour
F50; ASTM D1693B
ESCR 10% Igepal® 3.0 hour
3.0 hour
F50; ASTM D1693B
Melt Flow 4.0 g/10 min

@Load 2.16 kg,
Temperature 190 °C
4.0 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Shore D 60
60
ASTM D2240
Tensile Strength at Break 22.0 MPa
3190 psi
ASTM D638
Tensile Strength, Yield 24.0 MPa
3480 psi
ASTM D638
Elongation at Break >= 600 %
>= 600 %
ASTM D638
Flexural Strength 24.0 MPa
3480 psi
ASTM D790
Flexural Modulus 0.900 GPa
131 ksi
ASTM D790
1% Secant Modulus 950 MPa
138000 psi
ASTM D638
Izod Impact, Notched 1.80 J/cm
3.37 ft-lb/in
ASTM D256
Thermal Properties Metric English Comments
Vicat Softening Point 125 °C
257 °F
ASTM D1525
Brittleness Temperature <= -75.0 °C
<= -103 °F
ASTM D746
Processing Properties Metric English Comments
Mold Temperature 15.0 - 60.0 °C
59.0 - 140 °F
Injection Pressure 60.0 - 100 MPa
8700 - 14500 psi