SABIC PS 330 High Impact Polystyrene for Sheet Extrusion

Category Polymer , Thermoplastic , Polystyrene (PS) , Polystyrene, Impact Modified
Manufacturer SABIC
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC PS 330 High Impact Polystyrene for Sheet Extrusion.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Product Description: High Impact Polystyrene PS 330 is manufactured by continuous mass polymerization of styrene monomer. An elastomer is incorporated during polymerization to achieve impact resistance. It is generally opaque in color. It is a high impact strength polystyrene with a high heat deflection temperature and good physical properties.Typical Applications: It is primarily designed for extrusion and thermoforming applications. It can be used for food packaging and dairy products.Information provided by SABIC.
Physical Properties Metric English Comments
Bulk Density 0.600 g/cc
0.0217 lb/in³
ASTM D1895B
Density 1.04 g/cc
0.0376 lb/in³
Load Density; ASTM D792
Melt Flow 4.0 g/10 min

@Load 2.16 kg,
Temperature 230 °C
4.0 g/10 min

@Load 4.76 lb,
Temperature 446 °F
ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell L 67
67
ASTM D785
Hardness, Rockwell M 10
10
ASTM D785
Tensile Strength at Break 29.0 MPa
4210 psi
ASTM D638
Elongation at Break 50 %
50 %
ASTM D638
Tensile Modulus 2.353 GPa
341.3 ksi
ASTM D638
Flexural Strength 44.0 MPa
6380 psi
ASTM D790
Flexural Modulus 2.647 GPa
383.9 ksi
ASTM D790
Izod Impact, Notched 1.10 J/cm
2.06 ft-lb/in
ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 97.0 °C
207 °F
ASTM D648
Vicat Softening Point 99.0 °C

@Load 1.00 kg
210 °F

@Load 2.20 lb
ASTM D1525B
Flammability, UL94 HB

@Thickness 1.30 mm
HB

@Thickness 0.0512 in
HB

@Thickness 3.00 mm
HB

@Thickness 0.118 in