SCG Chemicals EL-Leneâ„¢ LD2305F Low Density Polyethylene Film
| Category | Polymer , Film , Thermoplastic , Polyethylene (PE) , LDPE , Low Density Polyethylene (LDPE), Film Grade |
| Manufacturer | SCG Chemicals Co. |
| Trade Name | EL-Lene™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SCG Chemicals EL-Leneâ„¢ LD2305F Low Density Polyethylene Film.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Key Characteristics:Excellent clarity and glossGood zip formationContains 1000 ppm slip agent and 500 ppm antiblocking agentRecommended Applications:Zip bagsGeneral purpose film for food packagingInformation provided by SCG Chemicals
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.923 g/cc | 0.923 g/cc | ASTM D1505 |
| Thickness | 38.0 microns | 1.50 mil | |
| Melt Flow | 3.5 g/10 min @Load 2.16 kg, Temperature 190 °C |
3.5 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Tensile Strength at Yield, TD | 9.00 MPa | 1310 psi | ASTM D882 |
| Film Elongation at Break, MD | 300 % | 300 % | ASTM D882 |
| Film Elongation at Break, TD | 550 % | 550 % | ASTM D882 |
| Secant Modulus, MD | 0.260 GPa | 37.7 ksi | ASTM D882 |
| Secant Modulus, TD | 0.250 GPa | 36.3 ksi | ASTM D882 |
| Elmendorf Tear Strength, MD | 15.7 g/micron | 400 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 10.8 g/micron | 275 g/mil | ASTM D1922 |
| Dart Drop | 2.10 g/micron | 53.3 g/mil | ASTM D1709 |
| Dart Drop Test | 78.0 g | 0.172 lb | ASTM D1709 |
| Film Tensile Strength at Break, MD | 24.0 MPa | 3480 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 19.0 MPa | 2760 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 110 °C | 230 °F | ASTM D2117 |
| Vicat Softening Point | 92.0 °C | 198 °F | ASTM D1525 |
| Brittleness Temperature | <= -73.0 °C | <= -99.4 °F | ASTM D746 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 5.0 % | 5.0 % | ASTM D1003 |
| Gloss | 78 % | 78 % | ASTM D2457 |