Saint-Gobain Vitreosil® CFQ/TSC Optical Fused Quartz

Category Ceramic , Glass , Oxide , Silicon Oxide
Manufacturer Saint-Gobain Quartz PLC
Trade Name Vitreosil®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Saint-Gobain Vitreosil® CFQ/TSC Optical Fused Quartz.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Vitreosil® CFQ/TSC grades are for use in less demanding applications including viewing windows for use in corrosive and high temperature environments and non-optical components such as spacers, insulators, etc.Vitreosil® optical fused quartz is made by flame fusion of naturally occurring quartz crystal in an oxy-hydrogen flame. Darkens slightly after prolonged UV exposure. Darkens after 107 RAD X-ray or gamma ray exposure.General properties of Fused Silica and Fused quartz: A very wide transmission range from UV to near IR; extremely high optical transmission, excellent resistance to high power laser energy, excellent homogeneity, high temperature resistance, very low thermal expansion (resistance to thermal shock), and chemical inertness. General uses for optical quartz are microlithography optical systems, optical fibers, photomasks, laser optics, LCD displays, light guides, optical, IR , and UV windows, spectrophotometer cells, slides, optical pyrometers, and lamp bodies/components.Information provided by Saint-Gobain Quartz PLC.
Physical Properties Metric English Comments
Density 2.20 g/cc
0.0795 lb/in³
Mechanical Properties Metric English Comments
Hardness, Knoop 820
820
Vickers Microhardness 1050 - 1350
1050 - 1350
kg/m² Vickers DPH
Hardness, Mohs 7.0
7.0
Tensile Strength, Ultimate 50.0 MPa
7250 psi
Modulus of Elasticity 72.0 GPa
10400 ksi
Flexural Strength 65.0 MPa
9430 psi
Bending Strength
Compressive Strength 1100 MPa
160000 psi
Poissons Ratio 0.16
0.16
Shear Modulus 31.0 GPa
4500 ksi
Shear Strength 30.0 MPa
4350 psi
Thermal Properties Metric English Comments
CTE, linear 0.540 µm/m-°C

@Temperature 0.000 - 1000 °C
0.300 µin/in-°F

@Temperature 32.0 - 1830 °F
average
Specific Heat Capacity 0.750 J/g-°C
0.179 BTU/lb-°F
Thermal Conductivity 1.38 W/m-K
9.58 BTU-in/hr-ft²-°F
Maximum Service Temperature, Air 1050 °C
1920 °F
Normal Conditions
1350 °C
2460 °F
Extended periods if cycles remain above 300°C
1350 °C
2460 °F
1650 °C
3000 °F
Quick Immersion
Softening Point 1730 °C
3150 °F
Varies with thermal history
Annealing Point 1200 °C
2190 °F
Varies with thermal history
Strain Point 1080 °C
1980 °F
Varies with thermal history
Optical Properties Metric English Comments
Refractive Index 1.457

@Wavelength 632.8 nm
1.457

@Wavelength 632.8 nm
n<sub>He-Ne</sub>; Temperature Coefficient = 10.0 ppm/K
1.4667

@Wavelength 435.83 nm
1.4667

@Wavelength 435.83 nm
n<sub>g</sub>; Temperature Coefficient = 10.6 ppm/K
Transmission, Visible 92 %
92 %
Including Fresnel reflection for 10 mm pathlength
IR Transmittance 92 %

@Wavelength <=2200 nm,
Thickness 10.0 mm
92 %

@Wavelength <=2200 nm,
Thickness 0.394 in
Including Fresnel reflection for 10 mm path length.
UV Transmittance 90 %

@Thickness 10.0 mm,
Wavelength 270 nm
90 %

@Thickness 0.394 in,
Wavelength 270 nm
Component Elements Properties Metric English Comments
SiO2 >= 99.99 %
>= 99.99 %
Electrical Properties Metric English Comments
Electrical Resistivity 6.00e+10 ohm-cm

@Temperature 800 °C
6.00e+10 ohm-cm

@Temperature 1470 °F
Dielectric Constant 3.78

@Frequency 100 - 2.50e+10 Hz
3.78

@Frequency 100 - 2.50e+10 Hz
Dielectric Strength 37.0 kV/mm
940 kV/in
Dissipation Factor 0.00010

@Frequency 1e+6 Hz
0.00010

@Frequency 1e+6 Hz
Descriptive Properties Value Comments
Fluorescence Blue/Violet
254 nm excitation
Granularity Faint